SABIC Innovative Plastics SABIC PPCOMPOUND 9712 PP
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | SABIC PPCOMPOUND |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics SABIC PPCOMPOUND 9712 PP.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
SABIC® PPcompound 9712 is a mineral filled, impact modified polypropylene TPO. This material combines high impact resistance, scratch resistance, and heat stability with interior automotive UV stability. This material can exhibit ductility at temperatures as low as -30 degrees C. The IMDS is 164207488.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.04 g/cc | 1.04 g/cc | ASTM D792 |
| Density | 1.03 g/cc | 0.0372 lb/in³ | ISO 1183 |
| Melt Flow | 14 g/10 min @Load 2.16 kg, Temperature 230 °C |
14 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 15.0 MPa | 2180 psi | 50 mm/min, 1A; ISO 527 |
| Tensile Strength, Yield | 22.0 MPa | 3190 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 65 % | 65 % | 50 mm/min; ISO 527 |
| Elongation at Yield | 5.0 % | 5.0 % | 50 mm/min; ISO 527 |
| Tensile Modulus | 1.86 GPa | 270 ksi | 1 mm/min; ISO 527 |
| Flexural Modulus | 2.10 GPa | 305 ksi | 2 mm/min, 64mm span; ISO 178 |
| Izod Impact, Notched (ISO) | 32.0 kJ/m² | 15.2 ft-lb/in² | 80*10*4mm, Cut; ISO 180/1A |
| 4.00 kJ/m² @Temperature -30.0 °C |
1.90 ft-lb/in² @Temperature -22.0 °F |
80*10*4mm, Cut; ISO 180/1A | |
| Charpy Impact, Notched | 3.40 J/cm² | 16.2 ft-lb/in² | 80*10*4mm, Cut; ISO 179/1eA |
| 0.300 J/cm² @Temperature -30.0 °C |
1.43 ft-lb/in² @Temperature -22.0 °F |
80*10*4mm, Cut; ISO 179/1eA | |
| Dart Drop, Total Energy | 19.0 J @Temperature 23.0 °C |
14.0 ft-lb @Temperature 73.4 °F |
Instrumented Impact Energy @ peak, 6.6 m/s; ASTM D3763 |
| 22.0 J @Temperature -30.0 °C |
16.2 ft-lb @Temperature -22.0 °F |
Instrumented Impact Energy @ peak, -30°C @ 6.6 m/s; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 58.0 µm/m-°C @Temperature -30.0 - 100 °C |
32.2 µin/in-°F @Temperature -22.0 - 212 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 150 µm/m-°C @Temperature -30.0 - 100 °C |
83.3 µin/in-°F @Temperature -22.0 - 212 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 103 °C | 217 °F | 80*10*4mm, Cut; ISO 75-1&2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 58.0 °C | 136 °F | 80*10*4mm, Cut; ISO 75-1&2 |
| Vicat Softening Point | 136 °C | 277 °F | 10N, 50°C/hr; ISO 306 |
Users viewing this material also viewed the following:
- Nye Lubricants 738 (RL) Synthetic Oil
- Process Technologies Inc BUNA-N Sanitary Gasket
- RheTech Products HP520-00 12% Talc Reinforced High Performance Polypropylene Copolymer, Non-UV Stabilized, Natural
- Chevron Phillips HiD® 99416 with Food Grade Antistat HDPE Blow Molding Resin (discontinued **)
- Michelman® DigiPrime® 5000 Primer
- SABIC Innovative Plastics Xenoy® XD1607 PBT+PC (Europe-Africa-Middle East)
- Polyplastics Duranex® CE7300 Polybutylene Terephthalate (PBT), Higher impact resistant
- Covestro Bayfill® EA 2002 Polyurethane Energy-Absorbing Semi-Rigid Foam, Friable Grade, MDI-based 2-Component Liquid System
- ExxonMobil 103 Mobilgrease XHP Series
- Clariant Renol PA143G10 Nylon 6/66 Copolymer, 10% Glass Fiber, Heat Stabilized
Copyright © lookpolymers.com All Rights Reserved