SABIC Innovative Plastics LNP THERMOCOMP DF002ERH PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP DF002ERH PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* DF002ERH is a compound based on Polycarbonate resin containing 10% Glass Fiber. Added features of this material include: Easy Molding, Healthcare, Mold Release.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.27 g/cc | 0.0459 lb/in³ | ISO 1183 |
| 1.275 g/cc | 0.04606 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.150 % | 0.150 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm @Time 86400 sec |
0.0040 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0043 cm/cm @Time 86400 sec |
0.0043 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0050 cm/cm @Time 86400 sec |
0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0051 cm/cm @Time 86400 sec |
0.0051 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 83.0 MPa | 12000 psi | ASTM D638 |
| 84.0 MPa | 12200 psi | ISO 527 | |
| Elongation at Break | 3.6 % | 3.6 % | ISO 527 |
| 3.8 % | 3.8 % | ASTM D638 | |
| Tensile Modulus | 4.10 GPa | 595 ksi | 1 mm/min; ISO 527 |
| 4.17 GPa | 605 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 117 MPa | 17000 psi | ISO 178 |
| 149 MPa | 21600 psi | ASTM D790 | |
| Flexural Modulus | 3.92 GPa | 569 ksi | ISO 178 |
| 4.28 GPa | 621 ksi | ASTM D790 | |
| Izod Impact, Notched | 0.970 J/cm | 1.82 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 9.29 J/cm | 17.4 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 61.0 kJ/m² | 29.0 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 13.0 J | 9.59 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 9.00 J | 6.64 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 38.1 µm/m-°C @Temperature -40.0 - 40.0 °C |
21.2 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 38.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
21.2 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 53.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
29.7 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 53.5 µm/m-°C @Temperature -40.0 - 40.0 °C |
29.7 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 141 °C | 286 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 141 °C @Thickness 3.20 mm |
286 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 137 °C | 279 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 136 °C @Thickness 3.20 mm |
277 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Nye Lubricants 123S (Nyeoil2) Oil
- Palm Labs Adhesives Turbo Fuse Series 120SI Surface Insensitive (40 Viscosity) Rapid Bonding Adhesive
- Huntsman Araldite GY 6008 Bisphenol A Epoxy Liquid Resin
- SABIC Innovative Plastics XYLEX X8300 PC+POLYESTER (Asia Pacific)
- A. Schulman POLYBLAK™ 2723Pm Premium Black Color Concentrate, 25% Carbon Black Based In HDPE
- A. Schulman PP 828-01 Polypropylene Molding Grade Impact Polypropylene
- Chevron Phillips K-Resin® KR03NW Styrene-Butadiene Copolymer, Sheet Grade
- Chosun Refractories CT-140S Fireclay Castables
- Arkema Group EVATANE® 42-60 Copolymer Ethylene - Vinyl Acetate
Copyright © lookpolymers.com All Rights Reserved