Arlon 25188T010 Silicone Rubber/Laminated ETFE Film
| Category | Polymer , Thermoset , Silicone , Silicone Rubber |
| Manufacturer | Arlon |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Arlon 25188T010 Silicone Rubber/Laminated ETFE Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Liner: 3 mil PTFE coated fiberglass; Side 1: uncured silicone rubber; Substrate: laminated ETFE film, treated for adhesion
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.10 g/cc | 1.10 g/cc | silicone property; Arlon SQA-TMS-024 |
| 1.70 g/cc | 1.70 g/cc | ETFE film property; ASTM D792 | |
| Thickness | 50.8 microns | 2.00 mil | ETFE film; Arlon SQA-TMS-003 |
| 203 microns | 8.00 mil | silicone; Arlon SQA-TMS-003 | |
| 254 microns | 10.0 mil | overall; Arlon SQA-TMS-003 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 18 | 18 | silicone property; ASTM D2240 |
| Hardness, Shore D | 67 | 67 | ETFE film property; ASTM D2240 |
| Tensile Strength, Ultimate | 6.89 MPa | 1000 psi | silicone property; ASTM D412 |
| 41.4 MPa | 6000 psi | ETFE film property; ASTM D638 | |
| Elongation at Break | 300 % | 300 % | ETFE film property; ASTM D638 |
| 950 % | 950 % | silicone property; ASTM D412 | |
| Modulus of Elasticity | 0.000517 GPa | 0.0750 ksi | Arlon SQA-TMS-008 |
| Poissons Ratio | 0.50 | 0.50 | silicone property |
| Adhesive Bond Strength | >= 0.0689 MPa | >= 10.0 psi | Arlon SQA-TMS-011 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 335 µm/m-°C @Temperature 20.0 °C |
186 µin/in-°F @Temperature 68.0 °F |
Silicone Property; ASTM E 831 |
| Thermal Conductivity | 0.190 W/m-K | 1.32 BTU-in/hr-ft²-°F | silicone property; Arlon SQA-TMS-022 |
| Maximum Service Temperature, Air | 154 °C | 310 °F | |
| Minimum Service Temperature, Air | -51.1 °C | -60.0 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | 49.2 kV/mm | 1250 kV/in | ASTM D149 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 15.0 min @Pressure 0.103 - 0.345 MPa, Temperature 121 °C |
0.250 hour @Pressure 15.0 - 50.0 psi, Temperature 250 °F |
|
| Shelf Life | 6.00 Month @Temperature 7.22 °C |
6.00 Month @Temperature 45.0 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | Translucent |
Users viewing this material also viewed the following:
- DuPont Performance Polymers Hypalon® 20 Chlorosulfonated Polyethylene Rubber, Mineral Filled Compound (discon
- Plenco 5350 Phenolic, Granular, Injection Molded
- Elastomer Engineering E50D Polyurethane
- Dow VORANOL™ 4240 Polyether Polyol
- Dynasol Calprene® H6215 Hydrogenated Rubber SEBS
- BASF Ultramid® A3EG5 25% Glass Filled PA66 (Conditioned)
- AorTech Biomaterials Elast-Eon™ E5-325 Biomedical Polyurethane Pellets
- A. Schulman POLYBATCH™ White B8750A Concentrate Based In HDPE
- Plenco 50045 PET, Pellet, Injection Molded, Natural Color (discontinued **)
Copyright © lookpolymers.com All Rights Reserved