SABIC Innovative Plastics Ultem 2110N PEI
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | ULTEM |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Ultem 2110N PEI.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
10% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.41 g/cc | 1.41 g/cc | ASTM D 792 |
| Melt Flow | 10.4 g/10 min @Load 6.60 kg, Temperature 337 °C |
10.4 g/10 min @Load 14.6 lb, Temperature 639 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 115 MPa | 16700 psi | Type I, 5 mm/min; ASTM D 638 |
| Tensile Strength, Yield | 114 MPa | 16500 psi | Type I, 5 mm/min; ASTM D 638 |
| Elongation at Break | 6.0 % | 6.0 % | Type I, 5 mm/min; ASTM D 638 |
| Tensile Modulus | 4.61 GPa | 669 ksi | 5 mm/min; ASTM D 638 |
| Flexural Strength | 199 MPa | 28900 psi | 2.6 mm/min, 100 mm span; ASTM D 790 |
| Flexural Modulus | 5.24 GPa | 760 ksi | 2.6 mm/min, 100 mm span; ASTM D 790 |
| Izod Impact, Notched | 0.480 J/cm @Temperature 23.0 °C |
0.899 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| 4.00 J/cm @Thickness 3.20 mm |
7.49 ft-lb/in @Thickness 0.126 in |
reverse notched; ASTM D 256 | |
| Izod Impact, Unnotched | 3.73 J/cm @Temperature 23.0 °C |
6.99 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 207 °C @Thickness 6.40 mm |
405 °F @Thickness 0.252 in |
unannealed; ASTM D 648 |
| Glass Transition Temp, Tg | 217 °C | 423 °F |
Users viewing this material also viewed the following:
- Precision Polymer Engineering Perlast® G60S FFKM White Perfluoroelastomer
- LyondellBasell Glycol Ether DE Diethylene glycol ethyl ether
- LATI Latishield 36/SP-05A ABS, Steel Fiber Reinforced
- SABIC Innovative Plastics NORYL WCD915 PPE-TPE (Asia Pacific)
- Taiwan Sheen Soon Sheenthane® A7551E2 Thermoplastic Polyurethane Elastomer
- Taiwan Sheen Soon Sheenthane® AS-422 TPU for PU Adhesive
- Fainplast Compounds PH 45/1 Flexible PVC, Transparent Extrusion
- Austin Novel Materials Texalan® 664D Polyester and Polyether based TPU
- Arkema Group KYNAR® 2801-00 Polyvinylidene Fluoride Powder
Copyright © lookpolymers.com All Rights Reserved