Asahi Kasei Xyron® 300Z Modified Polyphenylene Ether
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether, Heat Resistant |
| Manufacturer | Asahi Kasei |
| Trade Name | Xyron® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Asahi Kasei Xyron® 300Z Modified Polyphenylene Ether.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Flame RetardantInformation provided by Asahi Kasei
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.08 g/cc | 1.08 g/cc | 23°C; ASTM D792 |
| Moisture Absorption | 0.100 % | 0.100 % | 23°C, 50% RH 24 hours; ASTM D570 |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 45.0 MPa | 6530 psi | 23°C, 50% RH; ASTM D638 |
| Elongation at Break | 50 % | 50 % | 23°C, 50% RH; ASTM D638 |
| Flexural Strength | 78.0 MPa | 11300 psi | 23°C, 50% RH; ASTM D790 |
| Flexural Modulus | 2.40 GPa | 348 ksi | 23°C, 50% RH; ASTM D790 |
| Izod Impact, Notched | 1.76 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
3.30 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
ASTM D256 |
| 2.30 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
4.31 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 75.0 µm/m-°C @Temperature -30.0 - 60.0 °C |
41.7 µin/in-°F @Temperature -22.0 - 140 °F |
ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 3.20 mm |
V-0 @Thickness 0.126 in |
|
| 5VA @Thickness 2.50 mm |
5VA @Thickness 0.0984 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | 50% RH; ASTM D257 |
| Surface Resistance | 1.00e+16 ohm | 1.00e+16 ohm | 50% RH; ASTM D257 |
| Dielectric Constant | 2.9 @Frequency 1e+6 Hz |
2.9 @Frequency 1e+6 Hz |
50% RH; ASTM D150 |
| 2.9 @Frequency 1e+6 Hz |
2.9 @Frequency 1e+6 Hz |
50% RH; ASTM D150 | |
| Dielectric Strength | 25.0 kV/mm @Thickness 2.00 mm |
635 kV/in @Thickness 0.0787 in |
Short time; ASTM D149 |
| Dissipation Factor | 0.0030 @Frequency 60 Hz |
0.0030 @Frequency 60 Hz |
50% RH; ASTM D150 |
| 0.0040 @Frequency 1e+6 Hz |
0.0040 @Frequency 1e+6 Hz |
50% RH; ASTM D150 | |
| Arc Resistance | 70 sec | 70 sec | Tungsten; ASTM D495 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 220 - 270 °C | 428 - 518 °F | Resin Temperature |
| Mold Temperature | 50.0 - 80.0 °C | 122 - 176 °F | |
| Drying Temperature | 90.0 - 100 °C | 194 - 212 °F | Pre-drying Temperature |
| Dry Time | 2 - 4 hour | 2 - 4 hour |
Users viewing this material also viewed the following:
- NanoAmor 95%, OD/ID: 20-40/5-10 nm Aligned Multi-Walled Carbon Nanotubes
- Noble Polymers Ecobarrier™ 2618 Thermoplastic Olefin (TPO)
- PolyOne Geon™ Vinyl Flexible A8500 Polyvinyl Chloride, Flexible (PVC, Flexible)
- Kazanorgsintez Diproxamine 157
- Shinil Chemical SHINSTRA PBT SBV1015 Structural Polymer Lamp Housing
- UBE 7034MT2 Nylon 6/12 Monofilament (Drawing Ratio=5)
- A. Schulman POLYFORT™ FPP 3443U UV Resistant Homopolymer Polypropylene
- Covestro Baydur® STR/C-410 IMR Polyurethane Composite SRIM Foam, 60% Glass Filled, MDI-based 2-Component Liquid System
- EMS-Griltech Griltex® D 1299A Heat Stabilized Copolyamide Hotmelt Adhesive (Apparel Interlinings)
- E-Polymers TEKAPPO® JF6 Un-Reinforced Flame Retardant Heat Resistance M-PPO
Copyright © lookpolymers.com All Rights Reserved