- HOME
- POLYMER SEARCH
- Thermoplastic
- Polypropylene (PP)
- Polypropylene, Flame Retardant
- Aclo Accuguard Polypropylene HP1369V2CSL Homopolymer Flame Retardant Copper Stabilized
Aclo Accuguard Polypropylene HP1369V2CSL Homopolymer Flame Retardant Copper Stabilized
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Flame Retardant |
| Manufacturer | Aclo Compounders |
| Trade Name | Accuguard |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accuguard Polypropylene HP1369V2CSL Homopolymer Flame Retardant Copper Stabilized.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.940 g/cc | 0.0340 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.014 cm/cm | 0.014 in/in | ASTM D955 |
| Melt Flow | 24 g/10 min | 24 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 300 MPa | 43500 psi | ASTM D638 |
| Tensile Strength, Yield | 32.0 MPa | 4640 psi | ASTM D638 |
| Tensile Modulus | 1.100 GPa | 159.5 ksi | ASTM D638 |
| Flexural Strength | 39.0 MPa | 5660 psi | ASTM D790 |
| Flexural Modulus | 1.300 GPa | 188.5 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 87.8 °C | 190 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 52.2 °C | 126 °F | |
| UL RTI, Electrical | 110 °C | 230 °F | |
| UL RTI, Mechanical with Impact | 110 °C | 230 °F | |
| UL RTI, Mechanical without Impact | 110 °C | 230 °F | |
| Flammability, UL94 | V-2 @Thickness 1.59 mm |
V-2 @Thickness 0.0625 in |
UL File #E99379 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® FXG161R PC (Europe-Africa-Middle East)
- SABIC Innovative Plastics LNP LUBRICOMP AL003 ABS
- Techmer ES HiFill® PA6/6 GF33 L BKN001 33% Glass Filled (Conditioned)
- Saint-Gobain Norton® T-200 Mechanical Grade PTFE Sheet (0.062" thick)
- Borealis Beta-PPR™ RA7050-GN Polypropylene-Random-Copolymer for Pressure Pipe Systems
- Asahi Glass AFLAS® 150P TFE/P Fluoroelastomer
- 3M PS102 Semi-gloss Paper Label Product
- Beijing Evergrow Resources PTFE Porous Film