Loxim 433 01HB Nylon 6,6
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled , Nylon 66, Glass Fiber Filled, Flame Retardant |
| Manufacturer | Loxim Industries |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Loxim 433 01HB Nylon 6,6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Loxim Industries
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.37 g/cc | 1.37 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM D1299 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 190 MPa | 27600 psi | ASTM D683 |
| Elongation at Break | 3.0 - 4.0 % | 3.0 - 4.0 % | ASTM D638 |
| Flexural Modulus | 9.00 GPa | 1310 ksi | ASTM D790 |
| Izod Impact, Notched | 1.20 J/cm | 2.25 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 255 °C | 491 °F | ASTM D1525, HDT Method B |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
Users viewing this material also viewed the following:
- Kolon KOCETAL® GF702 G/F Reinforced Acetal Resin
- Wingate Alloys Winco HCC High Carbon, High Chrome Tool and Die Steel
- A. Schulman POLYBATCH™ Blue 4535 Concentrate Based In Polyethylene
- CIMBAR CIMTUFF® 9103s Talc
- Colorite Polymers CS1521SC Non Lead Wire and Cable Vinyl Compound
- Arlon 55572GA028 0.028" Cured Silicone Rubber with Fiberglass Substrate
- Caplinq LINQSTAT™ VCF-42424B
- Loctite® CHIPBONDER® 3609 Syringe Dispense
- Karina 802-10/55-AY-ERYB White PVC Compound
- ChevronTexaco Havoline® SAE 40 Motor Oil
Copyright © lookpolymers.com All Rights Reserved