Polyram RamShine PV300G2 ABS, 10% Glass Fiber
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), 10% Glass Fiber Filled |
| Manufacturer | Polyram |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram RamShine PV300G2 ABS, 10% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
10% glass fiber reinforced ABS for injection molding applicationsInformation provided by Polyram Ram On Ind.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | DIN 53479 |
| Water Absorption | 0.14 % | 0.14 % | DIN 53495 |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | |
| Melt Flow | 10 g/10 min @Load 10.0 kg, Temperature 220 °C |
10 g/10 min @Load 22.0 lb, Temperature 428 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 65.0 MPa | 9430 psi | ASTM-D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM-D638 |
| Tensile Modulus | 3.30 GPa | 479 ksi | ASTM-D790 |
| Flexural Strength | 80.0 MPa | 11600 psi | ASTM-D790 |
| Flexural Modulus | 3.00 GPa | 435 ksi | ASTM-D790 |
| Izod Impact, Notched | 0.850 J/cm @Temperature 23.0 °C |
1.59 ft-lb/in @Temperature 73.4 °F |
ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | DIN 53461 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | DIN 53482 |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | DIN 53482 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics LNP LUBRICOMP UCL36S PPA (Asia Pacific)
- SABIC Innovative Plastics ULTEM CRS5011 PEI (Asia Pacific)
- Samsung Cheil Industries Infino® HI-1001B PC/ABS, Unreinforced
- A. Schulman POLYBATCH™ Green 3015 Concentrate Based In Polyethylene
- A. Schulman POLYBATCH™ Green 3015 Concentrate Based In Polyethylene
- Covestro Makroblend® DP 2-7655 Polycarbonate + PET, Mineral Filled Impact Grade
- Axiall 8779 Moldings & Extrusions Flexible PVC
- LG Chemical HI835H PMMA, Impact Resistant Grade
Copyright © lookpolymers.com All Rights Reserved