Material Notes:

Daplen SB4411/2 is a 10% mineral and elastomer modified polypropylene compound intended for injection molding. The product is available in black, but other colors can be provided on request.Daplen SB4411/2 has been developed for bumper fascias and exterior trims.Information provided by the Manufacturer.

Physical Properties	Metric	English	Comments
Density	0.940 g/cc	0.0340 lb/in³	ISO 1183
Linear Mold Shrinkage	0.0105 cm/cm	0.0105 in/in	Borealis Method
Melt Flow	11 g/10 min @Load 2.16 kg, Temperature 230 °C	11 g/10 min @Load 4.76 lb, Temperature 446 °F	ISO 1133
	50 g/10 min @Load 5.00 kg, Temperature 230 °C	50 g/10 min @Load 11.0 lb, Temperature 446 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Ball Indentation Hardness	28.0 MPa	4060 psi	H385/30; ISO 2039
Tensile Strength, Yield	15.70 MPa	2277 psi	At 50 mm/min; ISO 527-2
Flexural Modulus	0.930 GPa	135 ksi	At 1 mm/min; ISO 178
Izod Impact, Notched (ISO)	33.0 kJ/m²	15.7 ft-lb/in²	ISO 180/1A
	5.00 kJ/m² @Temperature -30.0 °C	2.38 ft-lb/in² @Temperature -22.0 °F	ISO 180/1A
Charpy Impact Unnotched	NB @Temperature -20.0 °C	NB @Temperature -4.00 °F	ISO 179/1eU
Charpy Impact, Notched	3.30 J/cm²	15.7 ft-lb/in²	ISO 179/1eA
	0.500 J/cm² @Temperature -30.0 °C	2.38 ft-lb/in² @Temperature -22.0 °F	ISO 179/1eA
	0.600 J/cm² @Temperature -20.0 °C	2.86 ft-lb/in² @Temperature -4.00 °F	ISO 179/1eA

Thermal Properties	Metric	English	Comments
CTE, linear	75.0 µm/m-°C @Temperature 23.0 - 80.0 °C	41.7 µin/in-°F @Temperature 73.4 - 176 °F	Borealis Method
Deflection Temperature at 0.46 MPa (66 psi)	72.0 °C	162 °F	ISO 75-2
Deflection Temperature at 1.8 MPa (264 psi)	45.0 °C	113 °F	ISO 75-2
Vicat Softening Point	43.0 °C	109 °F	B (50N); ISO 306
	118 °C	244 °F	A (10N); ISO 306
Shrinkage	0.150 % @Temperature 90.0 °C, Time 7200 sec	0.150 % @Temperature 194 °F, Time 2.00 hour	Post Shrinkage; Borealis Method

Processing Properties	Metric	English	Comments
Melt Temperature	220 - 260 °C	428 - 500 °F
Mold Temperature	30.0 - 50.0 °C	86.0 - 122 °F