Haynes Hastelloy® S alloy, flat products, solution heat-treated at 538°C (1000°F), aged 4000 hours

Category Metal , Nonferrous Metal , Nickel Alloy , Superalloy
Manufacturer Haynes International, Inc.
Trade Name Hastelloy®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Haynes Hastelloy® S alloy, flat products, solution heat-treated at 538°C (1000°F), aged 4000 hours.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications include seal rings in gas turbine engines, and severe cyclical heating conditions where it retains strength, ductility, and integrity.Data provided by the manufacturer, Haynes International, Inc.
Physical Properties Metric English Comments
Density 8.75 g/cc
0.316 lb/in³
Mechanical Properties Metric English Comments
Hardness, Rockwell A 63

@Thickness 12.7 mm
 63

@Thickness 0.500 in
66

@Thickness 1.45 mm
 66

@Thickness 0.0571 in
Tensile Strength, Ultimate 1207 MPa

@Thickness 12.7 mm
 175100 psi

@Thickness 0.500 in
1253 MPa

@Thickness 1.45 mm
 181700 psi

@Thickness 0.0571 in
Tensile Strength, Yield 707 MPa

@Strain 0.200 %,
Thickness 12.7 mm
 103000 psi

@Strain 0.200 %,
Thickness 0.500 in
741 MPa

@Strain 0.200 %,
Thickness 1.45 mm
 107000 psi

@Strain 0.200 %,
Thickness 0.0571 in
Elongation at Break 41 %

@Thickness 1.45 mm
 41 %

@Thickness 0.0571 in
 in 50.8 mm
44 %

@Thickness 12.7 mm
 44 %

@Thickness 0.500 in
 in 50.8 mm
Modulus of Elasticity 132 GPa

@Temperature 1093 °C
 19100 ksi

@Temperature 1999 °F
 Heat treated at 1066°C, air cooled
151 GPa

@Temperature 927 °C
 21900 ksi

@Temperature 1700 °F
 Heat treated at 1066°C, air cooled
161 GPa

@Temperature 813 °C
 23400 ksi

@Temperature 1500 °F
 Heat treated at 1066°C, air cooled
166 GPa

@Temperature 760 °C
 24100 ksi

@Temperature 1400 °F
 Heat treated at 1066°C, air cooled
174 GPa

@Temperature 649 °C
 25200 ksi

@Temperature 1200 °F
 Heat treated at 1066°C, air cooled
182 GPa

@Temperature 538 °C
 26400 ksi

@Temperature 1000 °F
 Heat treated at 1066°C, air cooled
194 GPa

@Temperature 357 °C
 28100 ksi

@Temperature 675 °F
 Heat treated at 1066°C, air cooled
212 GPa

@Temperature 24.0 °C
 30700 ksi

@Temperature 75.2 °F
Charpy Impact 104 J

@Temperature 427 °C
 76.7 ft-lb

@Temperature 801 °F
 V Notch; plate
Thermal Properties Metric English Comments
CTE, linear 11.5 µm/m-°C

@Temperature 20.0 - 93.0 °C
 6.39 µin/in-°F

@Temperature 68.0 - 199 °F
12.2 µm/m-°C

@Temperature 20.0 - 204 °C
 6.78 µin/in-°F

@Temperature 68.0 - 399 °F
12.8 µm/m-°C

@Temperature 20.0 - 316 °C
 7.11 µin/in-°F

@Temperature 68.0 - 601 °F
13.1 µm/m-°C

@Temperature 20.0 - 427 °C
 7.28 µin/in-°F

@Temperature 68.0 - 801 °F
13.3 µm/m-°C

@Temperature 20.0 - 538 °C
 7.39 µin/in-°F

@Temperature 68.0 - 1000 °F
14.4 µm/m-°C

@Temperature 20.0 - 760 °C
 8.00 µin/in-°F

@Temperature 68.0 - 1400 °F
14.9 µm/m-°C

@Temperature 20.0 - 871 °C
 8.28 µin/in-°F

@Temperature 68.0 - 1600 °F
15.5 µm/m-°C

@Temperature 20.0 - 982 °C
 8.61 µin/in-°F

@Temperature 68.0 - 1800 °F
16.0 µm/m-°C

@Temperature 20.0 - 1093 °C
 8.89 µin/in-°F

@Temperature 68.0 - 1999 °F
Specific Heat Capacity 0.398 J/g-°C

@Temperature 0.000 °C
 0.0951 BTU/lb-°F

@Temperature 32.0 °F
0.414 J/g-°C

@Temperature 50.0 °C
 0.0989 BTU/lb-°F

@Temperature 122 °F
0.440 J/g-°C

@Temperature 150 °C
 0.105 BTU/lb-°F

@Temperature 302 °F
0.456 J/g-°C

@Temperature 250 °C
 0.109 BTU/lb-°F

@Temperature 482 °F
0.473 J/g-°C

@Temperature 350 °C
 0.113 BTU/lb-°F

@Temperature 662 °F
0.481 J/g-°C

@Temperature 450 °C
 0.115 BTU/lb-°F

@Temperature 842 °F
0.494 J/g-°C

@Temperature 550 °C
 0.118 BTU/lb-°F

@Temperature 1020 °F
0.502 J/g-°C

@Temperature 650 °C
 0.120 BTU/lb-°F

@Temperature 1200 °F
0.590 J/g-°C

@Temperature 800 °C
 0.141 BTU/lb-°F

@Temperature 1470 °F
0.594 J/g-°C

@Temperature 850 °C
 0.142 BTU/lb-°F

@Temperature 1560 °F
0.594 J/g-°C

@Temperature 900 °C
 0.142 BTU/lb-°F

@Temperature 1650 °F
0.594 J/g-°C

@Temperature 700 °C
 0.142 BTU/lb-°F

@Temperature 1290 °F
0.594 J/g-°C

@Temperature 750 °C
 0.142 BTU/lb-°F

@Temperature 1380 °F
0.598 J/g-°C

@Temperature 950 °C
 0.143 BTU/lb-°F

@Temperature 1740 °F
0.598 J/g-°C

@Temperature 1000 °C
 0.143 BTU/lb-°F

@Temperature 1830 °F
0.598 J/g-°C

@Temperature 1050 °C
 0.143 BTU/lb-°F

@Temperature 1920 °F
0.603 J/g-°C

@Temperature 1100 °C
 0.144 BTU/lb-°F

@Temperature 2010 °F
Thermal Conductivity 14.0 W/m-K

@Temperature 200 °C
 97.2 BTU-in/hr-ft²-°F

@Temperature 392 °F
16.1 W/m-K

@Temperature 300 °C
 112 BTU-in/hr-ft²-°F

@Temperature 572 °F
17.9 W/m-K

@Temperature 400 °C
 124 BTU-in/hr-ft²-°F

@Temperature 752 °F
19.5 W/m-K

@Temperature 500 °C
 135 BTU-in/hr-ft²-°F

@Temperature 932 °F
21.0 W/m-K

@Temperature 600 °C
 146 BTU-in/hr-ft²-°F

@Temperature 1110 °F
26.1 W/m-K

@Temperature 700 °C
 181 BTU-in/hr-ft²-°F

@Temperature 1290 °F
26.1 W/m-K

@Temperature 800 °C
 181 BTU-in/hr-ft²-°F

@Temperature 1470 °F
26.1 W/m-K

@Temperature 900 °C
 181 BTU-in/hr-ft²-°F

@Temperature 1650 °F
27.1 W/m-K

@Temperature 950 °C
 188 BTU-in/hr-ft²-°F

@Temperature 1740 °F
28.0 W/m-K

@Temperature 1000 °C
 194 BTU-in/hr-ft²-°F

@Temperature 1830 °F
Melting Point 1335 - 1380 °C
2435 - 2520 °F
Solidus 1335 °C
2435 °F
Liquidus 1380 °C
2520 °F
Maximum Service Temperature, Air 1093 °C
1999 °F
Component Elements Properties Metric English Comments
Aluminum, Al 0.10 - 0.50 %
0.10 - 0.50 %
Boron, B <= 0.015 %
<= 0.015 %
Carbon, C <= 0.020 %
<= 0.020 %
Chromium, Cr 14.5 - 17 %
14.5 - 17 %
Cobalt, Co <= 2.0 %
<= 2.0 %
Copper, Cu <= 0.35 %
<= 0.35 %
Iron, Fe <= 3.0 %
<= 3.0 %
Lanthanum, La 0.010 - 0.10 %
0.010 - 0.10 %
Manganese, Mn 0.30 - 1.0 %
0.30 - 1.0 %
Molybdenum, Mo 14 - 16.5 %
14 - 16.5 %
Nickel, Ni 67 %
67 %
Electrical Properties Metric English Comments
Electrical Resistivity 0.000128 ohm-cm

@Temperature 25.0 °C
 0.000128 ohm-cm

@Temperature 77.0 °F
 specimen aged 16000 hours at 650°C (1200°F)