- Acrylonitrile Butadiene Styrene (ABS), Impact Grade, Molded
- Styrolution Terluran® GP-22 ABS
Styrolution Terluran® GP-22 ABS
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Impact Grade, Molded |
| Manufacturer | Styrolution |
| Trade Name | Terluran® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styrolution Terluran® GP-22 ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Terluran GP-22 is an easy flowing grade of ABS for injection molding with high resistance to impact and heat deflection.Information provided by STYROLUTION, which is a joint venture between BASF and INEOS.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ISO 1183 |
| Water Absorption | 1.0 % | 1.0 % | ISO 62 |
| Moisture Absorption at Equilibrium | 0.22 % | 0.22 % | 23°C/50% R.H.; ISO 62 |
| Linear Mold Shrinkage | 0.0055 cm/cm | 0.0055 in/in | ASTM Data; MD |
| Melt Flow | 1.5 g/10 min @Load 5.00 kg, Temperature 200 °C |
1.5 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM Test |
| 4.8 g/10 min @Load 3.80 kg, Temperature 230 °C |
4.8 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM Test | |
| 19 g/10 min @Load 10.0 kg, Temperature 220 °C |
19 g/10 min @Load 22.0 lb, Temperature 428 °F |
ISO 1133 | |
| 19 g/10 min @Load 10.0 kg, Temperature 220 °C |
19 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM Test |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 103 | 103 | ASTM Test |
| Tensile Strength, Yield | 45.0 MPa | 6530 psi | 50mm/min; ISO 527 |
| 45.0 MPa | 6530 psi | 2 in/min; ASTM Test | |
| 19.0 MPa @Temperature 80.0 °C |
2760 psi @Temperature 176 °F |
ISO Data | |
| 63.0 MPa @Temperature -40.0 °C |
9140 psi @Temperature -40.0 °F |
ISO Data | |
| Elongation at Break | 10 % | 10 % | 50mm/min, Nominal strain; ISO 527 |
| Elongation at Yield | 2.6 % | 2.6 % | 50mm/min; ISO 527 |
| 2.6 % | 2.6 % | 2 in/min; ASTM Test | |
| 2.4 % @Temperature 80.0 °C |
2.4 % @Temperature 176 °F |
ISO Data | |
| 3.6 % @Temperature -40.0 °C |
3.6 % @Temperature -40.0 °F |
ISO Data | |
| Tensile Modulus | 2.30 GPa | 334 ksi | 1mm/min; ISO 527 |
| 2.30 GPa | 334 ksi | ASTM Test | |
| Flexural Strength | 65.0 MPa | 9430 psi | ISO Data |
| 65.0 MPa | 9430 psi | ASTM Test | |
| Flexural Modulus | 2.30 GPa | 334 ksi | ASTM Test |
| Izod Impact, Notched | 0.600 J/cm @Temperature -30.0 °C |
1.12 ft-lb/in @Temperature -22.0 °F |
ASTM Test |
| 1.00 J/cm @Temperature -18.0 °C |
1.87 ft-lb/in @Temperature -0.400 °F |
ASTM Test | |
| 3.00 J/cm @Thickness 3.17 mm |
5.62 ft-lb/in @Thickness 0.125 in |
ASTM Test | |
| Izod Impact, Notched (ISO) | 26.0 kJ/m² | 12.4 ft-lb/in² | ISO Test |
| Charpy Impact Unnotched | 18.0 J/cm² | 85.7 ft-lb/in² | ISO 179 |
| 10.0 J/cm² @Temperature -30.0 °C |
47.6 ft-lb/in² @Temperature -22.0 °F |
ISO 179 | |
| Charpy Impact, Notched | 2.20 J/cm² | 10.5 ft-lb/in² | ISO 179 |
| 0.800 J/cm² @Temperature -30.0 °C |
3.81 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 95.0 µm/m-°C | 52.8 µin/in-°F | ISO 11359 |
| Deflection Temperature at 0.46 MPa (66 psi) | 91.0 °C | 196 °F | ASTM Test |
| 103 °C | 217 °F | ISO 75 | |
| 104 °C | 219 °F | annealed; ASTM Test | |
| Deflection Temperature at 1.8 MPa (264 psi) | 78.0 °C | 172 °F | ASTM Test |
| 99.0 °C | 210 °F | ISO 75 | |
| 99.0 °C | 210 °F | annealed; ASTM Test | |
| Vicat Softening Point | 96.0 °C | 205 °F | Rate "A" Loading 2 (50 degC/h 50N); ASTM Test |
| 96.0 °C | 205 °F | (50 °C/h / 50N) - B/50; ISO 306 | |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
|
| HB @Thickness 0.800 mm |
HB @Thickness 0.0315 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | IEC 60093 |
| Dielectric Constant | 2.8 @Frequency 1.00e+6 Hz |
2.8 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 2.9 @Frequency 100 Hz |
2.9 @Frequency 100 Hz |
IEC 60250 | |
| Dielectric Strength | 37.0 kV/mm | 940 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.0048 @Frequency 100 Hz |
0.0048 @Frequency 100 Hz |
IEC 60250 |
| 0.0079 @Frequency 1.00e+6 Hz |
0.0079 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 250 °C | 482 °F | Injection molding |
| Mold Temperature | 100 °C | 212 °F | Ejection temperature |
| Injection Velocity | 60.0 mm/sec | 2.36 in/sec | Injection molding |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Natural | |
| Commercial Status | North America and Europe | |
| FDA | Yes | |
| Form | Pellets | |
| Impact Modified | Yes | |
| NSF Std. 14 | Yes | |
| NSF Std. 51 | Yes | |
| NSF Std. 61 | Yes | |
| Primary Processing Technique | Injection Molding | |
| Processing | Injection Molding | |
| Special characteristic | Lubricant | |
| Platable | ||
| UL.UL-C | Yes | |
| USP Class VI | No |
Users viewing this material also viewed the following:
- Poco Graphite SUPERSiC® Basic Silicon Carbide
- Parker Chomerics THERM-A-FORM T646 Cure-in-Place Potting and Underfill Material
- SABIC Innovative Plastics LNP VERTON RV0079 PA 66 (Asia Pacific)
- Unipetrol PP MONSTEN® MT 825 Polypropylene Random Copolymer
- DuPont Nucrel® 31001 Ethylene-Acrylic Acid Copolymer Resin for Blown and Cast Film
- A. Schulman POLYFORT™ FPP 2122UV-M-31 Black, Talc Filled Copolymer Polypropylene
- Dow Corning 7096N CLEAR SEALANT
- DuPont™ Surlyn® 8660 Ionomer Resin, Sodium
- Ashley Polymers Ashlene® ABS Resin F-216
Copyright © lookpolymers.com All Rights Reserved