- High Density Polyethylene (HDPE), Glass fiber Filled
- Techmer ES HiFill® HDPE 8904 UV GY
Techmer ES HiFill® HDPE 8904 UV GY
| Category | Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Glass fiber Filled |
| Manufacturer | Techmer ES |
| Trade Name | HiFill® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Techmer ES HiFill® HDPE 8904 UV GY.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Availability: North AmericaForms: PelletsAdditive: UV StabilizerFeatures: Good UV ResistanceAppearance: GreyInformation provided by TP Composites, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.954 g/cc | 0.0345 lb/in³ | ASTM D792 |
| Water Absorption | 0.010 % @Time 86400 sec |
0.010 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.030 cm/cm @Thickness 3.17 mm |
0.030 in/in @Thickness 0.125 in |
ASTM D955 |
| Melt Flow | 4.4 g/10 min @Load 2.16 kg, Temperature 190 °C |
4.4 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 59 | 59 | ASTM D785 |
| Tensile Strength, Yield | 33.8 MPa | 4900 psi | ASTM D638 |
| Elongation at Break | 9.0 % | 9.0 % | ASTM D638 |
| Flexural Strength | 41.4 MPa | 6000 psi | ASTM D790 |
| Flexural Modulus | 1.10 GPa | 160 ksi | ASTM D790 |
| Izod Impact, Notched | 1.07 J/cm @Thickness 3.17 mm |
2.00 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 144 µm/m-°C | 80.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 72.2 °C | 162 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | Unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Polymer Resources TP-IG30 Polybutylene Terephthalate, 30% Glass Reinforced, Reduced Warpage
- SABIC Innovative Plastics LNP LUBRICOMP WX95752L PBT (Asia Pacific)
- A. Schulman POLYBATCH™ 7171 POLYBATCH® Concentrate Based In Polyethylene
- ExxonMobil Mobilgrease HTM
- DuPont™ Fusabond® E158H Polymer Modifier
- ChevronTexaco Texcool® P 205
- Arkema Group ORGASOL® 2001 UD Nat 2 Polyamide 12, Food Contact Approved
- Cheng Yu Plastic FV30730 POM, 30% Mineral Reinforced
- Resinlab® EP1026 Black Epoxy Adhesive
Copyright © lookpolymers.com All Rights Reserved