- SABIC Innovative Plastics EXTEM UH1026 TPI Blend
SABIC Innovative Plastics EXTEM UH1026 TPI Blend
| Category | Polymer , Thermoplastic , Polyimide, Thermoplastic |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Extem |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics EXTEM UH1026 TPI Blend.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High heat amorphous TPI Blend, Chemical Resistant, High Flow, IR-Transparent
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.37 g/cc | 1.37 g/cc | ASTM D792 |
| Density | 1.37 g/cc | 0.0495 lb/in³ | ISO 1183 |
| Water Absorption | 0.39 % @Time 86400 sec |
0.39 % @Time 24.0 hour |
ISO 62-1 |
| Moisture Absorption | 0.110 % | 0.110 % | 50% RH, 24 hrs; ISO 62-4 |
| Water Absorption at Saturation | 2.1 % | 2.1 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0080 - 0.010 cm/cm @Thickness 3.20 mm |
0.0080 - 0.010 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 28 g/10 min @Load 6.60 kg, Temperature 400 °C |
28 g/10 min @Load 14.6 lb, Temperature 752 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 112 | 112 | ASTM D785 |
| Tensile Strength at Break | 108 MPa | 15700 psi | Type I, 5 mm/min; ASTM D638 |
| Tensile Strength | 68.0 MPa | 9860 psi | ASTM D638 |
| Tensile Strength, Yield | 115 MPa | 16700 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 9.0 % | 9.0 % | Type I, 5 mm/min; ASTM D638 |
| Elongation at Yield | 7.0 % | 7.0 % | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 3.41 GPa | 495 ksi | 5 mm/min; ASTM D638 |
| Flexural Strength | 109 MPa @Temperature 150 °C |
15800 psi @Temperature 302 °F |
ASTM D790 |
| Flexural Yield Strength | 175 MPa | 25400 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 3.43 GPa | 497 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 2.50 GPa @Temperature 150 °C |
363 ksi @Temperature 302 °F |
ASTM D790 | |
| Compressive Strength | 160 MPa | 23200 psi | SABIC Method |
| Izod Impact, Notched | 0.490 J/cm | 0.918 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 46.0 µm/m-°C @Temperature 23.0 - 150 °C |
25.6 µin/in-°F @Temperature 73.4 - 302 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 47.0 µm/m-°C @Temperature 23.0 - 150 °C |
26.1 µin/in-°F @Temperature 73.4 - 302 °F |
ASTM E 831 |
| Thermal Conductivity | 0.230 W/m-K | 1.60 BTU-in/hr-ft²-°F | ASTM C177 |
| Deflection Temperature at 0.46 MPa (66 psi) | 257 °C @Thickness 3.20 mm |
495 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 234 °C @Thickness 3.20 mm |
453 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Oxygen Index | 47 % | 47 % | ISO 4589 |
| Glow Wire Test | 875 °C | 1610 °F | IEC 60695-2-13 |
| 930 °C | 1710 °F | IEC 60695-2-13 | |
| 960 °C @Thickness 0.750 mm |
1760 °F @Thickness 0.0295 in |
IEC 60695-2-12 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | 90 % | 90 % | transparent; thickness not quantified |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 3.5 @Frequency 1.00e+7 Hz |
3.5 @Frequency 1.00e+7 Hz |
ASTM D150 |
| Dielectric Strength | 54.0 kV/mm @Thickness 0.800 mm |
1370 kV/in @Thickness 0.0315 in |
in air; ASTM D149 |
| Dissipation Factor | 0.00050 @Frequency 1.00e+7 Hz |
0.00050 @Frequency 1.00e+7 Hz |
ASTM D150 |
| Comparative Tracking Index | 100 - 175 V | 100 - 175 V | UL 746A |
| High Amp Arc Ignition, HAI | >= 120 arcs | >= 120 arcs | UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | 80.0 - 150 mm/min | 3.15 - 5.91 in/min | UL 746A |
| Descriptive Properties | Value | Comments |
|---|---|---|
| OSU total heat release (2 minute test) | 0kW-min/m^2 | FAR 25.853 |
| OSU peak heat release rate (5 minute test) | 21kW/m^2 | FAR 25.853 |
| Strength Retention after 1,000 hr aging in air at 240°C | 88% | UL 746B |
| Strength Retention after 2,000 hr aging in air at 240°C | 68% | UL 746B |
Users viewing this material also viewed the following:
- Materion Beryllium Copper Alloy 25 Tube; AT (TF00) Temper; over 76 mm o.d. (UNS C17200)
- Momentive Performance Materials Siloprenâ„¢ Electro 242-3 Electrically Insulating Liquid Silicone Rubber
- Latrobe Lescalloy® 4340 VAC-ARC ; 10.5" square High Strength Alloy Steel
- Spartech Royalstatâ„¢ R635 ABS/Polyolefin Static Control Sheet
- Teknor Apex APEX® 130-P Polyvinyl Chloride, Flexible
- Wellman Wellamid® GF10-42LI4-N-Gray 10% Glass Reinforced, Toughened Nylon 6
- BASF Elastollan 880 AN TPUR
- Plastics Group Polifil® T-30 30% Talc-Reinforced Polypropylene
- Haynes 230® alloy, 50% cold reduction, 1066°C anneal for 5 minutes
- Fluorocarbon Rubber (FPM), Low Temperature Grade
Copyright © lookpolymers.com All Rights Reserved