- Haynes Hastelloy® W alloy, gas metal arc welds, as-welded
Haynes Hastelloy® W alloy, gas metal arc welds, as-welded
| Category | Metal , Nonferrous Metal , Nickel Alloy , Superalloy |
| Manufacturer | Haynes International, Inc. |
| Trade Name | Hastelloy® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Haynes Hastelloy® W alloy, gas metal arc welds, as-welded.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Solid solution-strengthened developed as a filler metal for welding of dissimilar alloys. Applications include excellent dissimilar welding characteristics in the gas turbine, aerospace, and chemical process industries.Data provided by the manufacturer, Haynes International, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 9.00 g/cc | 0.325 lb/in³ | at RT |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 870 MPa | 126000 psi | |
| 310 MPa @Temperature 870 °C |
45000 psi @Temperature 1600 °F |
||
| Tensile Strength, Yield | 555 MPa | 80500 psi | |
| 285 MPa @Temperature 870 °C |
41300 psi @Temperature 1600 °F |
||
| Elongation at Break | 38 % | 38 % | |
| 41 % @Temperature 870 °C |
41 % @Temperature 1600 °F |
||
| Reduction of Area | 32 % | 32 % | |
| 42 % @Temperature 870 °C |
42 % @Temperature 1600 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 13.2 µm/m-°C @Temperature 20.0 - 600 °C |
7.33 µin/in-°F @Temperature 68.0 - 1110 °F |
|
| 13.2 µm/m-°C @Temperature 20.0 - 500 °C |
7.33 µin/in-°F @Temperature 68.0 - 932 °F |
||
| 13.5 µm/m-°C @Temperature 20.0 - 700 °C |
7.50 µin/in-°F @Temperature 68.0 - 1290 °F |
||
| 14.2 µm/m-°C @Temperature 20.0 - 800 °C |
7.89 µin/in-°F @Temperature 68.0 - 1470 °F |
||
| 14.8 µm/m-°C @Temperature 20.0 - 900 °C |
8.22 µin/in-°F @Temperature 68.0 - 1650 °F |
||
| 15.3 µm/m-°C @Temperature 20.0 - 1000 °C |
8.50 µin/in-°F @Temperature 68.0 - 1830 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Carbon, C | <= 0.12 % | <= 0.12 % | |
| Chromium, Cr | 5.0 % | 5.0 % | |
| Cobalt, Co | 2.5 % | 2.5 % | |
| Iron, Fe | 6.0 % | 6.0 % | |
| Manganese, Mn | <= 1.0 % | <= 1.0 % | |
| Molybdenum, Mo | 24 % | 24 % | |
| Nickel, Ni | 63 % | 63 % | |
| Silicon, Si | <= 1.0 % | <= 1.0 % | |
| Vanadium, V | <= 0.60 % | <= 0.60 % |
Users viewing this material also viewed the following:
- RheTech Products M12P256-01 12% Mica Reinforced Polypropylene Copolymer, Black
- JPJ Technologies 1600J HDPE Extrusion
- Tisan TISARBON® Flame Retardant (V0) Polycarbonate
- Topas Advanced Polymers TOPAS® 9506F-500 Cyclic Olefin Copolymer (COC)
- ExxonMobil 223 Mobilgrease XHP Series
- Chesterton ARC NVE SYSTEM Vinyl Ester Lining
- 3M Scotch-Weld™ EC100 General Purpose Instant Adhesive
- 3M Scotch-Weld™ MG77 AC Medical Grade Instant Adhesive Primer
- Solvay Specialty Polymers Amodel® AS-4133 L Polyphthalamide (PPA) (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved