A. Schulman ComAlloy Hiloy® 419 Polyester - PBT, Mineral Reinforced
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Mineral Filled |
| Manufacturer | A. Schulman ComAlloy |
| Trade Name | Hiloy® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | A. Schulman ComAlloy Hiloy® 419 Polyester - PBT, Mineral Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by the manufacturer, ComAlloy International Company.40% Mineral Reinforced.The ComAlloy product line has been integrated into the A Schulman product line.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.62 g/cc | 0.0585 lb/in³ | |
| Linear Mold Shrinkage | 0.0090 cm/cm | 0.0090 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 115 | 115 | ASTM D785 |
| Tensile Strength, Ultimate | 59.0 MPa | 8560 psi | ASTM D638 |
| Elongation at Break | 6.7 % | 6.7 % | ASTM D638 |
| Flexural Strength | 96.0 MPa | 13900 psi | ASTM D790 |
| Flexural Modulus | 4.00 GPa | 580 ksi | ASTM D790 |
| Izod Impact, Notched | 0.270 J/cm | 0.506 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.83 J/cm | 5.30 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 210 - 225 °C | 410 - 437 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 193 °C | 379 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 99.0 °C | 210 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Middle Barrel Temperature | 235 - 249 °C | 455 - 480 °F |
Users viewing this material also viewed the following:
- Multibase SILASTIC® Q7-4735 Dow-Corning Biomedical Grade ETR Elastomer
- Permabond 108 Cyanoacrylate, gap filling
- Karina E 898-10/137-IS-RG White PVC Compound
- A. Schulman POLYBATCH™ Grey 8368 Concentrate Based In Polyethylene
- Toyobo Vylopet® EMC330K Glass Reinforced Polyester, Easy Molding Grade
- TPI Porene® ABS-SP-100 Super High Impact ABS Resin
- ExxonMobil Mobil Polyrex EM
- Atom Adhesives AA-DUCT 2924 Epoxy Adhesive
- Lubrizol Advanced Materials Pearlstick® 45-40/15 Polycaprolactone based TPU
Copyright © lookpolymers.com All Rights Reserved