Solvay Specialty Polymers Kalix® 3850 Polyamide, High Performance (HPPA), 50% Glass Fiber

Category Polymer , Renewable/Recycled Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 50% Glass Fiber Reinforced
Manufacturer Solvay Specialty Polymers
Trade Name Kalix®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Kalix® 3850 Polyamide, High Performance (HPPA), 50% Glass Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Kalix® 3850 is a 16% bio-sourced, amorphous polyphthalamide (PPA)-based compound with 50% by weight glass fiber reinforcement. This material is uniquely formulated to prevent warpage and flash in parts produced using the injection molding process. The composition of the material balances the low flash and warpage performance of Kalix® 3950 with superior mechanical performance including higher stiffness and strength. The material has been specifically developed to provide a high quality surface finish and fill thin wall section parts such as those used in mobile electronic devices. It also provides superior stain resistance in comparison to other polyamide-based materials.Features: Good Dimensional Stability; Good Impact Resistance; Good Surface Finish; High Flow; High Stiffness; High Strength; Hot Water Moldability; Low Warpage; Minimal Flash; Paintable; Platable; Stain ResistantUses: Cell Phones; Electrical Parts; Electrical/Electronic Applications; Thin-walled PartsInjection Molding Notes: Kalix® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Kalix® resins be dried prior to molding.Additional Properties: Biobased Content - ASTM D6866 16 %; Flexural Elongation at Break - ISO 178 2.9 %Information provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Density 1.55 g/cc
0.0560 lb/in³
ASTM D792
Filler Content 50 %
50 %
Glass Fiber
Water Absorption 0.17 %

@Time 86400 sec
0.17 %

@Time 24.0 hour
ISO 62
Linear Mold Shrinkage, Flow 0.00010 cm/cm
0.00010 in/in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.0027 cm/cm
0.0027 in/in
ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength, Yield 260 MPa
37700 psi
ISO 527-2
Elongation at Break 2.6 %
2.6 %
ISO 527-2
Tensile Modulus 17.9 GPa
2600 ksi
ISO 527-2
Flexural Modulus 17.7 GPa
2570 ksi
ISO 178
Izod Impact, Notched (ISO) 17.0 kJ/m²
8.09 ft-lb/in²
Type 1, Notch A; ISO 180
Izod Impact, Unnotched (ISO) 87.0 kJ/m²
41.4 ft-lb/in²
ISO 180
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 145 °C
293 °F
HDT B; Unannealed; ISO 75-2/B
Deflection Temperature at 1.8 MPa (264 psi) 137 °C
279 °F
Annealed; ISO 75-2/A
Glass Transition Temp, Tg 144 °C
291 °F
DSC
Electrical Properties Metric English Comments
Dielectric Constant 3.86

@Frequency 2.40e+9 Hz
3.86

@Frequency 2.40e+9 Hz
ASTM D2520
3.98

@Frequency 1.00e+9 Hz
3.98

@Frequency 1.00e+9 Hz
ASTM D2520
Dissipation Factor 0.013

@Frequency 1.00e+9 Hz
0.013

@Frequency 1.00e+9 Hz
Method B; ASTM D2520
0.014

@Frequency 2.40e+9 Hz
0.014

@Frequency 2.40e+9 Hz
Method B; ASTM D2520
Processing Properties Metric English Comments
Rear Barrel Temperature 270 °C
518 °F
Front Barrel Temperature 300 °C
572 °F
Melt Temperature 310 - 330 °C
590 - 626 °F
Mold Temperature 80.0 - 130 °C
176 - 266 °F
Drying Temperature 80.0 °C

@Time 14400 - 43200 sec
176 °F

@Time 4.00 - 12.0 hour
Moisture Content <= 0.090 %
<= 0.090 %
Descriptive Properties Value Comments
Availability Asia Pacific
Europe
North America
Color Black; White
Form Pellets
Part Marking Code >PA10I/10T/X-GF50<
ISO 11469
Processing Technique Injection Molding; Water-Heated Mold Injection Molding
RoHS Compliance RoHS Compliant