- Styrolution Novodur® H702 ABS
Styrolution Novodur® H702 ABS
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Heat Resistant, Molded |
| Manufacturer | Styrolution |
| Trade Name | Novodur® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styrolution Novodur® H702 ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Novodur H702 is a high heat, high gloss injection molding grade with very good flowabilityInformation provided by Styrolution
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | ISO 294-4 |
| Melt Flow | 16 g/10 min @Load 10.0 kg, Temperature 220 °C |
16 g/10 min @Load 22.0 lb, Temperature 428 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 105 MPa | 15200 psi | ISO 2039-1 |
| Tensile Strength, Yield | 46.0 MPa | 6670 psi | ISO 527 |
| Elongation at Break | 15 % | 15 % | ISO 527 |
| Elongation at Yield | 2.6 % | 2.6 % | ISO 527 |
| Tensile Modulus | 2.50 GPa | 363 ksi | ISO 527 |
| Flexural Strength | 73.0 MPa | 10600 psi | ISO 178 |
| Flexural Modulus | 2.40 GPa | 348 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² @Temperature -30.0 °C |
3.81 ft-lb/in² @Temperature -22.0 °F |
ISO 180/A |
| 17.0 kJ/m² @Temperature 23.0 °C |
8.09 ft-lb/in² @Temperature 73.4 °F |
ISO 180/A | |
| Charpy Impact Unnotched | 9.00 J/cm² @Temperature -30.0 °C |
42.8 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| 10.0 J/cm² @Temperature 23.0 °C |
47.6 ft-lb/in² @Temperature 73.4 °F |
ISO 179 | |
| Charpy Impact, Notched | 0.800 J/cm² @Temperature -30.0 °C |
3.81 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| 1.60 J/cm² @Temperature 23.0 °C |
7.61 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 80.0 µm/m-°C | 44.4 µin/in-°F | ISO 11359 |
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C | 219 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 99.0 °C | 210 °F | ISO 75 |
| Vicat Softening Point | 103 °C @Load 5.10 kg |
217 °F @Load 11.2 lb |
50°C/h; ISO 306 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 60093 |
| Dielectric Constant | 3.1 @Frequency 100 Hz |
3.1 @Frequency 100 Hz |
IEC 60250 |
| Dielectric Strength | 36.0 kV/mm @Thickness 1.50 mm |
914 kV/in @Thickness 0.0591 in |
Short Time; IEC 60243-1 |
| Dissipation Factor | 0.0050 @Frequency 100 Hz |
0.0050 @Frequency 100 Hz |
IEC 60250 |
| 0.0090 @Frequency 1.00e+6 Hz |
0.0090 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 240 °C | 464 °F | ISO 294 |
| Mold Temperature | 70.0 °C | 158 °F | ISO 294 |
| Injection Velocity | 240 mm/sec | 9.45 in/sec | ISO 294 |
| Drying Temperature | 80.0 °C @Time 7200 - 14400 sec |
176 °F @Time 2.00 - 4.00 hour |
Users viewing this material also viewed the following:
- NOVA Chemicals Surpass® RMs341-U Octene sHDPE Rotational Molding Resin
- Kinlead LSS13 Low Temperature Grade Heat Sealable Film (thickness: 20 µm)
- Momentive Performance Materials Siloprenâ„¢ LSR 2650 ZKS Custom Liquid Silicone Rubber - Automotive
- Solvay TECHNYL® C 246SI V30 PA6, 30% glass filled, Conditioned
- Styron DL 239NA Carboxylated SB
- A. Schulman SUPERLINEAR™ XL 0370 Rotational Molding Resin
- Aaron Industries AAROPRENE® GFPP 2040 Glass Filled Polypropylene
- Huntsman PE6014 Blow Molding Polyethylene (discontinued **)
Copyright © lookpolymers.com All Rights Reserved