Manufacturer : Haynes International, Inc. Product List

Category

Cobalt Alloy	Superalloy	Nickel Alloy
Iron Base	Alpha/Near Alpha Titanium Alloy

Trade Name

Hastelloy®

Multimet®

Ultimet®

Tips：Up to 100 items are displayed.

PRODUCT NO.	Category	Trade Name
Haynes 188 alloy, 10% cold reduction, 3.2 mm thick sheet, 1065Â°C for 5 minutes	Superalloy
Haynes 188 alloy, 40% cold reduction, 3.2 mm thick sheet	Superalloy
Haynes 188 alloy, plate at RT after 4000 hours at 870Â°C (1600Â°F)	Superalloy
Haynes 214Â® alloy, 30% cold reduction, 1095Â°C (2000Â°F) for 5 minutes	Superalloy
Haynes 214Â® alloy, 50% cold reduction, 980Â°C (1800Â°F) for 5 minutes	Superalloy
Haynes 230Â® alloy plate	Superalloy
Haynes 230Â® alloy, 0% cold reduction	Superalloy
Haynes HastelloyÂ® S alloy, flat products	Superalloy	Hastelloy®
Haynes HastelloyÂ® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick	Superalloy	Hastelloy®
Haynes HastelloyÂ® W alloy, gas tungsten arc welds, aged 1000 hours at 650Â°C (1200Â°F)	Superalloy	Hastelloy®
Haynes HastelloyÂ® X alloy, sheet	Superalloy	Hastelloy®
Haynes HR-120Â® alloy, solution heat-treated	Iron Base
Haynes HR-120Â® alloy, solution heat-treated aged at 1400Â°F for 1000 hours	Iron Base
Haynes MultimetÂ® alloy, 1.6 mm thick sheet, 1177Â°C heat treatment, rapid air cooled	Iron Base	Multimet®
Haynes MultimetÂ® alloy, 6.15 mm hot-rolled bar, 30% cold reduction	Iron Base	Multimet®
Haynes UltimetÂ® alloy, aged 1000 hours at 316Â°C	Superalloy	Ultimet®
Haynes UltimetÂ® alloy, aged 1000 hours at 871Â°C (1600Â°F)	Superalloy	Ultimet®
Haynes UltimetÂ® alloy, aged 1000 hours at 982Â°C	Superalloy	Ultimet®
Haynes 230Â® alloy, plate, 8000 hours exposure at 760Â°C (1400Â°F)	Superalloy
Haynes 25 alloy, room temperature after 25% cold reduction, 1065Â°C anneal for 5 minutes	Superalloy
Haynes 25 alloy, room temperature sheet after 100 hours of 760Â°C exposure	Superalloy
Haynes 282Â® Nickel Alloy Sheet, Solution Annealed and Age-hardened	Nickel Alloy
Haynes 282Â® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) All Weld Cruciform	Nickel Alloy
Haynes 556Â® alloy, 0% cold reduction, 1010Â°C anneal for 5 minutes	Iron Base
Haynes 556Â® alloy, 0% cold reduction, 1065Â°C anneal for 5 minutes	Iron Base
Haynes 556Â® alloy, 0% cold reduction, 1121Â°C anneal for 5 minutes	Iron Base
Haynes 556Â® alloy, 10% cold reduction	Iron Base
Haynes 556Â® alloy, 40% cold reduction, 1010Â°C anneal for 5 minutes	Iron Base
Haynes 556Â® alloy, bar, after 4000 hours at 650Â°C (1200Â°F)	Iron Base
Haynes 556Â® alloy, bar, after 8000 hours at 870Â°C (1600Â°F)	Iron Base
Haynes 625 alloy, 30% cold reduction, 1065Â°C anneal for 5 minutes	Superalloy
Haynes 625 alloy, 40% cold reduction, 1120Â°C anneal for 5 minutes	Superalloy
Haynes 625 alloy, hot rolled and 1050Â°C mill-annealed plate	Superalloy
Haynes 625SQÂ® Nickel Alloy Sheet	Nickel Alloy
Haynes 718 alloy, cold rolled, solution-treated and aged sheet	Superalloy
Haynes HastelloyÂ® C-2000Â® Nickel Alloy Gas Tungsten Arc Welded (GTAW) All Weld Cruciform	Nickel Alloy	Hastelloy®
Haynes HastelloyÂ® C-22Â® alloy, 0% cold worked sheet	Superalloy	Hastelloy®
Haynes HastelloyÂ® C-22Â® alloy, 30% cold worked sheet	Superalloy	Hastelloy®
Haynes HastelloyÂ® C-22Â® alloy, GTAW, as welded, notched	Superalloy	Hastelloy®
Haynes HastelloyÂ® C-22Â® alloy, transverse, GMAW spray weldment, 23.4 mm thick plate	Superalloy	Hastelloy®
Haynes HastelloyÂ® G-30Â® alloy, 50% cold rolled	Superalloy	Hastelloy®
Haynes Hastelloy® B-3® alloy, after elevated temperature exposure	Superalloy	Hastelloy®
Haynes Hastelloy® G-35® Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) All Weld Cruciform	Nickel Alloy	Hastelloy®
Haynes Hastelloy® N, 1.14 mm sheet, aged 10000 hours at 760°C (1400°F)	Superalloy	Hastelloy®
Haynes R-41 alloy,	Superalloy
Haynes 230® alloy plate, 8000 hours exposure at 649°C (1200°F)	Superalloy
Haynes 230® alloy, 50% cold reduction	Superalloy
Haynes 230® alloy, cold rolled and 1232°C solution annealed sheet	Superalloy
Haynes 25 alloy, room temperature after 10% cold reduction, 1120°C anneal for 5 minutes	Superalloy