Haynes 230® alloy, 10% cold reduction, 1066°C anneal for 5 minutes

Category Metal , Nonferrous Metal , Nickel Alloy , Superalloy
Manufacturer Haynes International, Inc.
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Haynes 230® alloy, 10% cold reduction, 1066°C anneal for 5 minutes.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applications include combustion cans, transition ducts, flameholders, thermocouple sheaths and other gas turbine components; used for catalyst grid supports in ammonia burners, high-strength thermocouple protection tubes, high-temperature heat exchangers, ducts, high-temperature bellows; furnace retorts, chains and fixtures, burner flame shrouds, recuperator internals, dampers, nitriding furnace internals, heat-treating baskets, grates, trays, sparger tubes, and cyclone internals.Data provided by the manufacturer, Haynes International, Inc.
Physical Properties Metric English Comments
Density 8.97 g/cc
0.324 lb/in³
at RT
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 990 MPa
144000 psi
Tensile Strength, Yield 635 MPa

@Strain 0.200 %
92100 psi

@Strain 0.200 %
Elongation at Break 32.9 %
32.9 %
in 50.8 mm
Modulus of Elasticity 211 GPa
30600 ksi
RT
150 GPa

@Temperature 1000 °C
21800 ksi

@Temperature 1830 °F
157 GPa

@Temperature 900 °C
22800 ksi

@Temperature 1650 °F
164 GPa

@Temperature 800 °C
23800 ksi

@Temperature 1470 °F
171 GPa

@Temperature 700 °C
24800 ksi

@Temperature 1290 °F
177 GPa

@Temperature 600 °C
25700 ksi

@Temperature 1110 °F
184 GPa

@Temperature 500 °C
26700 ksi

@Temperature 932 °F
190 GPa

@Temperature 400 °C
27600 ksi

@Temperature 752 °F
196 GPa

@Temperature 300 °C
28400 ksi

@Temperature 572 °F
202 GPa

@Temperature 200 °C
29300 ksi

@Temperature 392 °F
207 GPa

@Temperature 100 °C
30000 ksi

@Temperature 212 °F
Charpy Impact 73.0 J
53.8 ft-lb
solution annealed (unknown temp)
Thermal Properties Metric English Comments
CTE, linear 12.7 µm/m-°C

@Temperature 25.0 - 100 °C
7.06 µin/in-°F

@Temperature 77.0 - 212 °F
13.0 µm/m-°C

@Temperature 25.0 - 200 °C
7.22 µin/in-°F

@Temperature 77.0 - 392 °F
13.3 µm/m-°C

@Temperature 25.0 - 300 °C
7.39 µin/in-°F

@Temperature 77.0 - 572 °F
13.7 µm/m-°C

@Temperature 25.0 - 400 °C
7.61 µin/in-°F

@Temperature 77.0 - 752 °F
14.0 µm/m-°C

@Temperature 25.0 - 500 °C
7.78 µin/in-°F

@Temperature 77.0 - 932 °F
14.4 µm/m-°C

@Temperature 25.0 - 600 °C
8.00 µin/in-°F

@Temperature 77.0 - 1110 °F
14.8 µm/m-°C

@Temperature 25.0 - 700 °C
8.22 µin/in-°F

@Temperature 77.0 - 1290 °F
15.2 µm/m-°C

@Temperature 25.0 - 800 °C
8.44 µin/in-°F

@Temperature 77.0 - 1470 °F
15.7 µm/m-°C

@Temperature 25.0 - 900 °C
8.72 µin/in-°F

@Temperature 77.0 - 1650 °F
16.1 µm/m-°C

@Temperature 25.0 - 1000 °C
8.94 µin/in-°F

@Temperature 77.0 - 1830 °F
Specific Heat Capacity 0.397 J/g-°C
0.0949 BTU/lb-°F
RT
0.419 J/g-°C

@Temperature 100 °C
0.100 BTU/lb-°F

@Temperature 212 °F
0.435 J/g-°C

@Temperature 200 °C
0.104 BTU/lb-°F

@Temperature 392 °F
0.448 J/g-°C

@Temperature 300 °C
0.107 BTU/lb-°F

@Temperature 572 °F
0.465 J/g-°C

@Temperature 400 °C
0.111 BTU/lb-°F

@Temperature 752 °F
0.473 J/g-°C

@Temperature 500 °C
0.113 BTU/lb-°F

@Temperature 932 °F
0.486 J/g-°C

@Temperature 600 °C
0.116 BTU/lb-°F

@Temperature 1110 °F
0.574 J/g-°C

@Temperature 700 °C
0.137 BTU/lb-°F

@Temperature 1290 °F
0.595 J/g-°C

@Temperature 800 °C
0.142 BTU/lb-°F

@Temperature 1470 °F
0.609 J/g-°C

@Temperature 900 °C
0.146 BTU/lb-°F

@Temperature 1650 °F
0.617 J/g-°C

@Temperature 1000 °C
0.147 BTU/lb-°F

@Temperature 1830 °F
Thermal Conductivity 8.90 W/m-K
61.8 BTU-in/hr-ft²-°F
RT
10.4 W/m-K

@Temperature 100 °C
72.2 BTU-in/hr-ft²-°F

@Temperature 212 °F
12.4 W/m-K

@Temperature 200 °C
86.1 BTU-in/hr-ft²-°F

@Temperature 392 °F
14.4 W/m-K

@Temperature 300 °C
99.9 BTU-in/hr-ft²-°F

@Temperature 572 °F
16.4 W/m-K

@Temperature 400 °C
114 BTU-in/hr-ft²-°F

@Temperature 752 °F
18.4 W/m-K

@Temperature 500 °C
128 BTU-in/hr-ft²-°F

@Temperature 932 °F
20.4 W/m-K

@Temperature 600 °C
142 BTU-in/hr-ft²-°F

@Temperature 1110 °F
22.4 W/m-K

@Temperature 700 °C
155 BTU-in/hr-ft²-°F

@Temperature 1290 °F
24.4 W/m-K

@Temperature 800 °C
169 BTU-in/hr-ft²-°F

@Temperature 1470 °F
26.4 W/m-K

@Temperature 900 °C
183 BTU-in/hr-ft²-°F

@Temperature 1650 °F
28.4 W/m-K

@Temperature 1000 °C
197 BTU-in/hr-ft²-°F

@Temperature 1830 °F
Melting Point 1301 - 1371 °C
2374 - 2500 °F
Solidus 1301 °C
2374 °F
Liquidus 1371 °C
2500 °F
Component Elements Properties Metric English Comments
Aluminum, Al 0.30 %
0.30 %
Boron, B <= 0.015 %
<= 0.015 %
Carbon, C 0.10 %
0.10 %
Chromium, Cr 22 %
22 %
Cobalt, Co <= 5.0 %
<= 5.0 %
Iron, Fe <= 3.0 %
<= 3.0 %
Electrical Properties Metric English Comments
Electrical Resistivity 0.000125 ohm-cm
0.000125 ohm-cm
RT
0.000125 ohm-cm

@Temperature 1000 °C
0.000125 ohm-cm

@Temperature 1830 °F
0.0001258 ohm-cm

@Temperature 100 °C
0.0001258 ohm-cm

@Temperature 212 °F
0.0001265 ohm-cm

@Temperature 200 °C
0.0001265 ohm-cm

@Temperature 392 °F
0.0001271 ohm-cm

@Temperature 900 °C
0.0001271 ohm-cm

@Temperature 1650 °F
0.0001273 ohm-cm

@Temperature 300 °C
0.0001273 ohm-cm

@Temperature 572 °F
0.0001284 ohm-cm

@Temperature 400 °C
0.0001284 ohm-cm

@Temperature 752 °F
0.0001291 ohm-cm

@Temperature 800 °C
0.0001291 ohm-cm

@Temperature 1470 °F
0.0001302 ohm-cm

@Temperature 500 °C
0.0001302 ohm-cm

@Temperature 932 °F
0.0001307 ohm-cm

@Temperature 700 °C
0.0001307 ohm-cm

@Temperature 1290 °F
0.0001312 ohm-cm

@Temperature 600 °C
0.0001312 ohm-cm

@Temperature 1110 °F