SABIC Innovative Plastics LNP LUBRICOMP FL003 PE
| Category | Polymer , Thermoplastic , Polyethylene (PE) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP FL003 PE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* FL003 is a compound based on Polyethylene resin containing 15% PTFE. Added features include: Internally Lubricated.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.03 g/cc | 1.03 g/cc | ASTM D792 |
| Density | 1.03 g/cc | 0.0372 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.0400 % | 0.0400 % | 50% RH, 24 hrs; ASTM D570 |
| 0.0400 % | 0.0400 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | >= 0.020 cm/cm @Time 86400 sec |
>= 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 12.0 MPa | 1740 psi | 5 mm/min; ISO 527 |
| 14.0 MPa | 2030 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 24.0 MPa | 3480 psi | Type I, 5 mm/min; ASTM D638 |
| 24.0 MPa | 3480 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 59 % | 59 % | Type I, 5 mm/min; ASTM D638 |
| 237 % | 237 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 8.4 % | 8.4 % | 5 mm/min; ISO 527 |
| 8.5 % | 8.5 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 1.31 GPa | 190 ksi | 1 mm/min; ISO 527 |
| 1.48 GPa | 215 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 20.0 MPa | 2900 psi | ISO 178 |
| Flexural Modulus | 0.850 GPa | 123 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 0.920 GPa | 133 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.390 J/cm | 0.731 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 14.6 J/cm | 27.4 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² | 1.43 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 94.0 kJ/m² | 44.7 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 8.00 J @Temperature 23.0 °C |
5.90 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 4.00 J | 2.95 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 134 µm/m-°C @Temperature -30.0 - 30.0 °C |
74.4 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 145 µm/m-°C @Temperature -30.0 - 30.0 °C |
80.6 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 82.0 °C | 180 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 72.0 °C @Thickness 3.20 mm |
162 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 46.0 °C | 115 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 46.0 °C @Thickness 3.20 mm |
115 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Poco Graphite ACF-10Q Industrial Grade Graphite
- PolyChem Alloy PolyOxyter 2501
- Quadrant EPP TIVAR® Extended Wear UHMW-PE, Premium Glass-filled, Partially Cross-linked (ASTM Product Data Sheet)
- Dielectric Polymers NT-140APS General Purpose Laminating Adhesive (discontinued **)
- Lanxess Durethan® BKV 230 H2.0 DUS008 000000 Nylon 6, 30% Glass Fiber
- Metton LMR M2100VO Liquid Molding Resin
- Solvay Specialty Polymers Diofan® P 530 Polyvinylidene Chloride (PVDC)
- A. Schulman SCHULAMID® 66 MV3H Unreinforced Nylon 6/6
- Chi Mei Polylac® PA-764 ABS - Flame Retardant
- DSM Arnite® TV4 460 KL PBT/PET Blend-30% Glass Reinforced (European Grade)
Copyright © lookpolymers.com All Rights Reserved