Haynes 214® alloy, hot rolled solution annealed plate 12.7 mm (1/2 in.) thick

Category Metal , Nonferrous Metal , Nickel Alloy , Superalloy
Manufacturer Haynes International, Inc.
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Haynes 214® alloy, hot rolled solution annealed plate 12.7 mm (1/2 in.) thick.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Intended principally for use at temperatures of 955°C and above, exhibits resistance to oxidation that exceeds virtually all conventional heat-resistant wrought alloys. Applications include mesh belts, trays, and fixtures for firing of pottery and fine china, and the heat treatment of electronic devices and technical grade ceramics, used for foil construction honeycomb seals, combustor splash plates, and other static oxidation- limited parts, catalytic converter internals, burner cup material in auxiliary heaters for military vehicles, refractory anchors, furnace flame hoods, and rotary calciners for processing chloride compounds, and as hospital waste incinerator internals.Data provided by the manufacturer, Haynes International, Inc.
Physical Properties Metric English Comments
Density 8.05 g/cc
0.291 lb/in³
at RT
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 960 MPa
139000 psi
34.0 MPa

@Temperature 1205 °C
 4930 psi

@Temperature 2201 °F
46.0 MPa

@Temperature 1150 °C
 6670 psi

@Temperature 2100 °F
62.0 MPa

@Temperature 1095 °C
 8990 psi

@Temperature 2003 °F
115 MPa

@Temperature 980 °C
 16700 psi

@Temperature 1800 °F
460 MPa

@Temperature 870 °C
 66700 psi

@Temperature 1600 °F
670 MPa

@Temperature 760 °C
 97200 psi

@Temperature 1400 °F
790 MPa

@Temperature 650 °C
 115000 psi

@Temperature 1200 °F
825 MPa

@Temperature 540 °C
 120000 psi

@Temperature 1000 °F
Tensile Strength, Yield 565 MPa

@Strain 0.200 %
 81900 psi

@Strain 0.200 %
10.0 MPa

@Strain 0.200 %,
Temperature 1205 °C
 1450 psi

@Strain 0.200 %,
Temperature 2201 °F
14.0 MPa

@Strain 0.200 %,
Temperature 1150 °C
 2030 psi

@Strain 0.200 %,
Temperature 2100 °F
29.0 MPa

@Strain 0.200 %,
Temperature 1095 °C
 4210 psi

@Strain 0.200 %,
Temperature 2003 °F
58.0 MPa

@Strain 0.200 %,
Temperature 980 °C
 8410 psi

@Strain 0.200 %,
Temperature 1800 °F
345 MPa

@Strain 0.200 %,
Temperature 870 °C
 50000 psi

@Strain 0.200 %,
Temperature 1600 °F
495 MPa

@Strain 0.200 %,
Temperature 540 °C
 71800 psi

@Strain 0.200 %,
Temperature 1000 °F
505 MPa

@Strain 0.200 %,
Temperature 760 °C
 73200 psi

@Strain 0.200 %,
Temperature 1400 °F
525 MPa

@Strain 0.200 %,
Temperature 650 °C
 76100 psi

@Strain 0.200 %,
Temperature 1200 °F
Elongation at Break 42.8 %
42.8 %
in 31.8 mm
23.1 %

@Temperature 760 °C
 23.1 %

@Temperature 1400 °F
 in 31.8 mm
33 %

@Temperature 650 °C
 33 %

@Temperature 1200 °F
 in 31.8 mm
33.6 %

@Temperature 870 °C
 33.6 %

@Temperature 1600 °F
 in 31.8 mm
47.8 %

@Temperature 540 °C
 47.8 %

@Temperature 1000 °F
 in 31.8 mm
86.4 %

@Temperature 980 °C
 86.4 %

@Temperature 1800 °F
 in 31.8 mm
88.6 %

@Temperature 1095 °C
 88.6 %

@Temperature 2003 °F
 in 31.8 mm
91.5 %

@Temperature 1205 °C
 91.5 %

@Temperature 2201 °F
 in 31.8 mm
99.4 %

@Temperature 1150 °C
 99.4 %

@Temperature 2100 °F
 in 31.8 mm
Modulus of Elasticity 218 GPa
31600 ksi
RT
137 GPa

@Temperature 1000 °C
 19900 ksi

@Temperature 1830 °F
151 GPa

@Temperature 900 °C
 21900 ksi

@Temperature 1650 °F
162 GPa

@Temperature 800 °C
 23500 ksi

@Temperature 1470 °F
170 GPa

@Temperature 700 °C
 24700 ksi

@Temperature 1290 °F
177 GPa

@Temperature 600 °C
 25700 ksi

@Temperature 1110 °F
184 GPa

@Temperature 500 °C
 26700 ksi

@Temperature 932 °F
190 GPa

@Temperature 400 °C
 27600 ksi

@Temperature 752 °F
199 GPa

@Temperature 300 °C
 28900 ksi

@Temperature 572 °F
204 GPa

@Temperature 200 °C
 29600 ksi

@Temperature 392 °F
210 GPa

@Temperature 100 °C
 30500 ksi

@Temperature 212 °F
Thermal Properties Metric English Comments
CTE, linear 13.3 µm/m-°C

@Temperature 25.0 - 200 °C
 7.39 µin/in-°F

@Temperature 77.0 - 392 °F
13.6 µm/m-°C

@Temperature 25.0 - 300 °C
 7.56 µin/in-°F

@Temperature 77.0 - 572 °F
14.1 µm/m-°C

@Temperature 25.0 - 400 °C
 7.83 µin/in-°F

@Temperature 77.0 - 752 °F
14.6 µm/m-°C

@Temperature 25.0 - 500 °C
 8.11 µin/in-°F

@Temperature 77.0 - 932 °F
15.2 µm/m-°C

@Temperature 25.0 - 600 °C
 8.44 µin/in-°F

@Temperature 77.0 - 1110 °F
15.8 µm/m-°C

@Temperature 25.0 - 700 °C
 8.78 µin/in-°F

@Temperature 77.0 - 1290 °F
16.6 µm/m-°C

@Temperature 25.0 - 800 °C
 9.22 µin/in-°F

@Temperature 77.0 - 1470 °F
17.6 µm/m-°C

@Temperature 25.0 - 900 °C
 9.78 µin/in-°F

@Temperature 77.0 - 1650 °F
18.6 µm/m-°C

@Temperature 25.0 - 1000 °C
 10.3 µin/in-°F

@Temperature 77.0 - 1830 °F
Specific Heat Capacity 0.452 J/g-°C
0.108 BTU/lb-°F
RT
0.470 J/g-°C

@Temperature 100 °C
 0.112 BTU/lb-°F

@Temperature 212 °F
0.493 J/g-°C

@Temperature 200 °C
 0.118 BTU/lb-°F

@Temperature 392 °F
0.515 J/g-°C

@Temperature 300 °C
 0.123 BTU/lb-°F

@Temperature 572 °F
Electrical Properties Metric English Comments
Electrical Resistivity 0.0001359 ohm-cm
0.0001359 ohm-cm
RT
0.0001209 ohm-cm

@Temperature 1050 °C
 0.0001209 ohm-cm

@Temperature 1920 °F
0.000121 ohm-cm

@Temperature 1100 °C
 0.000121 ohm-cm

@Temperature 2010 °F
0.0001216 ohm-cm

@Temperature 1000 °C
 0.0001216 ohm-cm

@Temperature 1830 °F
0.0001219 ohm-cm

@Temperature 1150 °C
 0.0001219 ohm-cm

@Temperature 2100 °F
0.0001229 ohm-cm

@Temperature 1200 °C
 0.0001229 ohm-cm

@Temperature 2190 °F
0.0001249 ohm-cm

@Temperature 900 °C
 0.0001249 ohm-cm

@Temperature 1650 °F
0.0001292 ohm-cm

@Temperature 800 °C
 0.0001292 ohm-cm

@Temperature 1470 °F
0.0001337 ohm-cm

@Temperature 700 °C
 0.0001337 ohm-cm

@Temperature 1290 °F
0.0001368 ohm-cm

@Temperature 600 °C
 0.0001368 ohm-cm

@Temperature 1110 °F
0.0001369 ohm-cm

@Temperature 100 °C
 0.0001369 ohm-cm

@Temperature 212 °F
0.0001369 ohm-cm

@Temperature 200 °C
 0.0001369 ohm-cm

@Temperature 392 °F
0.0001369 ohm-cm

@Temperature 300 °C
 0.0001369 ohm-cm

@Temperature 572 °F
0.0001369 ohm-cm

@Temperature 300 °C
 0.0001369 ohm-cm

@Temperature 572 °F
0.0001377 ohm-cm

@Temperature 400 °C
 0.0001377 ohm-cm

@Temperature 752 °F
0.0001379 ohm-cm

@Temperature 500 °C
 0.0001379 ohm-cm

@Temperature 932 °F