Ineos Nova FX530 Impact Polystyrene
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Impact Modified |
| Manufacturer | Ineos Nova |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ineos Nova FX530 Impact Polystyrene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features: Excellent environmental stress crack resistanceExcellent Izod impact strengthUL Classification 94 HBBalanced physical propertiesApplications: ExtrusionThermoformingSelected injection molding applicationsInformation provided by Nova ChemicalsINEOS NOVA began October 1 2007 as an expansion of the 50:50 joint venture between NOVA Chemicals and INEOS to include North American assets.Â
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.04 g/cc | 1.04 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 3.5 g/10 min @Load 5.00 kg, Temperature 200 °C |
3.5 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 19.0 MPa | 2760 psi | ASTM D638 |
| Elongation at Break | 60 % | 60 % | ASTM D638 |
| Tensile Modulus | 2.00 GPa | 290 ksi | ASTM D638 |
| Flexural Strength | 41.0 MPa | 5950 psi | at 5% strain; ASTM D790 |
| Flexural Modulus | 2.068 GPa | 299.9 ksi | ASTM D790 |
| Izod Impact, Notched | 1.92 J/cm @Diameter 3.17 mm |
3.60 ft-lb/in @Diameter 0.125 in |
bar; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 75.0 µm/m-°C @Temperature 20.0 °C |
41.7 µin/in-°F @Temperature 68.0 °F |
|
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C | 194 °F | annealed; ASTM D648 |
| Vicat Softening Point | 100 °C | 212 °F | Rate B; ASTM D1525 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 2.51 @Frequency 1e+6 Hz |
2.51 @Frequency 1e+6 Hz |
|
| Dielectric Strength | 15.7 kV/mm @Thickness 3.17 mm |
400 kV/in @Thickness 0.125 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 190 - 274 °C | 374 - 525 °F | |
| Mold Temperature | 38.0 - 82.0 °C | 100 - 180 °F |
Users viewing this material also viewed the following:
- PolyOne Edgetek® MLS-10GF/000 Polysulfone Alloy - 10% Glass Fiber Reinforced (discontinued **)
- Lucas-Milhaupt Silvaloy® A45 Flux Coated Rod Brazing Alloy
- Schott Nextrema® 724-8 Glass Ceramic
- Silberline EX 2629 Stabilized UV
- Sumitomo Bakelite Durez® 32245 Phenolic, Injection Grade
- UBE 7034T Nylon 6/12 Monofilament (Drawing Ratio=5, Diameter 2 mm)
- Borealis Visico™/Ambicat™ ME4425/LE4476 Ambient Curing, Moisture-Crosslinking Polyethylene Compound for Low Voltage Insulation
- Chosun Refractories SAL95S Special High Alumina brick
- 3M Scotchlite™ 680-75 Reflective Graphic Film
- Arlon 32580X030 0.030" (0.762 mm) Uncured Unsupported Silicone Rubber on a PET Carrier
Copyright © lookpolymers.com All Rights Reserved