Arlon 55579R031H 0.0315" (0.800 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
| Category | Polymer , Thermoset , Silicone , Silicone Rubber , Silicone, Molded, Glass Fiber Filled |
| Manufacturer | Arlon |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Arlon 55579R031H 0.0315" (0.800 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Design/Construction: Interleave: LDPELayer 2: Uncured Silicone Rubber Layer 1: Cured Silicone Rubber Substrate: Style 162 FiberglassThis data represents typical values for the production material. The data should not be used to write, or in place of, material specifications.Information provided by Arlon, Silicone Technologies Division
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Thickness | 63.5 microns | 2.50 mil | Interleave |
| 127 microns | 5.00 mil | Layer 1; Arlon SQA-TMS-003 | |
| 267 microns | 10.5 mil | Layer 2; Arlon SQA-TMS-003 | |
| 406 microns | 16.0 mil | Substrate; Arlon SQA-TMS-003 | |
| 800 microns | 31.5 mil | Overall; Arlon SQA-TMS-003 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 44 | 44 | Layer 1, Silicone Property; ASTM D2240 |
| 52 | 52 | Layer 2, Silicone Property; ASTM D2240 | |
| Tensile Strength | 6.14 MPa | 890 psi | Layer 2, Silicone Property; ASTM D412 |
| 7.58 MPa | 1100 psi | Layer 1, Silicone Property; ASTM D412 | |
| Elongation at Break | 550 % | 550 % | Layer 2, Silicone Property; ASTM D412 |
| 650 % | 650 % | Layer 1, Silicone Property; ASTM D412 | |
| Peel Strength | 4.33 kN/m | 24.7 pli | Bond Strength; ASTM D624 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 232 °C | 450 °F | |
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |
| UL RTI, Electrical | 220 °C | 428 °F | |
| UL RTI, Mechanical without Impact | 200 °C | 392 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | 15.7 kV/mm | 400 kV/in | ASTM D149 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 120 min @Temperature 204 °C |
2.00 hour @Temperature 400 °F |
Recommended Postcure Cycle |
| 15.0 min @Pressure 0.345 MPa, Temperature 177 °C |
0.250 hour @Pressure 50.0 psi, Temperature 350 °F |
Recommended Cure Cycle | |
| Shelf Life | 6.00 Month @Temperature 21.1 °C |
6.00 Month @Temperature 70.0 °F |
From date of manufacture |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Red | |
| Total Product Weight (oz/yd2) | 32.1 | Arlon SQA-TMS-025 |
Users viewing this material also viewed the following:
- Polimeri Europa Clearflex® RP 50 U Linear Medium Density Polyethylene
- Overview of materials for Nylon 610, Carbon Fiber Filled
- Indium Corp. WF-9942 Wave Solder Flux, No-Residue
- Unitika elitel UE3203 Polyester, Pellet
- UBE 7034T Nylon 6/12 Monofilament (Drawing Ratio=4.5, Diameter 2 mm)
- EMS-Grivory Grivory® L 16 W 20 black 9995 PA12
- Ascend Performance Materials Vydyne® R533T Nylon 66, Translucent, 33% Glass Filled, Dry as Molded
- Ashley Polymers Ashlene® P1044R Polycarbonate
- A. Schulman ComAlloy Comtuf® 152 Polypropylene, Mineral Reinforced, Impact Modified
Copyright © lookpolymers.com All Rights Reserved