Arkema Group Appryl® CZN 0525 Polypropylene, 25% Talc Filled

Category	Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 30% Talc Filler
Manufacturer	Arkema
Trade Name	Appryl®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Arkema Group Appryl® CZN 0525 Polypropylene, 25% Talc Filled.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Compound of a PP copolymer modified with EPR and 25% talc. This grade has been specially developed for interior trim applications, that required an excellent impact test associated with a high modulus. It is UV stabilized and has a good paintability. Main application is automotive dashboards.ISO data provided by the manufacturer, Arkema.

Physical Properties	Metric	English	Comments
Density	1.12 g/cc	0.0405 lb/in³
Melt Flow	7.0 g/10 min @Load 2.16 kg, Temperature 230 °C	7.0 g/10 min @Load 4.76 lb, Temperature 446 °F

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	19.0 MPa	2760 psi	50 mm/min
Elongation at Break	26 %	26 %	Nominal Strain; 50 mm/min
Elongation at Yield	4.0 %	4.0 %	50 mm/min
Tensile Modulus	1.92 GPa	278 ksi	1 mm/min
Charpy Impact Unnotched	NB	NB
Charpy Impact, Notched	1.30 J/cm²	6.19 ft-lb/in²
	0.360 J/cm² @Temperature -30.0 °C	1.71 ft-lb/in² @Temperature -22.0 °F

Thermal Properties	Metric	English	Comments
Melting Point	161 °C	322 °F	10°C/min
Deflection Temperature at 0.46 MPa (66 psi)	102 °C	216 °F
Deflection Temperature at 1.8 MPa (264 psi)	58.0 °C	136 °F
Vicat Softening Point	52.0 °C	126 °F	50°C/hr; 50N