BASF Ultramid® B3EG7 35% Glass Filled PA6 (Conditioned)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 40% Glass Fiber Filled |
| Manufacturer | BASF |
| Trade Name | Ultramid® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultramid® B3EG7 35% Glass Filled PA6 (Conditioned).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: 35% Glass fiber reinforced injection molding grade for industrial articles and electrical insulating parts.Information provided by BASF
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.500 - 0.800 g/cc | 0.0181 - 0.0289 lb/in³ | |
| Density | 1.41 g/cc | 0.0509 lb/in³ | ISO 1183 |
| Water Absorption | 5.9 - 6.5 % | 5.9 - 6.5 % | ISO 62 |
| Moisture Absorption at Equilibrium | >= 2.0 % | >= 2.0 % | 50% RH |
| 1.8 - 2.2 % | 1.8 - 2.2 % | ISO 62 | |
| >= 6.2 % | >= 6.2 % | Saturation | |
| Viscosity Measurement | 140 | 140 | ISO 307 |
| Linear Mold Shrinkage | 0.0035 cm/cm | 0.0035 in/in | |
| Melt Flow | 63.45 g/10 min @Load 5.00 kg, Temperature 275 °C |
63.45 g/10 min @Load 11.0 lb, Temperature 527 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 130 MPa | 18900 psi | ISO 527-1/-2 |
| Elongation at Break | 7.0 % | 7.0 % | ISO 527-1/-2 |
| Tensile Modulus | 7.20 GPa | 1040 ksi | ISO 527-1/-2 |
| Flexural Strength | 200 MPa | 29000 psi | ISO 178 |
| Flexural Modulus | 6.30 GPa | 914 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 27.0 kJ/m² @Temperature 23.0 °C |
12.8 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A |
| Charpy Impact Unnotched | 11.0 J/cm² @Temperature 23.0 °C |
52.3 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU |
| Charpy Impact, Notched | 3.30 J/cm² @Temperature 23.0 °C |
15.7 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Tensile Creep Modulus, 1000 hours | 3300 MPa @Strain <=0.500 % |
479000 psi @Strain <=0.500 % |
ISO 899-1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 0.360 W/m-K | 2.50 BTU-in/hr-ft²-°F | DIN 52612-1 |
| Melting Point | 220 °C | 428 °F | ISO 11357-1/-3 |
| Maximum Service Temperature, Air | 135 °C | 275 °F | for 50% loss of tensile strength after 20000hr |
| 165 °C | 329 °F | for 50% loss of tensile strength after 5000hr | |
| 200 °C | 392 °F | ||
| Decomposition Temperature | >= 300 °C | >= 572 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+10 ohm-cm | 1.00e+10 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+10 ohm | 1.00e+10 ohm | IEC 60093 |
| Dielectric Constant | 6.2 @Frequency 1.00e+6 Hz |
6.2 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Dissipation Factor | 0.19 @Frequency 1.00e+6 Hz |
0.19 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 0.19 @Frequency 100 Hz |
0.19 @Frequency 100 Hz |
IEC 60250 | |
| Comparative Tracking Index | 575 V | 575 V | Test Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 80.0 °C | 176 °F | Hopper Throat |
| Zone 1 | 260 °C | 500 °F | Feed Zone |
| Zone 2 | 370 °C | 698 °F | Compression |
| Zone 3 | 280 °C | 536 °F | Metering-zone |
| Zone 4 | 280 °C | 536 °F | Nozzle |
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | Injection Molding/Extrusion |
| 280 °C | 536 °F | Optimal | |
| Mold Temperature | 80.0 °C | 176 °F | Optimal |
| 80.0 - 90.0 °C | 176 - 194 °F | Injection Molding | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 4 hour | 4 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Commercial Status | Europe and North America | |
| Ignition Temperature | >400°C | ASTM D1929 |
| Peripheral screw speed | < 0.3 m/s |
Users viewing this material also viewed the following:
- Multibase Multi-Flex® TPE A 8021 BLK , 37.5% Filler Content
- MV Labs CU110 Cu(C2H3O2)2 Copper(II) acetate, anhydrous
- Fainplast Compounds RH 214 Rigid PVC, Antishock Extrusion
- LyondellBasell Petrothene® LP540200 High Density Polyethylene
- SABIC Innovative Plastics Valox® 771 PBT (Europe-Africa-Middle East)
- Teknor Apex Sinvicomp SSG 6006 Polyvinyl Chloride, Flexible
- Elgiloy® Co-Cr-Ni Alloy, Wire, 47% Cold Reduction (Coil Spring Range)
- Gouda Vuurvast GOLITE 160 GM Refractory Insulating Castable
- A. Schulman POLYFORT™ PX 1040
Copyright © lookpolymers.com All Rights Reserved