Haynes Hastelloy® S alloy, flat products

Category Metal , Nonferrous Metal , Nickel Alloy , Superalloy
Manufacturer Haynes International, Inc.
Trade Name Hastelloy®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Haynes Hastelloy® S alloy, flat products.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Nickel-based, high temperature alloy. Excellent thermal stability, low thermal expansion, excellent oxidation resistance to 1093°C, good high temperature and thermal fatigue strength. Applications include seal rings in gas turbine engines, and severe cyclical heating conditions where it retains strength, ductility, and integrity.Data provided by the manufacturer, Haynes International, Inc.
Physical Properties Metric English Comments
Density 8.75 g/cc
0.316 lb/in³
Mechanical Properties Metric English Comments
Hardness, Rockwell A 52

@Thickness 1.45 mm
 52

@Thickness 0.0571 in
57

@Thickness 12.7 mm
 57

@Thickness 0.500 in
Tensile Strength, Ultimate 110 MPa

@Thickness 1.10 - 1.60 mm,
Temperature 1093 °C
 16000 psi

@Thickness 0.0433 - 0.0630 in,
Temperature 1999 °F
117 MPa

@Thickness 9.50 - 25.4 mm,
Temperature 1093 °C
 17000 psi

@Thickness 0.374 - 1.00 in,
Temperature 1999 °F
193 MPa

@Thickness 1.10 - 1.60 mm,
Temperature 982 °C
 28000 psi

@Thickness 0.0433 - 0.0630 in,
Temperature 1800 °F
228 MPa

@Thickness 9.50 - 25.4 mm,
Temperature 982 °C
 33100 psi

@Thickness 0.374 - 1.00 in,
Temperature 1800 °F
341 MPa

@Thickness 1.10 - 1.60 mm,
Temperature 871 °C
 49500 psi

@Thickness 0.0433 - 0.0630 in,
Temperature 1600 °F
363 MPa

@Thickness 9.50 - 25.4 mm,
Temperature 871 °C
 52600 psi

@Thickness 0.374 - 1.00 in,
Temperature 1600 °F
547 MPa

@Thickness 9.50 - 25.4 mm,
Temperature 760 °C
 79300 psi

@Thickness 0.374 - 1.00 in,
Temperature 1400 °F
574 MPa

@Thickness 1.10 - 1.60 mm,
Temperature 760 °C
 83300 psi

@Thickness 0.0433 - 0.0630 in,
Temperature 1400 °F
683 MPa

@Thickness 9.50 - 25.4 mm,
Temperature 649 °C
 99100 psi

@Thickness 0.374 - 1.00 in,
Temperature 1200 °F
720 MPa

@Thickness 1.10 - 1.60 mm,
Temperature 649 °C
 104000 psi

@Thickness 0.0433 - 0.0630 in,
Temperature 1200 °F
727 MPa

@Thickness 9.50 - 25.4 mm,
Temperature 538 °C
 105000 psi

@Thickness 0.374 - 1.00 in,
Temperature 1000 °F
751 MPa

@Thickness 9.50 - 25.4 mm,
Temperature 427 °C
 109000 psi

@Thickness 0.374 - 1.00 in,
Temperature 801 °F
756 MPa

@Thickness 9.50 - 25.4 mm,
Temperature 316 °C
 110000 psi

@Thickness 0.374 - 1.00 in,
Temperature 601 °F
773 MPa

@Thickness 1.10 - 1.60 mm,
Temperature 538 °C
 112000 psi

@Thickness 0.0433 - 0.0630 in,
Temperature 1000 °F
789 MPa

@Thickness 9.50 - 25.4 mm,
Temperature 204 °C
 114000 psi

@Thickness 0.374 - 1.00 in,
Temperature 399 °F
814 MPa

@Thickness 9.50 - 25.4 mm,
Temperature 93.0 °C
 118000 psi

@Thickness 0.374 - 1.00 in,
Temperature 199 °F
844 MPa

@Thickness 1.10 - 1.60 mm,
Temperature 20.0 °C
 122000 psi

@Thickness 0.0433 - 0.0630 in,
Temperature 68.0 °F
849 MPa

@Thickness 9.50 - 25.4 mm,
Temperature 20.0 °C
 123000 psi

@Thickness 0.374 - 1.00 in,
Temperature 68.0 °F
864 MPa

@Thickness 12.7 mm,
Temperature 20.0 °C
 125000 psi

@Thickness 0.500 in,
Temperature 68.0 °F
887 MPa

@Thickness 1.45 mm,
Temperature 20.0 °C
 129000 psi

@Thickness 0.0571 in,
Temperature 68.0 °F
Tensile Strength, Yield 52.0 MPa

@Thickness 1.10 - 1.60 mm,
Temperature 1093 °C
 7540 psi

@Thickness 0.0433 - 0.0630 in,
Temperature 1999 °F
 0.2% offset
61.0 MPa

@Thickness 9.50 - 25.4 mm,
Temperature 1093 °C
 8850 psi

@Thickness 0.374 - 1.00 in,
Temperature 1999 °F
 0.2% offset
110 MPa

@Thickness 1.10 - 1.60 mm,
Temperature 982 °C
 16000 psi

@Thickness 0.0433 - 0.0630 in,
Temperature 1800 °F
 0.2% offset
135 MPa

@Thickness 9.50 - 25.4 mm,
Temperature 982 °C
 19600 psi

@Thickness 0.374 - 1.00 in,
Temperature 1800 °F
 0.2% offset
218 MPa

@Thickness 1.10 - 1.60 mm,
Temperature 871 °C
 31600 psi

@Thickness 0.0433 - 0.0630 in,
Temperature 1600 °F
 0.2% offset
233 MPa

@Thickness 9.50 - 25.4 mm,
Temperature 871 °C
 33800 psi

@Thickness 0.374 - 1.00 in,
Temperature 1600 °F
 0.2% offset
271 MPa

@Thickness 9.50 - 25.4 mm,
Temperature 760 °C
 39300 psi

@Thickness 0.374 - 1.00 in,
Temperature 1400 °F
 0.2% offset
274 MPa

@Thickness 9.50 - 25.4 mm,
Temperature 649 °C
 39700 psi

@Thickness 0.374 - 1.00 in,
Temperature 1200 °F
 0.2% offset
283 MPa

@Thickness 9.50 - 25.4 mm,
Temperature 538 °C
 41000 psi

@Thickness 0.374 - 1.00 in,
Temperature 1000 °F
 0.2% offset
291 MPa

@Thickness 9.50 - 25.4 mm,
Temperature 316 °C
 42200 psi

@Thickness 0.374 - 1.00 in,
Temperature 601 °F
 0.2% offset
297 MPa

@Thickness 9.50 - 25.4 mm,
Temperature 427 °C
 43100 psi

@Thickness 0.374 - 1.00 in,
Temperature 801 °F
 0.2% offset
311 MPa

@Thickness 1.10 - 1.60 mm,
Temperature 760 °C
 45100 psi

@Thickness 0.0433 - 0.0630 in,
Temperature 1400 °F
 0.2% offset
322 MPa

@Thickness 1.10 - 1.60 mm,
Temperature 649 °C
 46700 psi

@Thickness 0.0433 - 0.0630 in,
Temperature 1200 °F
 0.2% offset
331 MPa

@Thickness 9.50 - 25.4 mm,
Temperature 204 °C
 48000 psi

@Thickness 0.374 - 1.00 in,
Temperature 399 °F
 0.2% offset
338 MPa

@Thickness 1.10 - 1.60 mm,
Temperature 538 °C
 49000 psi

@Thickness 0.0433 - 0.0630 in,
Temperature 1000 °F
 0.2% offset
365 MPa

@Thickness 9.50 - 25.4 mm,
Temperature 93.0 °C
 52900 psi

@Thickness 0.374 - 1.00 in,
Temperature 199 °F
 0.2% offset
365 MPa

@Thickness 12.7 mm,
Temperature 20.0 °C
 52900 psi

@Thickness 0.500 in,
Temperature 68.0 °F
 0.2% offset
383 MPa

@Thickness 9.50 - 25.4 mm,
Temperature 20.0 °C
 55500 psi

@Thickness 0.374 - 1.00 in,
Temperature 68.0 °F
 0.2% offset
434 MPa

@Thickness 1.45 mm,
Temperature 20.0 °C
 62900 psi

@Thickness 0.0571 in,
Temperature 68.0 °F
 0.2% offset
444 MPa

@Thickness 1.10 - 1.60 mm,
Temperature 20.0 °C
 64400 psi

@Thickness 0.0433 - 0.0630 in,
Temperature 68.0 °F
 0.2% offset
Elongation at Break 46 %

@Thickness 1.10 - 1.60 mm,
Temperature 982 °C
 46 %

@Thickness 0.0433 - 0.0630 in,
Temperature 1800 °F
 in 50.8 mm
47 %

@Thickness 1.10 - 1.60 mm,
Temperature 871 °C
 47 %

@Thickness 0.0433 - 0.0630 in,
Temperature 1600 °F
 in 50.8 mm
49 %

@Thickness 1.10 - 1.60 mm,
Temperature 20.0 °C
 49 %

@Thickness 0.0433 - 0.0630 in,
Temperature 68.0 °F
 in 50.8 mm
50 %

@Thickness 1.10 - 1.60 mm,
Temperature 538 °C
 50 %

@Thickness 0.0433 - 0.0630 in,
Temperature 1000 °F
 in 50.8 mm
54 %

@Thickness 12.7 mm,
Temperature 20.0 °C
 54 %

@Thickness 0.500 in,
Temperature 68.0 °F
 in 50.8 mm
55 %

@Thickness 9.50 - 25.4 mm,
Temperature 20.0 °C
 55 %

@Thickness 0.374 - 1.00 in,
Temperature 68.0 °F
 in 50.8 mm
56 %

@Thickness 1.10 - 1.60 mm,
Temperature 649 °C
 56 %

@Thickness 0.0433 - 0.0630 in,
Temperature 1200 °F
 in 50.8 mm
57 %

@Thickness 9.50 - 25.4 mm,
Temperature 871 °C
 57 %

@Thickness 0.374 - 1.00 in,
Temperature 1600 °F
 in 50.8 mm
58 %

@Thickness 1.45 mm,
Temperature 20.0 °C
 58 %

@Thickness 0.0571 in,
Temperature 68.0 °F
 in 50.8 mm
59 %

@Thickness 9.50 - 25.4 mm,
Temperature 204 °C
 59 %

@Thickness 0.374 - 1.00 in,
Temperature 399 °F
 in 50.8 mm
59 %

@Thickness 9.50 - 25.4 mm,
Temperature 649 °C
 59 %

@Thickness 0.374 - 1.00 in,
Temperature 1200 °F
 in 50.8 mm
60 %

@Thickness 9.50 - 25.4 mm,
Temperature 93.0 °C
 60 %

@Thickness 0.374 - 1.00 in,
Temperature 199 °F
 in 50.8 mm
61 %

@Thickness 9.50 - 25.4 mm,
Temperature 538 °C
 61 %

@Thickness 0.374 - 1.00 in,
Temperature 1000 °F
 in 50.8 mm
62 %

@Thickness 9.50 - 25.4 mm,
Temperature 427 °C
 62 %

@Thickness 0.374 - 1.00 in,
Temperature 801 °F
 in 50.8 mm
62 %

@Thickness 9.50 - 25.4 mm,
Temperature 982 °C
 62 %

@Thickness 0.374 - 1.00 in,
Temperature 1800 °F
 in 50.8 mm
63 %

@Thickness 9.50 - 25.4 mm,
Temperature 316 °C
 63 %

@Thickness 0.374 - 1.00 in,
Temperature 601 °F
 in 50.8 mm
69 %

@Thickness 9.50 - 25.4 mm,
Temperature 760 °C
 69 %

@Thickness 0.374 - 1.00 in,
Temperature 1400 °F
 in 50.8 mm
69 %

@Thickness 9.50 - 25.4 mm,
Temperature 1093 °C
 69 %

@Thickness 0.374 - 1.00 in,
Temperature 1999 °F
 in 50.8 mm
70 %

@Thickness 1.10 - 1.60 mm,
Temperature 760 °C
 70 %

@Thickness 0.0433 - 0.0630 in,
Temperature 1400 °F
 in 50.8 mm
75 %

@Thickness 1.10 - 1.60 mm,
Temperature 1093 °C
 75 %

@Thickness 0.0433 - 0.0630 in,
Temperature 1999 °F
 in 50.8 mm
Modulus of Elasticity 132 GPa

@Temperature 1093 °C
 19100 ksi

@Temperature 1999 °F
 Heat treated at 1066°C, air cooled
151 GPa

@Temperature 927 °C
 21900 ksi

@Temperature 1700 °F
 Heat treated at 1066°C, air cooled
161 GPa

@Temperature 813 °C
 23400 ksi

@Temperature 1500 °F
 Heat treated at 1066°C, air cooled
166 GPa

@Temperature 760 °C
 24100 ksi

@Temperature 1400 °F
 Heat treated at 1066°C, air cooled
174 GPa

@Temperature 649 °C
 25200 ksi

@Temperature 1200 °F
 Heat treated at 1066°C, air cooled
182 GPa

@Temperature 538 °C
 26400 ksi

@Temperature 1000 °F
 Heat treated at 1066°C, air cooled
194 GPa

@Temperature 357 °C
 28100 ksi

@Temperature 675 °F
 Heat treated at 1066°C, air cooled
Users viewing this material also viewed the following:
Copyright © lookpolymers.com All Rights Reserved