- Arlon 51576B015 0.0155" (0.394 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
Arlon 51576B015 0.0155" (0.394 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
| Category | Polymer , Thermoset , Silicone , Silicone Rubber , Silicone, Molded, Glass Fiber Filled |
| Manufacturer | Arlon |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Arlon 51576B015 0.0155" (0.394 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Design/Construction: Side 1: Cured Silicone RubberSubstrate: 7628 Style Fiberglass Side 2: Uncured Silicone RubberInterleave: Polyethylene This data represents typical values for the production material. The data should not be used to write, or in place of, material specifications.Information provided by Arlon, Silicone Technologies Division
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.24 g/cc | 0.0448 lb/in³ | Side 2, Silicone Property; Arlon SQA-TMS-024 |
| 1.35 g/cc | 0.0488 lb/in³ | Side 1, Silicone Property; Arlon SQA-TMS-024 | |
| Thickness | 50.8 microns | 2.00 mil | Side 1; Arlon SQA-TMS-003 |
| 76.2 microns | 3.00 mil | Interleave | |
| 140 microns | 5.50 mil | Side 2; Arlon SQA-TMS-003 | |
| 394 microns | 15.5 mil | Overall; Arlon SQA-TMS-003 | |
| 2490 microns | 98.0 mil | Substrate; Arlon SQA-TMS-003 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 44 | 44 | Side 2, Silicone Property; ASTM D2240 |
| 52 | 52 | Side 1, Silicone Property; ASTM D2240 | |
| Tensile Strength | 6.14 MPa | 890 psi | Side 1, Silicone Property; ASTM D412 |
| 7.58 MPa | 1100 psi | Side 2, Silicone Property; ASTM D412 | |
| Elongation at Break | 550 % | 550 % | Side 1, Silicone Property; ASTM D412 |
| 650 % | 650 % | Side 2, Silicone Property; ASTM D412 | |
| Peel Strength | 1.88 kN/m | 10.7 pli | Bond Strength; ASTM D624 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 232 °C | 450 °F | |
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |
| UL RTI, Electrical | 220 °C | 428 °F | |
| UL RTI, Mechanical without Impact | 200 °C | 392 °F | |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | 25.2 kV/mm | 640 kV/in | ASTM D149 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 120 min @Temperature 204 °C |
2.00 hour @Temperature 400 °F |
Recommended Postcure Cycle |
| 15.0 min @Pressure 0.345 MPa, Temperature 177 °C |
0.250 hour @Pressure 50.0 psi, Temperature 350 °F |
Recommended Cure Cycle | |
| Shelf Life | 6.00 Month @Temperature 23.9 °C |
6.00 Month @Temperature 75.0 °F |
From date of manufacture |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Black | |
| Total Product Weight (oz/yd2) | 18.3 | Arlon SQA-TMS-025 |
Users viewing this material also viewed the following:
- Tipco Tipcolene® FPT 20 FR VO LTHA - UL94-V0 Flame Retardant, 20% Talc Polypropylene Homopolymer, Long Term Heat Stability
- Arkema Group Pebax® 3533 SN 01 Polyether Block Amide (PEBA) (Conditioned)
- Ametek High Purity Nickel Strip 899L Full Hard
- BASF Ultrason S 2010 PSU
- Arlon 51271R015 0.015" (0.381 mm) Uncured Silicone Rubber with Fiberglass Substrate
- BASF Lupranate® 278 Isocyanate
Copyright © lookpolymers.com All Rights Reserved