Addiplast Addinyl B2 ZV 50 Nylon 6, 50% Glass Filled
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 50% Glass Fiber Filled |
| Manufacturer | Addiplast |
| Trade Name | Addinyl |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Addiplast Addinyl B2 ZV 50 Nylon 6, 50% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Glass fiber reinforced, increased thermal aging stabilityInformation provided by Addiplast.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.55 g/cc | 0.0560 lb/in³ | ISO 1183/A |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 78 | 78 | Conditioned; ISO 868 |
| 84 | 84 | ISO 868 | |
| Tensile Strength at Break | 140 MPa | 20300 psi | Conditioned; ISO R 527 |
| 220 MPa | 31900 psi | ISO R 527 | |
| Elongation at Yield | 2.0 % | 2.0 % | ISO R 527 |
| 3.0 % | 3.0 % | Conditioned; ISO R 527 | |
| Modulus of Elasticity | 7.50 GPa | 1090 ksi | Conditioned; ISO 178 |
| 14.5 GPa | 2100 ksi | ISO 178 | |
| Izod Impact, Notched (ISO) | 20.0 kJ/m² | 9.52 ft-lb/in² | ISO 180/1A |
| 24.0 kJ/m² | 11.4 ft-lb/in² | Conditioned; ISO 180/1A | |
| Charpy Impact Unnotched | 7.00 J/cm² | 33.3 ft-lb/in² | ISO 179/IeU |
| 7.50 J/cm² | 35.7 ft-lb/in² | Conditioned; ISO 179/IeU | |
| Charpy Impact, Notched | 1.30 J/cm² | 6.19 ft-lb/in² | ISO 179/IeA |
| 2.00 J/cm² | 9.52 ft-lb/in² | Conditioned; ISO 179/IeA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 20.0 µm/m-°C | 11.1 µin/in-°F | ASTM E831 |
| Melting Point | 220 °C | 428 °F | ISO 3146/C2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 215 °C | 419 °F | ISO 75-2/AF |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+11 ohm-cm | 1.00e+11 ohm-cm | Conditioned; CEI 60093 |
| 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | CEI 60093 | |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | Conditioned; CEI 60243-1 |
| 35.0 kV/mm | 889 kV/in | CEI 60243-1 | |
| Comparative Tracking Index | 550 V | 550 V | CEI 60112/Solution A |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Wire & Cable Y594B Polyvinyl Chloride, Flexible (PVC, Flexible)
- SABIC PS 330 High Impact Polystyrene for Sheet Extrusion
- A. Schulman POLYBATCH™ Beige 6027E Concentrate Based In Polyethylene
- A. Schulman POLYBATCH™ White P8555 T2 Concentrate Based In Homopolymer Polypropylene
- Bapolene® 2292 Polyethylene Film Grade
- Axiall 10751 Wire & Cable Flexible PVC
- A. Schulman PP 1227E-01 Polypropylene High-Impact Polypropylene
Copyright © lookpolymers.com All Rights Reserved