- Asahi Kasei Xyron® X0722 Modified Polyphenylene Ether
Asahi Kasei Xyron® X0722 Modified Polyphenylene Ether
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether, Molded |
| Manufacturer | Asahi Kasei |
| Trade Name | Xyron® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Asahi Kasei Xyron® X0722 Modified Polyphenylene Ether.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
AutomotiveInformation provided by Asahi Kasei
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.10 g/cc | 1.10 g/cc | 23°C; ASTM D792 |
| Moisture Absorption | 0.0900 % | 0.0900 % | 23°C, 50% RH 24 hours; ASTM D570 |
| Linear Mold Shrinkage | 0.0060 - 0.0080 cm/cm | 0.0060 - 0.0080 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 47.0 MPa | 6820 psi | 23°C, 50% RH; ASTM D638 |
| Elongation at Break | 50 % | 50 % | 23°C, 50% RH; ASTM D638 |
| Flexural Strength | 67.0 MPa | 9720 psi | 23°C, 50% RH; ASTM D790 |
| Flexural Modulus | 2.11 GPa | 306 ksi | 23°C, 50% RH; ASTM D790 |
| Izod Impact, Notched | 2.45 J/cm @Thickness 6.40 mm, Temperature 23.0 °C |
4.59 ft-lb/in @Thickness 0.252 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 75.0 µm/m-°C @Temperature -30.0 - 60.0 °C |
41.7 µin/in-°F @Temperature -22.0 - 140 °F |
ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 120 °C | 248 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
Equivalant |
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
Equivalant |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 250 - 300 °C | 482 - 572 °F | Resin Temperature |
| Mold Temperature | 70.0 - 100 °C | 158 - 212 °F | |
| Drying Temperature | 90.0 - 120 °C | 194 - 248 °F | Pre-drying Temperature |
| Dry Time | 2 - 4 hour | 2 - 4 hour |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Geloy XTWE480 ASA (Asia Pacific)
- Gouda Vuurvast LP 85 AM Dense Refractory Brick
- Gouda Vuurvast GI 26 Insulating Refractory Brick
- A. Schulman POLYBATCH™ Mahogany 50381 Concentrate Based in Polyethylene
- Trelleborg E566 EPDM Rubber
- TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber with 60 PHR N990 (MT) Filler
- DuPont Teijin Films Teonex® Q83 Polyester Film, 200 Gauge
- Permabond A025 Anaerobic Retainer
- Lushan PR-5 Maleic Anhydride Grafted Polypropylene
Copyright © lookpolymers.com All Rights Reserved