SABIC Innovative Plastics LNP STAT-KON MD000AP PP
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON MD000AP PP.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* STAT-KON* MD000AP is a compound based on Polypropylene containing Carbon Powder. Added features of this grade include: Electrically Conductive, Exceptional Processing.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.01 g/cc | 1.01 g/cc | ASTM D792 |
| Density | 1.012 g/cc | 0.03656 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.0200 % | 0.0200 % | 50% RH, 24 hrs; ASTM D570 |
| 0.0200 % | 0.0200 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.014 cm/cm @Time 86400 sec |
0.014 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.016 cm/cm @Time 86400 sec |
0.016 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 22.0 MPa | 3190 psi | 5 mm/min; ISO 527 |
| 24.0 MPa | 3480 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 2.3 % | 2.3 % | 5 mm/min; ISO 527 |
| 2.6 % | 2.6 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 1.78 GPa | 258 ksi | 1 mm/min; ISO 527 |
| 1.98 GPa | 287 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 39.0 MPa | 5660 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 39.0 MPa | 5660 psi | ISO 178 | |
| Flexural Modulus | 1.57 GPa | 228 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 1.66 GPa | 241 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.320 J/cm | 0.599 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 6.76 J/cm | 12.7 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² | 1.43 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 38.0 kJ/m² | 18.1 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 15.0 J @Temperature 23.0 °C |
11.1 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 11.0 J | 8.11 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 89.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
49.4 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 90.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
50.0 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 88.0 °C | 190 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 109 °C @Thickness 3.20 mm |
228 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 58.0 °C | 136 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 60.0 °C @Thickness 3.20 mm |
140 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 100 ohm | 100 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- Outokumpu 4565 High Performance Austenitic Stainless Steel
- Polykemi AB SCANMID 6 B32^ E F15 Nylon 6, Glass Fiber Reinforced, Modified
- Kolon SPESIN® KP513G30WBL Multi Reinforced PBT Resin
- Saint-Gobain CHR® SGB6-04(R) CHEMLAM Brown Glass-PTFE Backing Silicone Adhesive Pressure Sensitive Tape
- Sylvin Technologies 5134-70 PVC Wire/Cable Compound
- Polyram RamOfin PPH308G50 Polypropylene, 50% Glass Fiber, Impact Modified
- Covestro Desmopan® DP 3065D Polyurethane
- EMS-Griltech Griltex® D 1566A Heat Stabilized Copolyamide Hotmelt Adhesive (Apparel Interlinings)
- BASF Paliogen® Blue L 6482 Color Additive
Copyright © lookpolymers.com All Rights Reserved