SABIC Innovative Plastics LNP LUBRICOMP WL003 PBT
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP WL003 PBT.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* WL003 is a compound based on PBT resin containing 15% PTFE. Added feature of th is grade is: Wear Resistant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.39 g/cc | 0.0502 lb/in³ | ISO 1183 |
| 1.396 g/cc | 0.05043 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.0400 % | 0.0400 % | 50% RH, 24 hrs; ASTM D570 |
| 0.0600 % | 0.0600 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | >= 0.020 cm/cm @Time 86400 sec |
>= 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| 0.041 cm/cm @Time 86400 sec |
0.041 in/in @Time 24.0 hour |
ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.020 - 0.040 cm/cm @Time 86400 sec |
0.020 - 0.040 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 47.0 MPa | 6820 psi | Type I, 5 mm/min; ASTM D638 |
| 47.0 MPa | 6820 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 47.0 MPa | 6820 psi | Type I, 5 mm/min; ASTM D638 |
| 47.0 MPa | 6820 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 6.4 % | 6.4 % | 5 mm/min; ISO 527 |
| 7.7 % | 7.7 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 5.7 % | 5.7 % | 5 mm/min; ISO 527 |
| 6.5 % | 6.5 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 2.78 GPa | 403 ksi | 50 mm/min; ASTM D638 |
| 2.87 GPa | 416 ksi | 1 mm/min; ISO 527 | |
| Flexural Modulus | 2.19 GPa | 318 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 2.50 GPa | 363 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.310 J/cm | 0.581 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.50 J/cm | 8.43 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 27.0 kJ/m² | 12.8 ft-lb/in² | 80*10*4; ISO 180/1U |
| Coefficient of Friction, Dynamic | 0.23 | 0.23 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.16 | 0.16 | ASTM D3702 Modified |
| K (wear) Factor | 40.3 x 10-8 mm³/N-M | 20.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 158 °C | 316 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 177 °C @Thickness 3.20 mm |
351 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 62.0 °C | 144 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 58.0 °C @Thickness 3.20 mm |
136 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Network Polymers NPP 25-1011B
- Nilit Nilamid B3N Unfilled, Nucleated PA6
- Formosa Plastics Formolene® FORMAX® L71709A Film (Hexene Grade) LLDPE (discontinued **)
- STAR Thermoplastic Alloys & Rubbers StarTUFF TF 40-HR-9 TPE
- Dow Corning 704 DIFFUSION PUMP FLUID
- DuPont™ Elvax® 3178Z Ethylene Vinyl Acetate
- Ensinger Tecapeek® XP-98HT Compression Molded PEEK HT, 30% Carbon Fiber
- Diamond Polymers NPP 60-1300 GF30 30% Glass Filled Polyester Alloy
- Bapolene® 4071 Polypropylene, Fiber/Injection Grade
Copyright © lookpolymers.com All Rights Reserved