SABIC Innovative Plastics Cycolac® INP630 ABS

Category	Polymer , Thermoplastic , ABS Polymer
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	Cycolac®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics Cycolac® INP630 ABS.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

INP630 is a specialty polymer that increases the service temperature of products. Can be used with a impact modifier to provide impact strength as well as high heat resistance. Provides excellent high heat resistance in thermoplastic polymers. Offers excellent flow properties in outdoor applications.This data was supplied by SABIC-IP for the Americas region.

Physical Properties	Metric	English	Comments
Specific Gravity	1.09 g/cc	1.09 g/cc	ASTM D 792
Density	1.09 g/cc	0.0394 lb/in³	ISO 1183
Melt Flow	10.9 g/10 min @Load 3.80 kg, Temperature 230 °C	10.9 g/10 min @Load 8.38 lb, Temperature 446 °F	ASTM D 1238
	21 g/10 min @Load 10.0 kg, Temperature 220 °C	21 g/10 min @Load 22.0 lb, Temperature 428 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Flexural Yield Strength	58.0 MPa	8410 psi	2 mm/min; ISO 178
	115 MPa	16700 psi	1.3 mm/min, 50 mm span; ASTM D 790
Flexural Modulus	3.62 GPa	525 ksi	2 mm/min; ISO 178
	3.88 GPa	563 ksi	1.3 mm/min, 50 mm span; ASTM D 790
Izod Impact, Notched	0.130 J/cm @Temperature -30.0 °C	0.244 ft-lb/in @Temperature -22.0 °F	ASTM D 256
	0.190 J/cm @Temperature 23.0 °C	0.356 ft-lb/in @Temperature 73.4 °F	ASTM D 256
Izod Impact, Notched (ISO)	1.00 kJ/m² @Temperature -30.0 °C	0.476 ft-lb/in² @Temperature -22.0 °F	80104; ISO 180/1A
	3.00 kJ/m² @Temperature 23.0 °C	1.43 ft-lb/in² @Temperature 73.4 °F	80104; ISO 180/1A
Charpy Impact, Notched	0.100 J/cm² @Temperature 23.0 °C	0.476 ft-lb/in² @Temperature 73.4 °F	ISO 179/2C

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	110 °C @Thickness 3.20 mm	230 °F @Thickness 0.126 in	unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi)	99.0 °C	210 °F	Flatw 80104 sp=64mm; ISO 75/Af
	100 °C @Thickness 3.20 mm	212 °F @Thickness 0.126 in	unannealed; ASTM D 648
Vicat Softening Point	116 °C	241 °F	Rate B/50; ISO 306
	118 °C	244 °F	Rate B/120; ISO 306

Optical Properties	Metric	English	Comments
Yellow Index	6.0 %	6.0 %	ASTM D 1925

Users viewing this material also viewed the following: