Addiplast Addinyl A2 M20 V10 Nylon 66, Glass/Mineral Filled
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Glass/Mineral Filled |
| Manufacturer | Addiplast |
| Trade Name | Addinyl |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Addiplast Addinyl A2 M20 V10 Nylon 66, Glass/Mineral Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Mixed products with improved stiffness and good dimensional stability, low warpage.Information provided by Addiplast.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in³ | ISO 1183/A |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 80 | 80 | Conditioned; ISO 868 |
| 86 | 86 | ISO 868 | |
| Tensile Strength at Break | 75.0 MPa | 10900 psi | Conditioned; ISO R 527 |
| 120 MPa | 17400 psi | ISO R 527 | |
| Elongation at Yield | 4.5 % | 4.5 % | ISO R 527 |
| 6.0 % | 6.0 % | Conditioned; ISO R 527 | |
| Modulus of Elasticity | 3.70 GPa | 537 ksi | Conditioned; ISO 178 |
| 7.80 GPa | 1130 ksi | ISO 178 | |
| Izod Impact, Notched (ISO) | 4.50 kJ/m² | 2.14 ft-lb/in² | ISO 180/1A |
| 5.00 kJ/m² | 2.38 ft-lb/in² | Conditioned; ISO 180/1A | |
| Charpy Impact Unnotched | 3.50 J/cm² | 16.7 ft-lb/in² | ISO 179/IeU |
| 4.50 J/cm² | 21.4 ft-lb/in² | Conditioned; ISO 179/IeU | |
| Charpy Impact, Notched | 0.400 J/cm² | 1.90 ft-lb/in² | ISO 179/IeA |
| 0.500 J/cm² | 2.38 ft-lb/in² | Conditioned; ISO 179/IeA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 40.0 µm/m-°C | 22.2 µin/in-°F | ASTM E831 |
| Melting Point | 260 °C | 500 °F | ISO 3146/C2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 240 °C | 464 °F | ISO 75-2/AF |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | Conditioned; CEI 60093 |
| 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | CEI 60093 | |
| Comparative Tracking Index | 600 V | 600 V | CEI 60112/Solution A |
Users viewing this material also viewed the following:
- MV Labs DY800 Dy2O3 Dysprosium oxide
- MetalTek C81500 Chrome Copper High Conductivity
- Latrobe LSSâ„¢ D2 Tool Steel (ASTM D2)
- Solvay TECHNYL® C 216 V30 PA6, 30% glass fiber, DRY
- Schwartz Technical Plastics LAMINEX® 2000 Cotton Fabric, Phenolic Resin Impregnated, Coarse
- E-Polymers TEKAMID® TA250G60W , 62% Glass Fiber Reinforced PA66, DAM
- Braskem H 105 Injection Molding Polypropylene
- 3M 470L Electroplating Tape
- E-Polymers EFLEX® S4070 High Temperature
Copyright © lookpolymers.com All Rights Reserved