- HOME
- POLYMER SEARCH
- Polymer Property : CTE, linear = 41.7 µin/in-°F
Polymer Property : CTE, linear = 41.7 µin/in-°F Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 75.0 - 97.0 µm/m-°C | 41.7 - 53.9 µin/in-°F | Average value: 85.0 µm/m-°C Grade Count:7 |
| Overview of materials for PCTG Copolyester This property data is a summary of similar materials in the MatWeb database for the category "PCTG Copolyester". Each property range of values reported is minimum and maximum values of appropriate M.. |
|||
| CTE, linear | 75.0 µm/m-°C @Temperature 20.0 °C |
41.7 µin/in-°F @Temperature 68.0 °F |
|
| Ineos Nova FX550 (ASTM) Advanced Styrenic Polymer
(discontinued **) Extremely high glossHigh Izod impact strengthUL Classification 94 HBPractical toughnessHigh flow for injection moldingScuff resistanceApplications: Replacement resin for selected ABS applicationsRef.. |
|||
| CTE, linear | 75.0 µm/m-°C @Temperature 20.0 °C |
41.7 µin/in-°F @Temperature 68.0 °F |
|
| Ineos Nova 4214 Medium Impact Polystyrene
(discontinued **) Excellent balance of properties, USP Class VIApplications: Consumer electronics, Injection molding applicationsProperties were determined on injection molded specimens at 23°C and 50% R.H. unless o.. |
|||
| CTE, linear | >= 75.0 µm/m-°C @Temperature 60.0 - 60.0 °C |
>= 41.7 µin/in-°F @Temperature 140 - 140 °F |
Average value: 75.0 µm/m-°C Grade Count:1 |
| Overview of materials for Epoxy, High Temperature This property data is a summary of similar materials in the MatWeb database for the category "Epoxy, Encapsulating, Mineral Filled". Each property range of values reported is minimum and maximum val.. |
|||
| CTE, linear | 75.0 - 790 µm/m-°C | 41.7 - 439 µin/in-°F | Average value: 294 µm/m-°C Grade Count:20 |
| Overview of materials for Polytetrafluoroethylene (PTFE), Extruded This property data is a summary of similar materials in the MatWeb database for the category "Polytetrafluoroethylene (PTFE), Extruded". Each property range of values reported is minimum and maximum.. |
|||
| CTE, linear | 75.0 - 150 µm/m-°C | 41.7 - 83.3 µin/in-°F | Average value: 108 µm/m-°C Grade Count:3 |
| Overview of materials for Polytetrafluoroethylene (PTFE), Carbon Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polytetrafluoroethylene (PTFE), Carbon Fiber Filled". Each property range of values reported is minimum .. |
|||
| CTE, linear | 75.0 µm/m-°C @Temperature -30.0 - 80.0 °C |
41.7 µin/in-°F @Temperature -22.0 - 176 °F |
ASTM E228 |
| LyondellBasell SEQUEL® 1480 Engineered Polyolefin Description: SEQUEL® 1480 engineered polyolefin material is designed for large automotive exterior applications that require ductile impact properties at low temperatures, excellent paintability,.. |
|||
| CTE, linear | 75.0 µm/m-°C @Temperature 20.0 °C |
41.7 µin/in-°F @Temperature 68.0 °F |
|
| Ineos Nova 5400 High Impact Polystyrene High impact, Good environmental stress crack resistance, USP Class VIApplications: Thermoformed containers and lids, Hot and cold beverage cups, Custom sheet, Single service packagingProperties were.. |
|||
| CTE, linear | 75.0 µm/m-°C @Temperature 20.0 °C |
41.7 µin/in-°F @Temperature 68.0 °F |
|
| Ineos Nova 5404 High Impact Polystyrene High impact, Good environmental stress crack resistance, USP Class VIApplications: Thermoformed containers and lids, Hot and cold beverage cups, Custom sheet, Single service packagingProperties were.. |
|||
| CTE, linear | 75.0 µm/m-°C @Temperature 20.0 °C |
41.7 µin/in-°F @Temperature 68.0 °F |
|
| Ineos Nova 5511 High Impact Polystyrene Good overall balance of properties, USP Class VIApplications: Audio cassettes and cartridges, Housewares, Toys, Industrial productsProperties were determined on injection molded specimens at 23°C.. |
|||
| CTE, linear | 75.0 µm/m-°C @Temperature 20.0 °C |
41.7 µin/in-°F @Temperature 68.0 °F |
|
| Ineos Nova FX530 Impact Polystyrene Features: Excellent environmental stress crack resistanceExcellent Izod impact strengthUL Classification 94 HBBalanced physical propertiesApplications: ExtrusionThermoformingSelected injection moldi.. |
|||
| CTE, linear | 75.0 µm/m-°C | 41.7 µin/in-°F | DIN 52328 |
| Isoflon PA 6G Cast Polyamide 6 General use for mechanical partsGood heat resistanceEasy to useHigh moisture regainInformation provided by Isoflon. |
|||
| CTE, linear | 75.0 - 110 µm/m-°C | 41.7 - 61.1 µin/in-°F | ASTM D696 |
| Guarniflon PTFE G405 Polytetrafluoroethylene 25% Glass Fiber PTFE G Standard Compound with glass fiberProperties: Enhanced wear resistance. Enhanced chemical resistance (except for alkali and hydrofluoric acid).Applications: Valve seats, seals, bearings, re.. |
|||
| CTE, linear | 75.0 - 85.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
41.7 - 47.2 µin/in-°F @Temperature -22.0 - 86.0 °F |
TMA |
| SABIC Innovative Plastics Noryl GTX CRN500 PPE+PA6 (Asia Pacific) Pa6 based unfilled GTX for Non-Auto marketThis data was supplied by SABIC-IP for the Asia Pacific region. |
|||
| CTE, linear | 75.0 - 85.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
41.7 - 47.2 µin/in-°F @Temperature -22.0 - 86.0 °F |
TMA |
| SABIC Innovative Plastics NORYL GTX GTX600 PPE+PA6 (Asia Pacific) Pa6 based unfilled GTX |
|||
| CTE, linear | 75.0 - 85.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
41.7 - 47.2 µin/in-°F @Temperature -22.0 - 86.0 °F |
TMA |
| SABIC Innovative Plastics Noryl GTX GTX6013 PPE+PA6 (Asia Pacific) This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
| CTE, linear | 75.0 µm/m-°C | 41.7 µin/in-°F | Below Tg |
| Tra-Con Tra-Bond 293-1 General Purpose Instrument Epoxy Adhesive TRA-BOND 293-1 general purpose epoxy adhesive is designed to provide strong, resilient bonds to a variety of difficult-to-bond substrates, such as gold, nickel, silver, copper, and brass. The 293-se.. |
|||
| CTE, linear | 75.0 µm/m-°C | 41.7 µin/in-°F | Below Tg |
| Tra-Con Tra-Bond 526M02 High Tg Fiber Optic Adhesive TRA-BOND 526M02 is a two-part, low viscosity epoxy system that was developed specifically for fiber optic applications. This material is recommended for bonding fiber optic bundles, potting glass fi.. |
|||
| CTE, linear | 75.0 - 85.0 µm/m-°C | 41.7 - 47.2 µin/in-°F | |
| Master Bond EP36AN One Part, Toughened, B-Stage Epoxy Description: Master Bond EP36AN is a unique one component, high performance epoxy for bonding, encapsulation, potting and coating featuring thermal conductivity, electrical insulation and high tempe.. |
|||
| CTE, linear | 75.0 µm/m-°C @Temperature 20.0 °C |
41.7 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| E-Polymers TEKAMID® TA210HI , High Impact Resistance PA66, DAM High impact resistanceInformation provided by E-Polymers Co. Ltd. |
|||
| CTE, linear | 75.0 µm/m-°C @Temperature -30.0 - 60.0 °C |
41.7 µin/in-°F @Temperature -22.0 - 140 °F |
ASTM D696 |
| Asahi Kasei Xyron® 200H Modified Polyphenylene Ether Heat ResistantInformation provided by Asahi Kasei |
|||
| CTE, linear | 75.0 µm/m-°C @Temperature -30.0 - 60.0 °C |
41.7 µin/in-°F @Temperature -22.0 - 140 °F |
ASTM D696 |
| Asahi Kasei Xyron® 240V Modified Polyphenylene Ether Flame RetardantInformation provided by Asahi Kasei |
|||
| CTE, linear | 75.0 µm/m-°C @Temperature -30.0 - 60.0 °C |
41.7 µin/in-°F @Temperature -22.0 - 140 °F |
ASTM D696 |
| Asahi Kasei Xyron® 300Z Modified Polyphenylene Ether Flame RetardantInformation provided by Asahi Kasei |
|||
| CTE, linear | 75.0 µm/m-°C @Temperature -30.0 - 60.0 °C |
41.7 µin/in-°F @Temperature -22.0 - 140 °F |
ASTM D696 |
| Asahi Kasei Xyron® X0700 Modified Polyphenylene Ether AutomotiveInformation provided by Asahi Kasei |
|||
| CTE, linear | 75.0 µm/m-°C @Temperature -30.0 - 60.0 °C |
41.7 µin/in-°F @Temperature -22.0 - 140 °F |
ASTM D696 |
| Asahi Kasei Xyron® X0722 Modified Polyphenylene Ether AutomotiveInformation provided by Asahi Kasei |
|||
| CTE, linear | 75.0 µm/m-°C @Temperature -30.0 - 60.0 °C |
41.7 µin/in-°F @Temperature -22.0 - 140 °F |
ASTM D696 |
| Asahi Kasei Xyron® X0715 Modified Polyphenylene Ether AutomotiveInformation provided by Asahi Kasei |
|||
| CTE, linear | 75.0 µm/m-°C | 41.7 µin/in-°F | GB1036 |
| Beijing Evergrow Resources Enylon® Information provided by Beijing Evergrow Resources. |
|||
| CTE, linear | 75.0 µm/m-°C @Temperature -30.0 - 100 °C |
41.7 µin/in-°F @Temperature -22.0 - 212 °F |
ASTM D696 |
| LyondellBasell Hostacom™ ZB752AC Polypropylene Homopolymer Description: Hostacom™ ZB752AC precolored, medium melt flow, 2,800 MPa flexural modulus, mineral-filled polypropylene homopolymer has a very good combination of strength, stiffness, and impact resi.. |
|||
| CTE, linear | 75.0 µm/m-°C @Temperature -30.0 - 80.0 °C |
41.7 µin/in-°F @Temperature -22.0 - 176 °F |
ASTM D696 |
| LyondellBasell INDURE™ X210 TPO Description: INDURE™ X210 engineered polyolefin material is designed for large automotive exterior applications that require ductile impact properties at low temperatures, and processability. Appli.. |
|||
Copyright © lookpolymers.com All Rights Reserved