| Haynes 214® alloy sheet |
Superalloy |
|
| Haynes 214® alloy, 0% cold reduction |
Superalloy |
|
| Haynes 214® alloy, 10% cold reduction |
Superalloy |
|
| Haynes 214® alloy, 10% cold reduction, 925°C for 5 minutes |
Superalloy |
|
| Haynes 214® alloy, 10% cold reduction, 980°C (1800°F) for 5 minutes |
Superalloy |
|
| Haynes 214® alloy, 20% cold reduction |
Superalloy |
|
| Haynes 214® alloy, 20% cold reduction, 1095°C (2000°F) for 5 minutes |
Superalloy |
|
| Haynes 214® alloy, 20% cold reduction, 925°C for 5 minutes |
Superalloy |
|
| Haynes 214® alloy, 20% cold reduction, 980°C (1800°F) for 5 minutes |
Superalloy |
|
| Haynes 214® alloy, 30% cold reduction, 1095°C (2000°F) for 5 minutes |
Superalloy |
|
| Haynes 214® alloy, 30% cold reduction, 925°C for 5 minutes |
Superalloy |
|
| Haynes 214® alloy, 40% cold reduction |
Superalloy |
|
| Haynes 214® alloy, 40% cold reduction, 1095°C (2000°F) for 5 minutes |
Superalloy |
|
| Haynes 214® alloy, 40% cold reduction, 925°C for 5 minutes |
Superalloy |
|
| Haynes 214® alloy, 40% cold reduction, 980°C (1800°F) for 5 minutes |
Superalloy |
|
| Haynes 214® alloy, 50% cold reduction |
Superalloy |
|
| Haynes 214® alloy, 50% cold reduction, 1095°C (2000°F) for 5 minutes |
Superalloy |
|
| Haynes 214® alloy, 50% cold reduction, 925°C for 5 minutes |
Superalloy |
|
| Haynes 214® alloy, 50% cold reduction, 980°C (1800°F) for 5 minutes |
Superalloy |
|
| Haynes 214® alloy, cold rolled annealed sheet 2.0-3.2 mm thick |
Superalloy |
|
| Haynes 214® alloy, hot rolled solution annealed plate 12.7 mm (1/2 in.) thick |
Superalloy |
|
| Haynes 214® alloy, sheet, 100 hours exposure at 760°C (1400°F) |
Superalloy |
|
| Haynes 214® alloy, sheet, 100 hours exposure at 870°C (1600°F) |
Superalloy |
|
| Haynes 214® alloy, sheet, 100 hours exposure at 980°C (1800°F) |
Superalloy |
|
| Haynes 214® alloy, sheet, 1000 hours exposure at 760°C (1400°F) |
Superalloy |
|
| Haynes 214® alloy, sheet, 1000 hours exposure at 870°C (1600°F) |
Superalloy |
|
| Haynes 214® alloy, sheet, 1000 hours exposure at 980°C (1800°F) |
Superalloy |
|
| Haynes 214® alloy, sheet, 32 hours exposure at 760°C (1400°F) |
Superalloy |
|
| Haynes 214® alloy, sheet, 32 hours exposure at 870°C (1600°F) |
Superalloy |
|
| Haynes 214® alloy, sheet, 32 hours exposure at 980°C (1800°F) |
Superalloy |
|
| Haynes 230® alloy plate |
Superalloy |
|
| Haynes 230® alloy plate, 1000 hours exposure at 649°C (1200°F) |
Superalloy |
|
| Haynes 230® alloy plate, 4000 hours exposure at 649°C (1200°F) |
Superalloy |
|
| Haynes 230® alloy, 0% cold reduction |
Superalloy |
|
| Haynes 230® alloy, 10% cold reduction |
Superalloy |
|
| Haynes 230® alloy, 10% cold reduction, 1066°C anneal for 5 minutes |
Superalloy |
|
| Haynes 230® alloy, 10% cold reduction, 1121°C anneal for 5 minutes |
Superalloy |
|
| Haynes 230® alloy, 10% cold reduction, 1177°C anneal for 5 minutes |
Superalloy |
|
| Haynes 230® alloy, 20% cold reduction |
Superalloy |
|
| Haynes 230® alloy, 20% cold reduction, 1066°C anneal for 5 minutes |
Superalloy |
|
| Haynes 230® alloy, 20% cold reduction, 1121°C anneal for 5 minutes |
Superalloy |
|
| Haynes 230® alloy, 20% cold reduction, 1177°C anneal for 5 minutes |
Superalloy |
|
| Haynes 230® alloy, 30% cold reduction |
Superalloy |
|
| Haynes 230® alloy, 30% cold reduction, 1066°C anneal for 5 minutes |
Superalloy |
|
| Haynes 230® alloy, 30% cold reduction, 1121°C anneal for 5 minutes |
Superalloy |
|
| Haynes 230® alloy, 30% cold reduction, 1177°C anneal for 5 minutes |
Superalloy |
|
| Haynes 230® alloy, 40% cold reduction |
Superalloy |
|
| Haynes 230® alloy, 40% cold reduction, 1066°C anneal for 5 minutes |
Superalloy |
|
| Haynes 230® alloy, 40% cold reduction, 1121°C anneal for 5 minutes |
Superalloy |
|
| Haynes 230® alloy, 40% cold reduction, 1177°C anneal for 5 minutes |
Superalloy |
|
| Haynes 230® alloy, plate, 1000 hours exposure at 871°C (1600°F) |
Superalloy |
|
| Haynes 230® alloy, plate, 4000 hours exposure at 760°C (1400°F) |
Superalloy |
|
| Haynes 242® alloy, cold reduced sheet, annealed, 20% cold work |
Superalloy |
|
| Haynes Hastelloy® G-30® alloy, all-weld metal, GTAW weld 3.2 mm diameter filler wire |
Superalloy |
Hastelloy®
|
| Haynes Hastelloy® G-30® alloy, mill annealed |
Superalloy |
Hastelloy®
|
| Haynes Hastelloy® G-35® Nickel Alloy Plate, Annealed at 2025°F (1107°C) |
Nickel Alloy |
Hastelloy®
|
| Haynes Hastelloy® G-35® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) Plate |
Nickel Alloy |
Hastelloy®
|
| Haynes Hastelloy® Hybrid-BC1® Nickel Alloy Bar, Hot Rolled and Solution Annealed |
Nickel Alloy |
Hastelloy®
|
| Haynes Hastelloy® Hybrid-BC1® Nickel Alloy Shielded Metal Arc Welded (SMAW) Plate |
Nickel Alloy |
Hastelloy®
|
| Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 538°C (1000°F) |
Superalloy |
Hastelloy®
|
| Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 704°C (1300°F) |
Superalloy |
Hastelloy®
|
| Haynes Hastelloy® N, 1.6 mm sheet, heat treated at 1175°C, welded and tested as welded |
Superalloy |
Hastelloy®
|
| Haynes Hastelloy® N, weld metal as welded |
Superalloy |
Hastelloy®
|
| Haynes Hastelloy® N, weld metal, aged 500 hours at 649°C (1200°F) |
Superalloy |
Hastelloy®
|
| Haynes Hastelloy® S alloy, flat products |
Superalloy |
Hastelloy®
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 538°C (1000°F), aged 1000 hours |
Superalloy |
Hastelloy®
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 538°C (1000°F), aged 16000 hours |
Superalloy |
Hastelloy®
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 538°C (1000°F), aged 4000 hours |
Superalloy |
Hastelloy®
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 538°C (1000°F), aged 8000 hours |
Superalloy |
Hastelloy®
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 649°C (1200°F), aged 16000 hours |
Superalloy |
Hastelloy®
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 649°C (1200°F), aged 4000 hours |
Superalloy |
Hastelloy®
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 649°C (1200°F), aged 8000 hours |
Superalloy |
Hastelloy®
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 760°C (1400°F), aged 16000 hours |
Superalloy |
Hastelloy®
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 760°C (1400°F), aged 4000 hours |
Superalloy |
Hastelloy®
|
| Haynes Hastelloy® S alloy, flat products, solution heat-treated at 760°C (1400°F), aged 8000 hours |
Superalloy |
Hastelloy®
|
| Haynes Hastelloy® S alloy, gas tungsten arc welded |
Superalloy |
Hastelloy®
|
| Haynes Hastelloy® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick |
Superalloy |
Hastelloy®
|
| Haynes Hastelloy® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick, aged 1000 hours |
Superalloy |
Hastelloy®
|
| Haynes Hastelloy® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick, aged 16000 hours |
Superalloy |
Hastelloy®
|
| Haynes Hastelloy® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick, aged at 649°C (1200°F) for 8000 hours |
Superalloy |
Hastelloy®
|
| Haynes Hastelloy® S alloy, gas tungsten arc welded, aged 1300 hours |
Superalloy |
Hastelloy®
|
| Haynes Hastelloy® S alloy, gas tungsten arc welded, aged at 538°C (1000°F) for 4000 hours |
Superalloy |
Hastelloy®
|
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 1000 hours |
Superalloy |
Hastelloy®
|
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 16000 hours |
Superalloy |
Hastelloy®
|
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 4000 hours |
Superalloy |
Hastelloy®
|
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 427°C (800°F), aged 8000 hours |
Superalloy |
Hastelloy®
|
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 16000 hours |
Superalloy |
Hastelloy®
|
| Haynes Hastelloy® S alloy, plate 12.7 mm (1/2 in.) thick, solution heat-treated at 871°C (1600°F), aged 8000 hours |
Superalloy |
Hastelloy®
|
| Haynes Hastelloy® S alloy, weld metal, aged 1000 hours |
Superalloy |
Hastelloy®
|
| Haynes Hastelloy® S alloy, weld metal, aged 16000 hours |
Superalloy |
Hastelloy®
|
| Haynes Hastelloy® S alloy, weld metal, aged 4000 hours |
Superalloy |
Hastelloy®
|
| Haynes Hastelloy® S alloy, weld metal, aged at 649°C (1200°F) for 1000 hours |
Superalloy |
Hastelloy®
|
| Haynes Hastelloy® W alloy as a weld filler, base metal Alloy 188/ Multimet alloy 12.7 mm plate weldments |
Superalloy |
Hastelloy®
|
| Haynes Hastelloy® W alloy as a weld filler, base metal Alloy 625/ Alloy 718 12.7 mm plate weldments |
Superalloy |
Hastelloy®
|
| Haynes Hastelloy® W alloy as a weld filler, base metal Carbon steel 12.7 mm plate weldments |
Superalloy |
Hastelloy®
|
| Haynes Hastelloy® W alloy as a weld filler, base metal Multimet alloy 12.7 mm plate weldment |
Superalloy |
Hastelloy®
|
| Haynes Hastelloy® W alloy as a weld filler, base metal Type 304 Carbon steel 12.7 mm plate weldments |
Superalloy |
Hastelloy®
|
| Haynes Hastelloy® W alloy as a weld filler, base metal Type 304 Stainless steel 12.7 mm plate weldments |
Superalloy |
Hastelloy®
|
| Haynes Hastelloy® W alloy, gas metal arc welds, aged 1000 hours at 650°C (1200°F) |
Superalloy |
Hastelloy®
|
| Haynes Hastelloy® W alloy, gas metal arc welds, as-welded |
Superalloy |
Hastelloy®
|