Arlon 45541R012 0.012" (0.305 mm) Uncured Rubber with Fiberglass Substrate

Category	Polymer , Thermoset , Silicone , Silicone Rubber
Manufacturer	Arlon
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Arlon 45541R012 0.012" (0.305 mm) Uncured Rubber with Fiberglass Substrate.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Design/Construction:Side 1: Uncured RubberSide 2: Uncured Rubber Appearance: Red silicone gumThis data represents typical values for the production material. The data should not be used to write, or in place of, material specifications.Information provided by Arlon, Silicone Technologies Division

Physical Properties	Metric	English	Comments
Thickness	38.1 microns	1.50 mil	Polyethylene Interleave
	76.2 microns	3.00 mil	Prime Coated 113 Fiberglass, Substrate
	152 - 203 microns	6.00 - 8.00 mil	Side 1
	279 - 330 microns	11.0 - 13.0 mil	Overall

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	40 - 50	40 - 50	Compound Property
Tensile Strength	5.90 - 7.205 MPa	855 - 1045 psi	Compound Property
Elongation at Break	340 - 410 %	340 - 410 %	Compound Property
Peel Strength	>= 0.526 kN/m	>= 3.00 pli	[ppi], Bond Strength

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	232 °C	450 °F
Minimum Service Temperature, Air	-56.7 °C	-70.0 °F

Electrical Properties	Metric	English	Comments
Dielectric Strength	>= 15.7 kV/mm	>= 400 kV/in

Processing Properties	Metric	English	Comments
Cure Time	15.0 min @Temperature 177 °C	0.250 hour @Temperature 350 °F	Recommended Cure Cycle
	120 min @Temperature 232 °C	2.00 hour @Temperature 450 °F	Recommended Postcure Cycle
Shelf Life	6.00 Month @Temperature <=23.9 °C	6.00 Month @Temperature <=75.0 °F	From date of manufacture

Descriptive Properties	Value	Comments
Color	Red
Total Product Weight (oz/yd2)	10 - 14
Uncoated Fabric Break Strength	150 lb/in	Warp Direction, Substrate Property
	70 lb/in	Fill Direction, Substrate Property