- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 99.0 °C
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 99.0 °C Product List
Thermal PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 99.0 °C | 210 °F | |
| Plastcom SLOVALEN PQ 81 T 25 PP, 25% mineral filling FeaturesModified PP for injection moulding with the content of 25% mineral filling. Increased rigidity, strength and thermal use up to 130°C depending on the talc content. Decreased shri nkage. Gen.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 99.0 °C | 210 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics Cycolac® INP630 ABS INP630 is a specialty polymer that increases the service temperature of products. Can be used with a impact modifier to provide impact strength as well as high heat resistance.
Provides excellent hi.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 99.0 °C | 210 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics Cycolac® INP630 ABS+SAN INP630 is a specialty polymer that increases the service temperature of products. Can be used with a impact modifier to provide impact strength as well as high heat resistance. Provides excellent hi.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 99.0 °C @Thickness 6.40 mm |
210 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Cycoloy® CX7240U PC+ABS Cycoloy* CX7240U resin is an injection moldable PC/ABS blend with a UV stabilization package. It contains non-brominated and non-chlorinated flame retardant systems to meet thin wall flame resistanc.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 99.0 °C @Thickness 3.20 mm |
210 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP FARADEX WX94736 PBT LNP* Faradex* WX94736 is a compound based on Polybutylene Terephalate resin containing Stainless Steel. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 99.0 °C | 210 °F | Unannealed; ASTM D648 |
| PolyOne Edgetek® AS-10GF/000 BLACK Acrylonitrile Butadiene Styrene (ABS) The Edgetek® Engineering Thermoplastic Compounds portfolio covers a broad range of standard and custom-formulated high performance materials. This portfolio includes high-temperature materials for .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 99.0 °C | 210 °F | Unannealed; ASTM D648 |
| PolyOne Edgetek® AS-10GF/000 FR V0 BLACK Acrylonitrile Butadiene Styrene (ABS) Information provided by PolyOne |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 99.0 °C @Thickness 6.40 mm |
210 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| LG Chemical LUPOS GP2300 ABS+GF30%, General Purpose Feature: Injection Molding, ABS+GF30%, General PurposeApplication: Electric & Electronic (Housing, Components)CAS No. 9003-54-7, 9003-56-9 and 65997-17-3Information provided by LG Chemical |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 99.0 °C @Thickness 3.20 mm |
210 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP KL003 Acetal Copolymer (Asia Pacific) LNP* LUBRICOMP* KL003 is a compound based on Acetal Copolymer resin containing PTFE. Added features of this material include: Internally Lubricated. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 99.0 °C @Thickness 3.20 mm |
210 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP KL004 Acetal Copolymer (Europe-Africa-Middle East) LNP* LUBRICOMP* KL004 is a compound based on Acetal Copolymer containing PTFE. Added features include Internally Lubricated. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 99.0 °C | 210 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP LUBRICOMP KP004A Acetal Homopolymer LNP* LUBRICOMP* KP004A is a compound based on Acetal Homopolymer resin containing 20% PTFE/Silicone. Added feature of this material is: Wear Resistant. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 99.0 °C @Thickness 3.20 mm |
210 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics LNP LUBRICOMP KP004A Acetal Homopolymer LNP* LUBRICOMP* KP004A is a compound based on Acetal Homopolymer resin containing 20% PTFE/Silicone. Added feature of this material is: Wear Resistant. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 99.0 °C | 210 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP LUBRICOMP KP004AXC Acetal Homopolymer LNP LUBRICOMP* KP004AXC is a compound based on Acetal Homopolymer resin containing 20% PTFE/Silicone. Added feature of this material is: Wear Resistant. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 99.0 °C | 210 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP LUBRILOY D20001 PPO LNP* LUBRILOY* Z20001 is a compound based on PPO resin containing Proprietary Lubricant. Added features of this material include: Wear Resistant, Flame Retardant. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 99.0 °C | 210 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP STAT-KON AE003 ABS (Europe-Africa-Middle East) LNP* STATKON* AE003 is a compound based on Acrylonitrile Butadiene Styrene resin containing Carbon Fiber. Added features inclurde : Electrically Conductive. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 99.0 °C @Thickness 6.40 mm |
210 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| SABIC Innovative Plastics Xenoy® 5220U PBT+PC (Asia Pacific) Unreinforced PBT+PC Alloy. Impact Modified. Improved retention of mechanical properties under UV exposure. Excellent low temperature impact and chemical resistance. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 99.0 °C | 210 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| SABIC Innovative Plastics Xylex X7200 PC+POLYESTER (Europe-Africa-Middle East) General purpose, UV stabilised Xylex gradeThis data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 99.0 °C | 210 °F | ISO 75 |
| Styrolution Novodur® H702 ABS Novodur H702 is a high heat, high gloss injection molding grade with very good flowabilityInformation provided by Styrolution |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 99.0 °C | 210 °F | ISO 75 |
| Styrolution Terluran® GP-22 ABS Terluran GP-22 is an easy flowing grade of ABS for injection molding with high resistance to impact and heat deflection.Information provided by STYROLUTION, which is a joint venture between BASF and.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 99.0 °C | 210 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| SABIC Innovative Plastics LNP THERMOCOMP MF002S PP LNP* Thermocomp* MF002S is a compound based on Polypropylene resin containing 10% Glass Fiber. Added features of this material include: Heat Stabilized. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 99.0 °C | 210 °F | ASTM D648 |
| PlastxWorld Veroplas PB2001F Nylon 66 flame retarded (UL94 V0), unfilled injection molding gradeInformation provided by PlastxWorld Inc. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 99.0 °C | 210 °F | ISO 75-1,-2 |
| Covestro Bayblend® T65 HI PC/ABS Blend Main characteristics:• High toughness even at low temperatures• High dimensional accuracy and stability• Good paintability• Good flowabilityGrade characteristics:• Improve low temperature .. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 99.0 °C | 210 °F | annealed; ISO 75 |
| Chi Mei Polyrex® PG-383 Polystyrene High heat; high strength |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 99.0 °C | 210 °F | ASTM D638 |
| ExxonMobil Paxon™ 7004 Crosslinkable Rotational Molding Resin Product Description: Paxon™ 7000 series of crosslinkable mHDPE resins are designed to offer outstanding ESCR, toughness, thermal, impact and notch failure resistance. These resins are ideally suite.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 99.0 °C | 210 °F | ASTM D648 |
| Buckeye Polymers BP ABS 5425 ABS General PurposeABS is a copolymer of acrylonitrile and styrene, modified with butadiene rubber. ABS is primarily used for their combination of toughness, rigidity, chemical resistance, ease of proc.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 99.0 °C | 210 °F | ASTM D648 |
| Ashley Polymers Ashlene® 528MS/528SMS Nylon 66, MoS2 Filled A general purpose Molybdenum-disulfide filled nylon resin.Data provided by the manufacturer |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 99.0 °C | 210 °F | ASTM D648 |
| A. Schulman ComAlloy Hiloy® 419 Polyester - PBT, Mineral Reinforced Data provided by the manufacturer, ComAlloy International Company.40% Mineral Reinforced.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 99.0 °C | 210 °F | ASTM D648 |
| Buckeye Polymers BP ABS 4233 B ABS Utility GradeABS is a copolymer of acrylonitrile and styrene, modified with butadiene rubber. ABS is primarily used for their combination of toughness, rigidity, chemical resistance, ease of proces.. |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 99.0 - 112 °C | 210 - 234 °F | Average value: 106 °C Grade Count:6 |
| Overview of materials for Acrylic, Cast This property data is a summary of similar materials in the MatWeb database for the category "Acrylic, Cast". Each property range of values reported is minimum and maximum values of appropriate MatW.. |
|||
Copyright © lookpolymers.com All Rights Reserved