Styron INSPIREâ„¢ TF1500 ESU Polypropylene

Category	Polymer , Thermoplastic , Polypropylene (PP)
Manufacturer	Styron
Trade Name	INSPIRE™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Styron INSPIREâ„¢ TF1500 ESU Polypropylene.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Talc filled, high impact PP compound. INSPIREâ„¢ TF1500 ESU has been developed for aesthetic automotive applications, with good scratch resistance and UV light stabilization.Information provided by DowThe Inspire brand was spun off from Dow Chemical to Styron in 2010

Physical Properties	Metric	English	Comments
Density	1.02 g/cc	0.0368 lb/inÂ³
Filler Content	15 %	15 %	Talc
Melt Flow	9.5 g/10 min @Load 2.16 kg, Temperature 230 Â°C	9.5 g/10 min @Load 4.76 lb, Temperature 446 Â°F	ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	20.0 MPa	2900 psi	50mm/min; ISO 527
Elongation at Break	70 %	70 %	50 mm/min; ISO 527
Tensile Modulus	1.95 GPa	283 ksi	1 mm/min; ISO 527
Flexural Modulus	1.85 GPa	268 ksi	3 points and 2 mm/min; ISO 178
Izod Impact, Notched (ISO)	25.0 kJ/mÂ²	11.9 ft-lb/inÂ²	ISO 180/1A
	5.00 kJ/mÂ² @Temperature -40.0 Â°C	2.38 ft-lb/inÂ² @Temperature -40.0 Â°F	ISO 180/1A
	10.0 kJ/mÂ² @Temperature 0.000 Â°C	4.76 ft-lb/inÂ² @Temperature 32.0 Â°F	ISO 180/1A

Thermal Properties	Metric	English	Comments
CTE, linear	85.0 Âµm/m-Â°C @Temperature 20.0 Â°C	47.2 Âµin/in-Â°F @Temperature 68.0 Â°F	ASTM D696
Deflection Temperature at 0.46 MPa (66 psi)	110 Â°C	230 Â°F	Unannealed; ISO 75
Deflection Temperature at 1.8 MPa (264 psi)	58.0 Â°C	136 Â°F	Unannealed; ISO 75
Vicat Softening Point	135 Â°C	275 Â°F	ISO 306 A
Shrinkage	0.90 - 1.2 %	0.90 - 1.2 %