Braskem BT 003 HDPE Blow Molding Polyethylene (discontinued **)
| Category | Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Blow Molding Grade |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Braskem BT 003 HDPE Blow Molding Polyethylene
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Bottles for food products, lubricating and cooking oil; toys; bottler for surface-active agents; sheets. Information provided by Braskem
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.962 g/cc | 0.0348 lb/in³ | ASTM D1505 |
| ESCR 100% Igepal® | 16 hour @Thickness 3.00 mm, Temperature 23.0 °C |
16 hour @Thickness 0.118 in, Temperature 73.4 °F |
compression molded plaques; ASTM D1693B |
| Melt Flow | 0.33 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.33 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| High Load Melt Index | 45 g/10 min @Load 21.6 kg, Temperature 190 °C |
45 g/10 min @Load 47.6 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 65 | 65 | ASTM D2240 |
| Tensile Strength at Break | 28.0 MPa | 4060 psi | ASTM D638 |
| Tensile Strength, Yield | 24.0 MPa | 3480 psi | ASTM D638 |
| Flexural Modulus | 1.439 GPa | 208.7 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 72.0 °C | 162 °F | ASTM D648 |
| Vicat Softening Point | 128 °C | 262 °F | ASTM D1525 |
Users viewing this material also viewed the following:
- Pacific Sintered Materials FCC-214-S(HT) High Carbon Copper Steel Powdered Metal
- Kolon KOPET® KP133G30 FR-PET Resin
- DuPont Nucrel® 30907 Ethylene Acid Copolymer Resin
- TIMET TIMETAL® 21S Titanium Alloy (Ti-15Mo-3Nb-3Al-0.2Si, ASTM Grade 21); Aged at 593°C
- Washington Penn Medium Impact Copolymer 40% Calcium Carbonate Filled
- Fainplast Compounds Ethylplus 613 HPE Polyethylene Cable Compound
- Dow Corning 2210 ANTIFOAM
- Arkema Group Rilsan® BUM 30 Nylon 11, 30% Glass Bead Filled (Conditioned)
- Bhansali Engineering Abstron KU600N ABS Heat Resistant
Copyright © lookpolymers.com All Rights Reserved