Sibur NGP 40-32 Polyvinyl Chloride (PVC)
| Category | Polymer , Thermoplastic , Vinyl (PVC) , PVC, Molded |
| Manufacturer | Sibur |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sibur NGP 40-32 Polyvinyl Chloride (PVC).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Shall correspond to control sample, approved in accordance with the established procedure. Pores, which can be seen by eyes, are not allowed. Plastic shall no burn at stop of worm extruder for a period of 20 minutes. For application of protective sheaths for wires and cables operating in a range of temperatures from -40°C to 70°C under conditions of high fire hazard and corresponding to the requirements of standard MEK 332, part 3 on non-propagation of burning. These products inhibit flame propagation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.50 g/cc | 0.0542 lb/in³ | |
| Water Absorption | <= 0.25 % | <= 0.25 % | |
| Collected Volatile Condensable Material | <= 2.0 % | <= 2.0 % | Loss in mass at 160°C during 6 hours |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | >= 14.0 MPa | >= 2030 psi | |
| Elongation at Break | >= 280 % | >= 280 % |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Brittleness Temperature | <= -40.0 °C | <= -40.0 °F | |
| Flammability Test | <= 32 | <= 32 | In seconds, method A |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 3.00e+11 ohm-cm @Temperature 20.0 °C |
>= 3.00e+11 ohm-cm @Temperature 68.0 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Non-colored, black, white | |
| Elongation Retained After Ageing | 85% | Aged for 7 days at 100±2°C |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics LNP LUBRILOY RF203 PA 66 (Europe-Africa-Middle East)
- Stir SpA SA 81 N (PVC)
- Saint-Gobain Chemfab® 10 Anti-Static PTFE-Coated Glass
- Polyram Polytron P30N03 Polypropylene, 30% Long Glass Fibers
- DSM Fibre Intermediates Nyrim® 1500 (Conditioned)
- ExxonMobil Santoprene® 121-60M200 Thermoplastic Vulcanizate - UV Resistant
- Asahi Kasei Thermofil N3-40MF-1350 40% Mineral Reinforced, Heat Stabilized
- 3M FA021 Matte Clear Acetate Label Products
- Multibase Multi-Pro® 4007 XGS Polypropylene
Copyright © lookpolymers.com All Rights Reserved