- Haynes Hastelloy® W alloy as a weld filler, base metal Alloy 188/ Multimet alloy 12.7 mm plate weldments
Haynes Hastelloy® W alloy as a weld filler, base metal Alloy 188/ Multimet alloy 12.7 mm plate weldments
| Category | Metal , Nonferrous Metal , Nickel Alloy , Superalloy |
| Manufacturer | Haynes International, Inc. |
| Trade Name | Hastelloy® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Haynes Hastelloy® W alloy as a weld filler, base metal Alloy 188/ Multimet alloy 12.7 mm plate weldments.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Solid solution-strengthened developed as a filler metal for welding of dissimilar alloys. Applications include excellent dissimilar welding characteristics in the gas turbine, aerospace, and chemical process industries.Data provided by the manufacturer, Haynes International, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 9.00 g/cc | 0.325 lb/in³ | at RT |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 805 MPa | 117000 psi | |
| 320 MPa @Temperature 870 °C |
46400 psi @Temperature 1600 °F |
||
| Tensile Strength, Yield | 455 MPa | 66000 psi | |
| 235 MPa @Temperature 870 °C |
34100 psi @Temperature 1600 °F |
||
| Elongation at Break | 35 % | 35 % | Failures in base metal. |
| 19 % @Temperature 870 °C |
19 % @Temperature 1600 °F |
Failures in base metal. | |
| Reduction of Area | 64 % | 64 % | Failures in base metal. |
| 19 % @Temperature 870 °C |
19 % @Temperature 1600 °F |
Failures in base metal. |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 13.2 µm/m-°C @Temperature 20.0 - 600 °C |
7.33 µin/in-°F @Temperature 68.0 - 1110 °F |
|
| 13.2 µm/m-°C @Temperature 20.0 - 500 °C |
7.33 µin/in-°F @Temperature 68.0 - 932 °F |
||
| 13.5 µm/m-°C @Temperature 20.0 - 700 °C |
7.50 µin/in-°F @Temperature 68.0 - 1290 °F |
||
| 14.2 µm/m-°C @Temperature 20.0 - 800 °C |
7.89 µin/in-°F @Temperature 68.0 - 1470 °F |
||
| 14.8 µm/m-°C @Temperature 20.0 - 900 °C |
8.22 µin/in-°F @Temperature 68.0 - 1650 °F |
||
| 15.3 µm/m-°C @Temperature 20.0 - 1000 °C |
8.50 µin/in-°F @Temperature 68.0 - 1830 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Carbon, C | <= 0.12 % | <= 0.12 % | |
| Chromium, Cr | 5.0 % | 5.0 % | |
| Cobalt, Co | 2.5 % | 2.5 % | |
| Iron, Fe | 6.0 % | 6.0 % | |
| Manganese, Mn | <= 1.0 % | <= 1.0 % | |
| Molybdenum, Mo | 24 % | 24 % | |
| Nickel, Ni | 63 % | 63 % | |
| Silicon, Si | <= 1.0 % | <= 1.0 % | |
| Vanadium, V | <= 0.60 % | <= 0.60 % |
Users viewing this material also viewed the following:
- Chevron Phillips HiD® 9502H - 9503H High Performance Series HDPE Blow Molding Resin (discontinued **)
- Albis Plastics Cellulose Acetate Butyrate B902 (UV Inhibitor Added), 22% Plasticizer (discontinued **)
- Solvay Specialty Polymers Diofan® B 204 Polyvinylidene Chloride (PVDC)
- Master Bond UV15-42C One Component, Optically Clear, Tough UV Curable System
- Universal Wire Works HP9-4-20 (AMS 6468) Low Alloy Steel Welding Wire
- Formosa Plastics Formolene® 2610A Compounding and Injection Molding Polypropylene
- Westlake Plastics PEEK
- Aaron Industries AAROPRENE® TFPP 2040 Talc Filled Polypropylene
- A. Schulman POLYBATCH™ Red 5500 Concentrate Based In Polyethylene
Copyright © lookpolymers.com All Rights Reserved