Aclo Accutech Polypropylene Homopolymer HP0336W20L1 Wollastonite Reinforced
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Mineral Reinforced |
| Manufacturer | Aclo Compounders |
| Trade Name | Accutech |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accutech Polypropylene Homopolymer HP0336W20L1 Wollastonite Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0090 cm/cm | 0.0090 in/in | MD; ASTM D955 |
| Melt Flow | 12 g/10 min | 12 g/10 min | ASTM D1238 |
| Ash | 20 % | 20 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 89 | 89 | ASTM D785 |
| Tensile Strength at Break | 25.0 MPa | 3630 psi | ASTM D638 |
| Tensile Strength, Yield | 34.0 MPa | 4930 psi | ASTM D638 |
| Elongation at Break | 20 % | 20 % | ASTM D638 |
| Elongation at Yield | 6.0 % | 6.0 % | ASTM D638 |
| Tensile Modulus | 2.099 GPa | 304.5 ksi | ASTM D638 |
| Flexural Strength | 40.0 MPa | 5800 psi | ASTM D790 |
| Flexural Modulus | 2.00 GPa | 290 ksi | ASTM D790 |
| Izod Impact, Notched | 0.400 J/cm | 0.750 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 66.1 °C | 151 °F |
Users viewing this material also viewed the following:
- RheTech Products HP522-286 15% Talc Reinforced High Performance Polypropylene Copolymer, UV Stabilized, ZUCA Medium Graphite
- Sylvin Technologies 9604-90 LMW Clear PVC for Injection Molding
- Styron CALIBREâ„¢ 7102-15 Polycarbonate
- Sylvin Technologies 6046 PVC Wire/Cable Compound
- TIMET TIMETAL® 21S Titanium Alloy (Ti-15Mo-3Nb-3Al-0.2Si, ASTM Grade 21); Aged at 538°C
- Fainplast Compounds GA 88/3 Flexible PVC, Flame Retardant Sheathing
- Clariant Renol PBTG30-L Polybutylene Terephthalate, 30% Glass Reinforced
- ChevronTexaco Bright-Cut® AD Metal Working Fluid
Copyright © lookpolymers.com All Rights Reserved