SABIC Innovative Plastics LNP LUBRILOY RX05497 PA 66

Category	Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	LNP Lubriloy
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics LNP LUBRILOY RX05497 PA 66.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LNP LUBRILOY* RX05497 is a compound based on Nylon 66 resin containing Proprietary Lubricant. Added feature of this material is: Wear Resistant.

Physical Properties	Metric	English	Comments
Density	1.12 g/cc	0.0405 lb/inÂ³	ASTM D792
	1.12 g/cc	0.0405 lb/inÂ³	ISO 1183
Moisture Absorption	0.880 %	0.880 %	50% RH, 24 hrs; ASTM D570
	1.18 %	1.18 %	23Â°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow	0.023 - 0.025 cm/cm @Time 86400 sec	0.023 - 0.025 in/in @Time 24.0 hour	ASTM D955
	0.0231 - 0.0252 cm/cm @Time 86400 sec	0.0231 - 0.0252 in/in @Time 24.0 hour	ISO 294
Linear Mold Shrinkage, Transverse	0.023 - 0.025 cm/cm @Time 86400 sec	0.023 - 0.025 in/in @Time 24.0 hour	ASTM D955
	0.0231 - 0.0252 cm/cm @Time 86400 sec	0.0231 - 0.0252 in/in @Time 24.0 hour	ISO 294

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	57.0 MPa	8270 psi	ISO 527
	67.0 MPa	9720 psi	ASTM D638
Tensile Strength, Yield	69.0 MPa	10000 psi	ISO 527
	82.0 MPa	11900 psi	ASTM D638
Elongation at Break	24.4 %	24.4 %	ASTM D638
	31.4 %	31.4 %	ISO 527
Elongation at Yield	5.2 %	5.2 %	ASTM D638
	17.2 %	17.2 %	ISO 527
Tensile Modulus	2.73 GPa	396 ksi	1 mm/min; ISO 527
	3.04 GPa	441 ksi	50 mm/min; ASTM D638
Flexural Strength	90.0 MPa	13100 psi	ISO 178
	105 MPa	15200 psi	ASTM D790
Flexural Modulus	2.43 GPa	352 ksi	ISO 178
	2.79 GPa	405 ksi	ASTM D790
Izod Impact, Notched	0.640 J/cm	1.20 ft-lb/in	ASTM D256
Izod Impact, Unnotched	NB	NB	ASTM D4812
Izod Impact, Notched (ISO)	6.00 kJ/mÂ²	2.86 ft-lb/inÂ²	80104; ISO 180/1A
Izod Impact, Unnotched (ISO)	137 kJ/mÂ²	65.2 ft-lb/inÂ²	80104; ISO 180/1U
Dart Drop, Total Energy	60.0 J	44.3 ft-lb	Instrumented Impact Energy @ peak; ASTM D3763
Impact Test	76.0 J	56.1 ft-lb	Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic	0.30	0.30	ASTM D3702 Modified
Coefficient of Friction, Static	0.16	0.16	ASTM D3702 Modified
K (wear) Factor	20.1 x 10^-8 mmÂ³/N-M	10.0 x 10^-10 inÂ³-min/ft-lb-hr	Washer; ASTM D3702 Modified

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	98.6 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	54.8 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ASTM E 831
	98.6 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	54.8 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ISO 11359-2
CTE, linear, Transverse to Flow	91.2 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	50.7 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ASTM E 831
	91.3 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	50.7 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi)	58.0 Â°C	136 Â°F	Flatw 80104 sp=64mm; ISO 75/Af
	58.0 Â°C @Thickness 3.20 mm	136 Â°F @Thickness 0.126 in	unannealed; ASTM D648