SABIC Innovative Plastics Valox® HX312C PBT (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Valox®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Valox® HX312C PBT (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Unreinforced PBT with release. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI), food contact compliant. EtO and steam sterilizable.
Physical Properties Metric English Comments
Specific Gravity 1.31 g/cc
1.31 g/cc
ASTM D792
Density 1.31 g/cc
0.0473 lb/in³
ISO 1183
Moisture Absorption 0.0800 %
0.0800 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.35 %
0.35 %
ISO 62
Linear Mold Shrinkage, Flow 0.0090 - 0.016 cm/cm

@Thickness 3.20 mm
 0.0090 - 0.016 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 35 g/10 min

@Load 1.20 kg,
Temperature 250 °C
 35 g/10 min

@Load 2.65 lb,
Temperature 482 °F
 ASTM D1238
Melt Index of Compound 31 g/10 min

@Load 1.20 kg,
Temperature 250 °C
 31 g/10 min

@Load 2.65 lb,
Temperature 482 °F
 MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 30.0 MPa
4350 psi
Type I, 50 mm/min; ASTM D638
30.0 MPa
4350 psi
50 mm/min; ISO 527
Tensile Strength, Yield 51.0 MPa
7400 psi
Type I, 50 mm/min; ASTM D638
58.0 MPa
8410 psi
50 mm/min; ISO 527
Elongation at Break 25 %
25 %
Type I, 50 mm/min; ASTM D638
25 %
25 %
50 mm/min; ISO 527
Elongation at Yield 6.0 %
6.0 %
Type I, 50 mm/min; ASTM D638
6.0 %
6.0 %
50 mm/min; ISO 527
Tensile Modulus 2.50 GPa
363 ksi
50 mm/min; ASTM D638
2.50 GPa
363 ksi
1 mm/min; ISO 527
Flexural Yield Strength 82.0 MPa
11900 psi
1.3 mm/min, 50 mm span; ASTM D790
85.0 MPa
12300 psi
2 mm/min; ISO 178
Flexural Modulus 2.34 GPa
339 ksi
1.3 mm/min, 50 mm span; ASTM D790
2.40 GPa
348 ksi
2 mm/min; ISO 178
Izod Impact, Notched 0.530 J/cm
0.993 ft-lb/in
ASTM D256
0.530 J/cm

@Temperature -30.0 °C
 0.993 ft-lb/in

@Temperature -22.0 °F
 ASTM D256
Izod Impact, Notched (ISO) 3.00 kJ/m²
1.43 ft-lb/in²
80*10*4; ISO 180/1A
3.00 kJ/m²

@Temperature -30.0 °C
 1.43 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) NB
NB
80*10*4; ISO 180/1U
NB

@Temperature -30.0 °C
 NB

@Temperature -22.0 °F
 80*10*4; ISO 180/1U
Charpy Impact Unnotched NB
NB
Edgew 80*10*4 sp=62mm; ISO 179/1eU
NB

@Temperature -30.0 °C
 NB

@Temperature -22.0 °F
 Edgew 80*10*4 sp=62mm; ISO 179/1eU
Charpy Impact, Notched 0.300 J/cm²
1.43 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
0.200 J/cm²

@Temperature -30.0 °C
 0.952 ft-lb/in²

@Temperature -22.0 °F
 Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 40.0 J

@Temperature 23.0 °C
 29.5 ft-lb

@Temperature 73.4 °F
 ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 100 µm/m-°C

@Temperature -40.0 - 40.0 °C
 55.6 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
100 µm/m-°C

@Temperature 23.0 - 80.0 °C
 55.6 µin/in-°F

@Temperature 73.4 - 176 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 100 µm/m-°C

@Temperature -40.0 - 40.0 °C
 55.6 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
100 µm/m-°C

@Temperature 23.0 - 80.0 °C
 55.6 µin/in-°F

@Temperature 73.4 - 176 °F
 ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 58.0 °C
136 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
54.0 °C

@Thickness 3.20 mm
 129 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Vicat Softening Point 165 °C
329 °F
Rate B/120; ISO 306
175 °C
347 °F
Rate B/50; ASTM D1525
175 °C
347 °F
Rate B/50; ISO 306