ExxonMobil Bicor® 100 LTSC OPP Film

Category Polymer , Film , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade
Manufacturer Exxon Chemical
Trade Name Bicor®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil Bicor® 100 LTSC OPP Film.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: Bicor LTSC is a two-side coated OPP film which is designed for use in high-speed or demanding horizontal, fin seal, packaging applications. The low-temperature seal coating (LTSC) delivers a low seal initiation temperature, wide operating range for applications where accurate heat control is a problem or dwell times vary because of frequent machine speed changes. LTSC’s acrylic surface is excellent for surface printing and provides good aroma barrier. Availability: Latin America, North America and South AmericaKey Features:Wide sealing range with a low minim seal temperature (MST)Excellent seal strength and hot tackRobust performances on horizontal flowpack machinesExcellent humidity seal retention on LTSC sideGood flavor and aroma barrierOutstanding optical propertiesIdeal support for normal ink systemsFeatures:Acrylic CoatedFlavor & Aroma BarrierHumidity ResistantIn Lamination Lap SealableLTS CoatedVery Broad Seal RangeApplications:BakeryBiscuits/Cookie/CrackersConfectionery, ChocolateConfectionery, GumConfectionery, SugarFrozen FoodHealth and Beauty CareHousehold and DetergentsTobaccoUses:HFF Flexible PackagingProcessing Method: Inner Web Adhesive Lamination, Solvent Flexographic Printing, Solvent Rotogravure Printing, Surface Print Unsupported and Water-based Flexographic Printing Information provided by ExxonMobil Chemical
Physical Properties Metric English Comments
Water Vapor Transmission 5.70 g/m²/day
0.367 g/100 in²/day
38°C, 90% RH; ExxonMobil Method
Thickness 25.4 microns
1.00 mil
Nominal; ExxonMobil Method
Coating Weight 22.6 g/m²
14.1 lb/ream
ExxonMobil Method
Mechanical Properties Metric English Comments
Coefficient of Friction 0.23
0.23
ExxonMobil Method
Film Tensile Strength at Break, MD 138 MPa
20000 psi
20 in/min, 2.0 in Jaw Separation; ExxonMobil Method
Film Tensile Strength at Break, TD 207 MPa
30000 psi
20 in/min, 2.0 in Jaw Separation; ExxonMobil Method
Thermal Properties Metric English Comments
Shrinkage, MD 4.5 %
4.5 %
at 275°F; ExxonMobil Method
Shrinkage, TD 4.0 %
4.0 %
at 275°F; ExxonMobil Method
Optical Properties Metric English Comments
Haze 2.1 %
2.1 %
ExxonMobil Method
Gloss 90 %
90 %
45º, Acrylic Surface; ExxonMobil Method
Descriptive Properties Value Comments
Crimp Seal MST 160°F
LTSC/LTSC, 200g/in
Crimp Seal Strength 530 g/in
LTSC/LTSC, 260°F, 20psi, 3/4sec
Yield 31100 in2/lb