SABIC Innovative Plastics NORYL GFN1520V PPE+HIPS
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL GFN1520V PPE+HIPS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
NORYL GFN1520V is a 20% glass fibre reinforced material with improved hydrolytic stability. This grade has been certified for potable water applications up to 85C in Europe and North America, color dependent.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.24 g/cc | 1.24 g/cc | ASTM D792 |
| Density | 1.25 g/cc | 0.0452 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.0600 % | 0.0600 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.20 % | 0.20 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm @Thickness 3.20 mm |
0.0020 - 0.0040 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0030 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0030 - 0.0060 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 7.0 g/10 min @Load 5.00 kg, Temperature 280 °C |
7.0 g/10 min @Load 11.0 lb, Temperature 536 °F |
ASTM D1238 |
| Melt Index of Compound | 13 g/10 min @Load 10.0 kg, Temperature 280 °C |
13 g/10 min @Load 22.0 lb, Temperature 536 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 93.0 MPa | 13500 psi | Type I, 5 mm/min; ASTM D638 |
| 100 MPa | 14500 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 93.0 MPa | 13500 psi | Type I, 5 mm/min; ASTM D638 |
| 100 MPa | 14500 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 2.5 % | 2.5 % | 5 mm/min; ISO 527 |
| 2.6 % | 2.6 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 2.5 % | 2.5 % | 5 mm/min; ISO 527 |
| 2.6 % | 2.6 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 6.20 GPa | 899 ksi | 5 mm/min; ASTM D638 |
| 6.40 GPa | 928 ksi | 1 mm/min; ISO 527 | |
| Flexural Yield Strength | 140 MPa | 20300 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 145 MPa | 21000 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 5.30 GPa | 769 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 5.30 GPa | 769 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.830 J/cm | 1.55 ft-lb/in | ASTM D256 |
| 0.710 J/cm @Temperature -30.0 °C |
1.33 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Unnotched | 4.90 J/cm | 9.18 ft-lb/in | ASTM D4812 |
| 4.90 J/cm @Temperature -30.0 °C |
9.18 ft-lb/in @Temperature -22.0 °F |
ASTM D4812 | |
| Izod Impact, Unnotched (ISO) | 30.0 kJ/m² | 14.3 ft-lb/in² | 80*10*4; ISO 180/1U |
| 30.0 kJ/m² @Temperature -30.0 °C |
14.3 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1U | |
| Charpy Impact Unnotched | 3.50 J/cm² | 16.7 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eU |
| 3.50 J/cm² @Temperature -30.0 °C |
16.7 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eU | |
| Dart Drop, Total Energy | 16.0 J @Temperature 23.0 °C |
11.8 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 30.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
16.7 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 30.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
16.7 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 70.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
38.9 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 70.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
38.9 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 140 °C | 284 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 135 °C | 275 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 137 °C @Thickness 3.20 mm |
279 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 140 °C | 284 °F | Rate B/50; ASTM D1525 |
| 140 °C | 284 °F | Rate B/50; ISO 306 | |
| 145 °C | 293 °F | Rate B/120; ISO 306 | |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
UL 94 |
| Oxygen Index | 26 % | 26 % | ISO 4589 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | ROA; IEC 60093 |
| Dielectric Constant | 2.9 @Frequency 1.00e+6 Hz |
2.9 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 2.9 @Frequency 50.0 - 60.0 Hz |
2.9 @Frequency 50.0 - 60.0 Hz |
IEC 60250 | |
| Dielectric Strength | 18.0 kV/mm @Thickness 3.20 mm |
457 kV/in @Thickness 0.126 in |
in oil; IEC 60243-1 |
| Dissipation Factor | 0.00080 @Frequency 50.0 - 60.0 Hz |
0.00080 @Frequency 50.0 - 60.0 Hz |
IEC 60250 |
| 0.0030 @Frequency 1.00e+6 Hz |
0.0030 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ball Pressure Test, 125°C +/- 2°C | Passes | IEC 60695-10-2 |
Users viewing this material also viewed the following:
- Proto3000 Objet Digital Materials™ DM_8310 Rigid Opaque Prototyping Polymer
- SABIC Innovative Plastics LNP COLORCOMP EX10304C PEI (Asia Pacific)
- Karina E 75/236-D-IS Clear PVC Compound
- Intercontinental Polymers HoPBT 550 HoPBT Polymer Type - Clear, Polyester Pellets
- Saint-Gobain CHR® SG23-03(R) Primary Glass-PTFE Backing Acrylic Adhesive Pressure Sensitive Tape
- Silberline Sparkle Silvex® 755-20-C
- Chase Plastics CP Pryme® PC110R Polycarbonate, 10% Glass Fiber Reinforced
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 10.0 PHR Cumar P10 Plasticizer
- Kolon SPESIN® KP213G15 Flame Retardant PBT Resin (discontinued **)
Copyright © lookpolymers.com All Rights Reserved