- Sax Polymers SAXALEN PPH304G25 Polypropylene Homopolymer, 25% Glass Filled
Sax Polymers SAXALEN PPH304G25 Polypropylene Homopolymer, 25% Glass Filled
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Glass Fiber Filler |
| Manufacturer | Sax Polymers |
| Trade Name | SAXALEN |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sax Polymers SAXALEN PPH304G25 Polypropylene Homopolymer, 25% Glass Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
SAXALEN PPH304G25 is a 25% glass filled Polypropylene - Homopolymer intended for injection molding. This compound is characterized by high stiffness good impact resistance und reduced creep under load.Information provided by SAX Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | |
| Melt Flow | 14 g/10 min @Load 2.16 kg, Temperature 230 °C |
14 g/10 min @Load 4.76 lb, Temperature 446 °F |
from MVR; ISO 1033 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 78.0 MPa | 11300 psi | 5 mm/min; ISO 527-1 |
| Elongation at Break | 3.0 % | 3.0 % | 5 mm/min; ISO 527-1 |
| Tensile Modulus | 5.30 GPa | 769 ksi | 1 mm/min; ISO 527-1 |
| Flexural Strength | 100 MPa | 14500 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 4.40 GPa | 638 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² @Temperature -30.0 °C |
3.33 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1A |
| 8.00 kJ/m² @Temperature 23.0 °C |
3.81 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 40.0 kJ/m² @Temperature -30.0 °C |
19.0 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1U |
| 43.0 kJ/m² @Temperature 23.0 °C |
20.5 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1U | |
| Charpy Impact Unnotched | 4.00 J/cm² @Temperature -30.0 °C |
19.0 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 4.80 J/cm² @Temperature 23.0 °C |
22.8 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 0.700 J/cm² @Temperature -30.0 °C |
3.33 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 0.900 J/cm² @Temperature 23.0 °C |
4.28 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 137 °C | 279 °F | 80*10*4 s=60mm; ISO 75-1 a |
| Vicat Softening Point | 135 °C | 275 °F | B/120; ISO 306 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 220 - 250 °C | 428 - 482 °F | |
| Mold Temperature | 40.0 - 70.0 °C | 104 - 158 °F |
Users viewing this material also viewed the following:
- MV Labs CD300 CdCO3 Cadmium carbonate
- Nitriflex N-7411 NBR / PVC
- BASF Capron® SEG6 H1 30% Glass-Filled Nylon 6 (Dry) (discontinued **)
- Westlake EMAC® SP2202 21.5% Ethylene-Methyl Acrylate Copolymer
- Lubrizol ESTANE® 58130 Ester Based Thermoplastic Polyurethane (European Grade)
- China Tungsten YG13 Tungsten Carbide Powder
- CIMBAR CIMTUFF® 9107 Talc
- Arlon 28601M015 0.015" (0.381 mm) Uncured Silicone Rubber with Fiberglass Substrate
Copyright © lookpolymers.com All Rights Reserved