Arlon R36461R014 0.014" (0.356 mm) Uncured Silicone Rubber with Fiberglass Substrate

Category	Polymer , Thermoset , Silicone , Silicone Rubber , Silicone, Molded, Glass Fiber Filled
Manufacturer	Arlon
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Arlon R36461R014 0.014" (0.356 mm) Uncured Silicone Rubber with Fiberglass Substrate.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Design/Construction: Liner: Polyethylene Side 1: Uncured Silicone Rubber Substrate: Style 7628 Fiberglass Side 2: Uncured Silicone Rubber Liner: Polyethylene This data represents typical values for the production material. The data should not be used to write, or in place of, material specifications.Information provided by Arlon, Silicone Technologies Division

Physical Properties	Metric	English	Comments
Density	1.40 g/cc	0.0506 lb/in³	Silicone Property; Arlon SQA-TMS-024
Thickness	76.2 microns	3.00 mil	Side 1; Arlon SQA-TMS-003
	76.2 microns	3.00 mil	Side 2; Arlon SQA-TMS-003
	76.2 microns	3.00 mil	Liner 1
	76.2 microns	3.00 mil	Liner 2
	203 microns	8.00 mil	Substrate; Arlon SQA-TMS-003
	356 microns	14.0 mil	Overall; Arlon SQA-TMS-003

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	58	58	Silicone Property; ASTM D2240
Tensile Strength	7.58 MPa	1100 psi	Silicone Property; ASTM D412
Elongation at Break	250 %	250 %	Silicone Property; ASTM D412
Peel Strength	1.26 kN/m	7.20 pli	Bond Strength; ASTM D624

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	232 °C	450 °F
Minimum Service Temperature, Air	-56.7 °C	-70.0 °F

Processing Properties	Metric	English	Comments
Cure Time	120 min @Temperature 204 °C	2.00 hour @Temperature 400 °F	Recommended Postcure Cycle
	15.0 min @Pressure 0.0689 - 0.345 MPa, Temperature 149 °C	0.250 hour @Pressure 10.0 - 50.0 psi, Temperature 300 °F	Recommended Cure Cycle
Shelf Life	6.00 Month @Temperature 21.1 - 26.7 °C	6.00 Month @Temperature 70.0 - 80.0 °F	From date of manufacture

Descriptive Properties	Value	Comments
Color	Red
Total Product Weight (oz/yd2)	15	Arlon SQA-TMS-025
Uncoated Fabric Break Strength	200 lb/in	Fill Strength, Substrate Property, Arlon SQA-TMS-026
	250 lb/in	Warp Strength, Substrate Property, Arlon SQA-TMS-026