| Category | Polymer , Thermoplastic , Ionomer |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | A. Schulman FORMION™ FI 389 Ionomer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by A. Schulman.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.950 g/cc | 0.950 g/cc | ISO 1183/1 |
| Linear Mold Shrinkage | 0.0080 - 0.012 cm/cm @Thickness 3.20 mm |
0.0080 - 0.012 in/in @Thickness 0.126 in |
72 hr; ISO 294 |
| 0.011 - 0.015 cm/cm @Thickness 3.20 mm |
0.011 - 0.015 in/in @Thickness 0.126 in |
aged 48 hrs at 121°C; ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 63 | 63 | 15 sec delay; ISO 868 |
| Tensile Strength, Ultimate | 21.0 MPa | 3050 psi | at max load; ISO 527 |
| Elongation at Break | 410 % | 410 % | ISO 527 |
| Flexural Modulus | 0.860 GPa | 125 ksi | Tangent; ISO 178 |
| Izod Impact, Notched (ISO) | NB | NB | ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 72.0 °C @Thickness 3.20 mm |
162 °F @Thickness 0.126 in |
ISO 75 |
Users viewing this material also viewed the following:
- Menzolit Menzolit® SMC 0390 Unsaturated Polyester UP
- Lavergne VYPET VNT 615 FR PET 15% Glass Reinforced, Flame Retardant
- Heatbath/Park Alu-Braze 960 Aluminum Brazing Salt
- Hexcel® HexForce™ 1620 Fiber Glass Fabric
- A. Schulman POLYFORT™ FPP1666 Talc Filled Homopolymer Polypropylene
- Chosun Refractories N3-2 Fireclay brick
- Clariant Renol PA143G10 Nylon 6/66 Copolymer, 10% Glass Fiber, Heat Stabilized
- DuPont Performance Polymers Hytrel® G4074 Polyester Elastomer TPC-ET (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved