- Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 162 °F
Polymer Property : Deflection Temperature at 0.46 MPa (66 psi) = 162 °F Product List
Thermal PropertiesTips: 30 items are displayed at most.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 72.0 °C | 162 °F | |
|
Eastman Eastapak 7352 PET
(discontinued **)
Unreinforced Low IV. ISO data as provided by the manufacturer, Eastman Chemical.This product is discontinued; 2003.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 72.0 °C | 162 °F | ASTM D648 |
|
Braskem HB 0055 HDPE Blow Molding Polyethylene
(discontinued **)
Applications: 200 liters L-ring drums. Information provided by Braskem
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 72.0 °C | 162 °F | ASTM D648 |
|
Braskem BT 100K HDPE Blow Molding Polyethylene
(discontinued **)
Applications: Large containers from 60 to 200 litersInformation provided by Braskem
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 72.0 °C | 162 °F | ASTM D648 |
|
Braskem BT 003 HDPE Blow Molding Polyethylene
(discontinued **)
Applications: Bottles for food products, lubricating and cooking oil; toys; bottler for surface-active agents; sheets. Information provided by Braskem
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 72.0 °C | 162 °F | ISO 75 |
|
Manifattura Cattaneo PVC U Polyvinyl Chloride
Manifattura Cattaneo products are available in semi-finished forms such as bars, profiles, sheets and plates.Information provided by Manifattura Cattaneo s.p.a.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 72.0 °C | 162 °F | ASTM D648 |
|
LyondellBasell Petrothene® LB500301 High Density Polyethylene, Blow Molding Grade
PETROTHENE LB500301 is a polyethylene resin that exhibits excellent environmental stress crack resistance and is especially designed for heavy duty bottles, such as those containing detergent and ch..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
72.0
°C <br>@Thickness 3.20 mm
|
162
°F <br>@Thickness 0.126 in
|
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP LUBRICOMP FL003 PE
LNP* LUBRICOMP* FL003 is a compound based on Polyethylene resin containing 15% PTFE. Added features include: Internally Lubricated.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 72.2 °C | 162 °F | Unannealed; ASTM D648 |
|
Techmer ES HiFill FR® HDPE 8904 FR UV GY
Availability: North AmericaForms: PelletsAdditive: UV StabilizerFeatures: Flame Retardant and Good UV ResistanceAppearance: GrayInformation provided by TP Composites, Inc.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 72.2 °C | 162 °F | Unannealed; ASTM D648 |
|
Techmer ES HiFill® HDPE 8904 UV GY
Availability: North AmericaForms: PelletsAdditive: UV StabilizerFeatures: Good UV ResistanceAppearance: GreyInformation provided by TP Composites, Inc.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 72.0 °C | 162 °F | Annealed; ASTM D648 |
|
Spartech Royalite R60M Hi-Impact ABS/PVC Resin
Data provided by the manufacturer. This rigid, fire-rated, proprietary resin is specifically formulated to meet the requirements of the FAR 25.853 A flammability test. Primary applications are air..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 72.0 °C | 162 °F | ASTM D648 |
|
Borealis Borecene Compact™ RM7406 Black Metallocene Linear Polyethylene for Rotational Molding
Borecene Compact RM7406 is a third generation linear medium density black polyethylene for rotational molding. The narrow molecular weight imparted through metallocene catalyst technology provides ..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 72.0 °C | 162 °F | ASTM D648 |
|
Borealis Borecene™ RM7402 Linear Polyethylene for Rotational Molding
Borecene RM7402 is a third generation linear medium density natural polyethylene for rotational molding. The narrow molecular weight distribution imparted through metallocene catalyst technology pro..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 72.0 °C | 162 °F | ISO 75-2 |
|
Borealis BorPURE™ RE450MO Polypropylene Random Copolymer
BorPure™ RE450MO is a specially modified highly-transparent polypropylene random copolymer with medium melt flow rate. This grade is characterized by optimum combination of high impact strength and..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 72.2 °C | 162 °F | ASTM D648 |
|
A. Schulman LB502-01 High Molecular Weight, High-Density Polyethylene Copolymer
DescriptionLP 502-01 Natural is a high molecular weight, high-density polyethylene copolymer, designed for blow molding of large parts where the finished product demands outstanding physical perform..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 72.2 °C | 162 °F | ASTM D648 |
|
A. Schulman LB502-01 High Molecular Weight, High-Density Polyethylene Copolymer
DescriptionLP 502-01 Natural is a high molecular weight, high-density polyethylene copolymer, designed for blow molding of large parts where the finished product demands outstanding physical perform..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) |
72.0
°C <br>@Thickness 3.20 mm
|
162
°F <br>@Thickness 0.126 in
|
ISO 75 |
|
A. Schulman FORMION™ FI 389 Ionomer
Information provided by A. Schulman.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 72.2 °C | 162 °F | ASTM D648 |
|
A. Schulman LB502-01 High Molecular Weight, High-Density Polyethylene Copolymer
DescriptionLP 502-01 Natural is a high molecular weight, high-density polyethylene copolymer, designed for blow molding of large parts where the finished product demands outstanding physical perform..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 72.2 °C | 162 °F | ASTM D648 |
|
A. Schulman LB502-01 High Molecular Weight, High-Density Polyethylene Copolymer
DescriptionLP 502-01 Natural is a high molecular weight, high-density polyethylene copolymer, designed for blow molding of large parts where the finished product demands outstanding physical perform..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 72.0 °C | 162 °F | ISO 75 |
|
Eastman DuraStar DS1000 Polymer, Natural
Durastar DS1000 polymer has excellent appearance and clarity. Its most outstanding features are chemical resistance and excellent processing characteristics. Exposure to aromatic oils often causes c..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 72.0 °C | 162 °F | ASTM D648 |
|
Eastman Eastar DN114 Copolyester, Natural
Applications:LightingProduct Description: Eastar copolyesters are brilliantly clear polymers that have excellent impact strength, chemical resistance, dimensional stability, and low shrinkage. DN1..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 72.0 °C | 162 °F | ASTM D648 |
|
Eastman Tenite 285A2R30020 Cellulose Acetate Butyrate, Natural, Trsp
Applications:Tool handlesToys/sporting goodsProduct Description: Tenite cellulosic plastics are noted for their excellent balance of properties - toughness, hardness, strength, surface gloss, clar..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 72.0 °C | 162 °F | ASTM D648 |
|
Eastman TiGlaze SV Copolyester
TiGLAZE SV copolyester is a specialty copolyester for the architectural glazing industry, designed to provide a unique balance of toughness, stiffness and material value. The material has a CC1 Ligh..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 72.2 °C | 162 °F | Unannealed; ASTM D648 |
|
Dow R792-35RNA Polypropylene Random Copolymer Resin
OverviewControlled rheology productConsistent processabilityContains clarifying additiveContains an antistatic additiveComplies with U.S. FDA 21 CFR 177.1520 (c)3.1a, Canadian HPFB No ObjectionDOW R..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 72.0 °C | 162 °F | ASTM-D648 |
|
Braskem AC59 HDPE Monofilament Polyethylene Homopolymer
AC59 resin is a high-density polyethylene homopolymer produced by the solution process and designed for monofilament applications. It contains antioxidant additives. Its applications include: film ..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 72.0 °C | 162 °F | ASTM-D648 |
|
Braskem GP100OR HDPE High Density Extrusion Polyethylene
GP100OR is a high-density polyethylene compound specially developed for the manufacturing of extruded pipes for gas distribution. It is produced with bimodal technology and has high molar mass. It s..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 72.0 °C | 162 °F | ISO 75 |
|
Addcomp PRIEX® 25097 Maleic Anhydride Grafted PP random copolymer
Fields of application: Functionalised polypropylene to be used as compatibiliser for polymer blends or coupling agent for glass fiber, wood flour, natural fibers, multilayer films, aluminum foils, o..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 72.2 °C | 162 °F | unannealed; ASTM D-648 |
|
Axiall 8607 Rigid PVC, Extrusion
Georgia Gulf 8607 is a special purpose pelletized compound formulated for high impact, rigid extrusion profiles.Information provided by Georgia GulfGeorgia Gulf became Axiall Corporation in 2013.
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 72.0 - 97.0 °C | 162 - 207 °F | Average value: 87.2 °C Grade Count:4 |
|
Overview of materials for ABS/PVC Alloy
This property data is a summary of similar materials in the MatWeb database for the category "ABS/PVC Alloy". Each property range of values reported is minimum and maximum values of appropriate MatW..
|
|||
| Deflection Temperature at 0.46 MPa (66 psi) | 72.0 - 156 °C | 162 - 313 °F | Average value: 115 °C Grade Count:165 |
|
Overview of materials for Polypropylene, Mineral Reinforced
This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene, Mineral Reinforced". Each property range of values reported is minimum and maximum values..
|
|||